A kind of composite catalytic filter material for degrading dioxin at low temperature and preparation method thereof

A technology of high temperature resistant filter material and filter material, which can be used in catalyst activation/preparation, chemical instruments and methods, separation methods, etc. Has the effect of performance and stability

Active Publication Date: 2021-07-16
ZHEJIANG UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its disadvantage is that the loaded low-temperature Mn-based catalyst is prone to chlorine poisoning and deactivation, and the incineration flue gas contains a certain concentration of HCl acid gas and chlorinated organic pollutants. Therefore, research and development of a catalytic filter with excellent chlorine poisoning resistance material is necessary

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of composite catalytic filter material for degrading dioxin at low temperature and preparation method thereof
  • A kind of composite catalytic filter material for degrading dioxin at low temperature and preparation method thereof
  • A kind of composite catalytic filter material for degrading dioxin at low temperature and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Such as figure 1 Shown, preparation method of the present invention is as follows:

[0035] (1) Filter material activation: First cut out a polyphenylene sulfide needle felt filter material disc with a diameter of 20mm, wash it three times with deionized water, dry it in an oven at 105°C for 6 hours, and weigh it; weigh 0.0577g Sodium lauryl sulfate powder was prepared into 200 mL of 0.001 mol / L sodium lauryl sulfate solution with deionized water as a solvent, and the dried polyphenylene sulfide disc was immersed in the solution, and ultrasonically activated for 1 h.

[0036] (2) Precipitation in situ: a). Impregnating Ce active components: Weigh 0.3251 g of cerium chloride heptahydrate and add it to the solution obtained in step (1), and stir at room temperature for 12 hours.

[0037] b).KMnO 4 Oxidation: Weigh 1.3790g of potassium permanganate powder, dissolve it in 100mL of deionized water, and prepare a 0.08mol / L potassium permanganate solution, and add 100mL of 0...

Embodiment 2

[0041] (1) Filter material activation: first cut out a polyphenylene sulfide needle felt filter material disc with a diameter of 20mm, wash it three times with deionized water, dry it in an oven at 105°C for 6 hours, and weigh it; weigh 0.2307g Sodium lauryl sulfate powder was prepared into 200 mL of 0.004 mol / L sodium lauryl sulfate solution with deionized water as a solvent, and the dried polyphenylene sulfide disc was immersed in the solution, and ultrasonically activated for 2 hours.

[0042] (2) Precipitation in situ: a): impregnation of Ce active components: Weigh 0.6502 g of cerium chloride heptahydrate and add it to the solution obtained in step (1), and stir at room temperature for 16 hours.

[0043] b): KMnO 4 Oxidation: Weigh 2.7580g of potassium permanganate powder, dissolve it in 100mL of deionized water, and prepare a 0.17mol / L potassium permanganate solution, and add 100mL of 0.17mol / L potassium permanganate solution to step a ) in the resulting solution, stirr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a composite catalytic filter material for low-temperature degradation of dioxins and a preparation method thereof, belonging to the technical field of waste incineration tail gas treatment. The high-temperature-resistant filter material is used as a catalyst carrier, activated by the filter material, precipitated in situ, and impregnated with V active group and low-temperature plasma oxidation steps to prepare loaded VO x -MnCeO x Composite catalytic filter material for three-way catalyst. The advantages of the present invention are: (1) excellent low-temperature activity and selectivity for catalytic degradation of dioxins; (2) active component V with high activity and excellent chlorine poisoning resistance is added to the filter material, through Effectively oxidize V active components, improve catalytic activity and chlorine poisoning resistance; (3) achieve even and firm loading of the catalyst on the surface of the filter material by in-situ precipitation method, mild preparation conditions, maintain the original performance and stability of the filter material, long lasting.

Description

technical field [0001] The invention belongs to the technical field of waste incineration tail gas treatment, and in particular relates to a composite catalytic filter material for low-temperature degradation of dioxins and a preparation method thereof. Background technique [0002] In recent years, my country's domestic waste incineration industry has been greatly developed, the rate of waste incineration and disposal will continue to rise, and the scale of waste incineration power plants under construction and proposed to be built continues to expand. The "avoidance effect" cannot be ignored, especially the trace amount of dioxin pollutants emitted in the incineration flue gas poses a serious threat to the environment and human health, which has attracted great attention from the state. In 2014, my country's dioxin emission standard was lowered to 0.1ngTEQ / Nm 3 (GB18485-2014). [0003] At present, waste incineration plants mainly use the combination of activated carbon in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01D39/08B01J23/34B01J37/34B01D46/02B01D53/86B01D53/70
CPCB01D39/08B01D46/02B01D53/8662B01D2239/0618B01D2239/10B01J23/34B01J37/349
Inventor 陆胜勇彭亚旗刘红蕾汤明慧李晓东严建华
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap