A kind of plastering anti-cracking waterproof mortar and preparation method thereof

A technology of waterproof mortar and water repellent, applied in the field of building materials, can solve the problems of plastering mortar not having heat resistance, fire resistance, low durability of plastering mortar, not enough economical and environmental protection, etc., so as to improve bulges and cracks and reduce elasticity. Modulus, the effect of reducing peeling

Active Publication Date: 2021-03-23
佛山市建通混凝土制品有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, plastering mortar generally does not have the performance of heat resistance and fire prevention. When a fire breaks out in a building, the temperature of the wall surface will change due to the fire. The temperature expands, and it is easy to produce bulges or cracks, which is difficult to meet the higher actual engineering needs. The durability of the plastering mortar is not high, and the wall after the fire needs to be repaired in a large area, which is not economical and environmentally friendly.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A kind of plastering anti-cracking waterproof mortar, which is prepared by the following steps: Weigh the raw material components according to the proportion, first mix 280kg / m 3 Cement, 78 kg / m 3 Stone powder, 1.3 kg / m 3 Polypropylene anti-split fibers and 1120 kg / m 3 Sand pre-mixed and stirred for 1min, then mixed with 185 kg / m 3 Water, 8.1 kg / m 3 Admixture, 10.3 kg / m 3 Water repellent, 36 kg / m 3 Coumarone resin and 42 kg / m 3 Aluminum dihydrogen phosphate, stirred and mixed for 5 minutes to obtain the mortar;

[0042] Among them, the admixture is formed by mixing a thickening water-retaining agent and an open time regulator in a mass ratio of 10:3.

Embodiment 2

[0044] A kind of plastering anti-cracking waterproof mortar, which is prepared by the following steps: Weigh the raw material components according to the proportion, first mix 314kg / m 3 Cement, 66 kg / m 3 Stone powder, 0.8 kg / m 3 Polypropylene anti-split fibers and 1100 kg / m 3 The sand is pre-mixed and stirred for 2 minutes, and then mixed with 215kg / m 3 Water, 6.5 kg / m 3 Admixture, 8.9kg / m 3 Water repellant, 44 kg / m 3 Coumarone resin and 34 kg / m 3 Aluminum dihydrogen phosphate, stirred and mixed for 3 minutes to obtain the mortar;

[0045]Among them, the admixture is formed by mixing a thickening water-retaining agent and an open time regulator in a mass ratio of 9:5.

Embodiment 3

[0047] A kind of plastering anti-cracking waterproof mortar, which is prepared by the following steps: Weigh the raw material components according to the proportion, first mix 300kg / m 3 Cement, 72 kg / m 3 Stone powder, 0.9 kg / m 3 Polypropylene anti-split fibers and 1320 kg / m 3 The sand is pre-mixed and stirred for 2 minutes, and then mixed with 195kg / m 3 Water, 7.6kg / m 3 Admixture, 11.7kg / m 3 Water repellant, 48 kg / m 3 Coumarone resin and 28 kg / m 3 Aluminum dihydrogen phosphate, stirred and mixed for 5 minutes to obtain the mortar;

[0048] Among them, the admixture is formed by mixing a thickening water-retaining agent and an open time regulator according to a mass ratio of 15:4.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The application relates to the field of concrete, and specifically discloses a plastering anti-cracking waterproof mortar and a preparation method thereof. Mortar includes cement: 280-314 parts; sand: 1100-1320 parts; stone powder: 66-78 parts; admixture: 6.5-8.1 parts; polypropylene anti-cracking fiber: 0.8-1.3 parts; waterproofing agent: 8.9-11.7 parts; coumarone resin: 36-48 parts; aluminum dihydrogen phosphate: 28-42 parts; water: 185-215 parts; the preparation method is: after mixing and stirring each raw material of the mortar, That is the mortar. This application uses coumarone resin to crack and shrink under high temperature conditions to ease the high temperature expansion efficiency of plastering mortar, improve the high temperature bonding strength of aluminum dihydrogen phosphate, and improve the bulging and cracking of mortar after fire.

Description

technical field [0001] The application relates to the field of building materials, more specifically, it relates to a plastering anti-cracking waterproof mortar. Background technique [0002] With the advancement and development of grassroots construction and urbanization, the demand for plastering mortar used in building decoration projects is also increasing. Plastering mortar is a type of plastering mortar used to level or protect the base surface of the building Mortar, collectively referred to as mortar, is suitable for decoration of interior and exterior walls, cover surfaces, bottom surfaces, ceiling plastering, etc. of construction and decoration projects, and plays a protective and beautifying role. [0003] At present, plastering mortar generally does not have the performance of heat resistance and fire prevention. When a fire breaks out in a building, the temperature of the wall surface will change due to the fire. The temperature expands, and it is easy to produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B22/16C04B24/26C04B111/34C04B111/27
CPCC04B22/16C04B24/26C04B24/2617C04B28/04C04B2111/00482C04B2111/27C04B2111/343C04B2201/50C04B14/06C04B18/12C04B2103/44C04B2103/465C04B2103/0068C04B16/0633C04B2103/65C04B22/002
Inventor 高春雷梁俊文郑凯升梁德强黄育林
Owner 佛山市建通混凝土制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products