Glass fiber impregnating agent for glass fiber reinforced plastic pipeline and preparation method and device

A technology for glass fibers and preparation devices, which are used in transportation and packaging, chemical instruments and methods, mixers with rotary stirring devices, etc., to achieve increased wear resistance and flexibility, good bonding performance, and increased short-term failure pressure Effect

Pending Publication Date: 2021-03-19
邢台金牛玻纤有限责任公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The short-term failure pressure of existing FRP pipes in the market is generally 2.6-2.7 times the nominal pressure, which gradually cannot meet the growing needs of the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass fiber impregnating agent for glass fiber reinforced plastic pipeline and preparation method and device
  • Glass fiber impregnating agent for glass fiber reinforced plastic pipeline and preparation method and device
  • Glass fiber impregnating agent for glass fiber reinforced plastic pipeline and preparation method and device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Embodiment 1 A kind of glass fiber sizing agent for FRP pipeline

[0048] This embodiment discloses a glass fiber sizing agent for FRP pipelines, the sizing agent includes coupling agent, lubricant A, lubricant B, film forming agent, antistatic agent, pH regulator and water, the coupling agent The agent is an enhanced silane coupling agent; the lubricant is a mixture of lubricant A and lubricant B, lubricant A is a polyoxyethylene ether lubricant, and lubricant B is a quaternary ammonium salt lubricant. The film agent is a mixture of two different types of epoxy emulsions, film forming agent A and film forming agent B, the antistatic agent is an ammonium salt antistatic agent, and the pH regulator is an organic acid with a pH of 2.5-6; The percentage of the solid mass of each component in the sizing agent to the solid mass of the sizing agent is expressed as follows:

[0049]

[0050]

[0051] The solid mass of the wetting agent accounts for 3.5-7.5% of the total...

Embodiment 2

[0055] Embodiment 2 A kind of glass fiber sizing agent preparation device for FRP pipeline

[0056] This embodiment discloses a device for preparing a glass fiber sizing agent for FRP pipes, such as figure 1 As shown, the main tank body 2 is included, the main tank body 2 is provided with a main stirring mechanism 5, the top of the main tank body 2 is provided with a main driving mechanism 4 for making the main stirring mechanism 5 carry out material stirring, and the top of the main tank body 2 is provided with Feed pipe, the bottom end is provided with discharge pipe 61, described main stirring mechanism 5 comprises main stirring shaft 51, is radially provided with several heating stirring bodies 52 on the main stirring shaft 51, and main driving mechanism 4 includes for making main The agitator shaft 51 is a lifting drive part for reciprocating up and down and a rotary drive part for rotating the main agitator shaft 51 , and the lift drive part and the rotary drive part are...

Embodiment 3

[0068] Embodiment 3 A kind of preparation method of glass fiber sizing agent for FRP pipeline

[0069] This embodiment discloses a method for preparing a glass fiber sizing agent for FRP pipelines, comprising the following steps:

[0070] Step A According to the ratio, add a total of 40-50% of pure water into the main tank through the feed pipe, then add a total of 1-5% of the pH regulator, turn on the main stirring mechanism to stir evenly, and the stirring time is 3 -5min, the stirring speed is 15r / min;

[0071] Step B: Add the required amount of polyamide-based silane coupling agent into the main tank through the feeding pipe according to the speed of 0.3kg / min and stir evenly. The stirring time is 20-40min. Test the pH of the mixed liquid and control its pH 3-4.5;

[0072] Step C: Put the required amount of lubricant and antistatic agent into the auxiliary tank with pure water at 60-70 degrees Celsius through the auxiliary feeding pipe for material premixing, start the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a glass fiber impregnating agent for a glass fiber reinforced plastic pipeline and a preparation method and device, and belongs to the technical field of glass fiber impregnating agents. The impregnating agent comprises 5-13% of a coupling agent, 15-30% of a lubricant A, 0.5-3.0% of a lubricant B, 49-72% of a film-forming agent, 1-8% of an antistatic agent, 1-5% of a pH regulator, and the balance being water, wherein the solid mass of the impregnating agent accounts for 3.5-7.5% of the total mass of the impregnating agent, and the coupling agent is an enhanced silane coupling agent. The lubricant is a mixture of a lubricant A and a lubricant B, the lubricant A is a polyoxyethylene ether lubricant, the lubricant B is a quaternary ammonium salt lubricant, the film-forming agent is a mixture of two different types of epoxy emulsions, namely a film-forming agent A and a film-forming agent B, the antistatic agent is an ammonium salt antistatic agent, and the pH regulator is an organic acid; the prepared impregnating agent is excellent in performance, the quality of a glass fiber product can be improved, a processed glass fiber reinforced plastic pipeline has thecomprehensive performance of excellent mechanical strength and high pressure resistance, the short-time failure pressure of the glass fiber reinforced plastic pipeline is improved, and the market requirements are met.

Description

technical field [0001] The invention belongs to the technical field of glass fiber sizing agent, and in particular relates to a glass fiber sizing agent for FRP pipelines, a preparation method and a device. Background technique [0002] High-pressure oil pipes are pressure-resistant pipes required in the process of oil collection and transportation, and are generally made of steel and glass fiber reinforced plastics. At present, major domestic oil fields have successively experienced secondary oil recovery and tertiary oil recovery, and oil production has entered a period of high water content or ultra-high water content development. The water contains a large amount of corrosive substances, and high water content leads to higher and higher corrosiveness of the transported liquid. This puts higher and higher requirements on the corrosion resistance of the pipeline; in accordance with the requirements of 6.3.2 and 6.3.3 of "High Pressure FRP Oil Pipes for the Oil and Gas Indu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C25/40C03C25/36B01F7/18B01F15/00
CPCC03C25/40C03C25/36B01F27/90B01F35/322
Inventor 韩立星李彪张建鹏
Owner 邢台金牛玻纤有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap