Frequency-stable low-dielectric microwave dielectric ceramic material and preparation method thereof

A technology of microwave dielectric ceramics and frequency stabilization, applied in the field of material science, can solve the problems of easy limitation of material application, deterioration of material dielectric properties and mechanical strength, and grain growth

Active Publication Date: 2021-06-08
JIAXING GLEAD ELECTRONICS CO LTD
View PDF11 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in practical applications, due to the simple perovskite structure of CaTiO 3 , SrTiO 3 or Ca 1-x Sr x TiO 3 The linearity of the temperature coefficient of the corresponding product is poor, and the frequency temperature coefficient of the corresponding product is difficult to satisfy τ in the whole temperature range (such as -40 ° C ~ 110 ° C) at the same time f The requirement of ≤±5ppm/℃, the frequency stability of related devices is poor, which limits its use in mobile base stations
[0005] On the other hand, due to the sintering process of Mg 2+ Si 4+ There is a big difference in the diffusion rate, and it is very easy t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Frequency-stable low-dielectric microwave dielectric ceramic material and preparation method thereof
  • Frequency-stable low-dielectric microwave dielectric ceramic material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 1) Synthesis of main phase ceramic material A:

[0030] According to the chemical formula Mg 2.00 co 0.10 SiO 4.10 Measuring ratio weighing raw materials MgO, SiO 2 and CoO, add deionized water according to the ratio of mixture to deionized water 1:3, mix and grind for 20 hours, then dry in an oven at 120°C, grind with a quartz mortar and pass through a 40-mesh sieve, and then put the powder into alumina The crucible was calcined at 1250°C for 3 hours to obtain the main phase calcined powder A.

[0031] 2) Synthesis of auxiliary phase ceramic material B:

[0032] According to the chemical composition 0.99CaO·0.11SrO-0.06La 2 o 3 0.05Al 2 o 3 -1.00TiO 2 Weigh raw material CaCO 3 , SrCO 3 , La 2 o 3 、Al 2 o 3 and TiO 2 Mix, add deionized water according to the ratio of mixture and deionized water 1:2, mix and grind for 16 hours, then dry in an oven at 120°C, grind with a quartz mortar and pass through a 40-mesh sieve, and then put the powder into alumina ...

Embodiment 2

[0035] 1) Synthesis of main phase ceramic material A:

[0036] According to the chemical formula Mg 2.02 Zn 0.05 SiO 4.07 Measuring ratio weighing raw materials MgO, SiO 2 and ZnO, add deionized water according to the ratio of mixture to deionized water 1:3, mix and grind for 16 hours, then dry in an oven at 120°C, grind with a quartz mortar and pass through a 40-mesh sieve, and then put the powder into alumina The crucible was calcined at 1200°C for 3 hours to obtain the main phase calcined powder A.

[0037] 2) Synthesis of auxiliary phase ceramic material B:

[0038] According to the chemical composition 1.05CaO·0.12SrO-0.08Nd 2 o 3 0.06Al 2 o 3 -1.05TiO 2 Weigh raw material CaCO 3 , SrCO 3 、Nd 2 o 3 、Al 2 o 3 and TiO 2 For mixing, add deionized water according to the ratio of mixture and deionized water 1:2, mix and grind for 20 hours, then dry in an oven at 120°C, grind with a quartz mortar and pass through a 40-mesh sieve, and then put the powder into alu...

Embodiment 3

[0041] 1) Synthesis of main phase ceramic material A:

[0042] According to the chemical formula Mg 1.95 co 0.10 SiO 4.05 Measuring ratio weighing raw materials MgO, SiO 2 and CoO, add deionized water according to the ratio of mixture to deionized water 1:3, mix and grind for 20 hours, then dry in an oven at 120°C, grind with a quartz mortar and pass through a 40-mesh sieve, and then put the powder into alumina The crucible was calcined at 1150°C for 4 hours to obtain the main phase calcined powder A.

[0043] 2) Synthesis of auxiliary phase ceramic material B:

[0044] According to the chemical composition 1.25CaO·0.20SrO-0.15La 2 o 3 0.12Al 2 o 3 -1.20TiO 2 Weigh raw material CaCO 3 , SrCO 3 , La 2 o 3 、Al 2 o 3 and TiO 2 Mix, add deionized water according to the ratio of mixture and deionized water 1:2, mix and grind for 16 hours, then dry in an oven at 120°C, grind with a quartz mortar and pass through a 40-mesh sieve, and then put the powder into alumina ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a frequency-stable low-dielectric microwave dielectric ceramic material and a preparation method thereof. The material is prepared from the following components in percentage by mass: 70-90% of a main-phase ceramic material A, 10-30% of an auxiliary-phase ceramic material B and 0-1.0% of an oxide sintering aid C, The main-phase ceramic material A is MgxMeySiO2+x+y; the auxiliary-phase ceramic material B is composed of aRO-bRe2O3-cTiO2, R is at least one of Ca or Sr, Re2O3 is at least two of Sm2O3, Nd2O3, Y2O3, Al2O3 and La2O3; and the oxide sintering aid C is at least one of MnO2, WO3 and CeO2. The dielectric constant of the prepared microwave dielectric ceramic material is 9.5-13.6, the frequency temperature coefficient tau f is continuously adjustable between -16 ppm/DEG C and 13 ppm/DEG C, and the ceramic material has good frequency stability and is suitable for the fields of new-generation mobile communication, high-frequency network communication and the like.

Description

technical field [0001] The invention belongs to the technical field of material science, and in particular relates to a frequency-stable low-medium microwave dielectric ceramic material and a preparation method thereof. Background technique [0002] Microwave dielectric ceramics are functional ceramic materials used in microwave frequency circuits to achieve one or more functions. They play an important role in the application of modern communication technology. key material. With the new generation of mobile communication and high-frequency network communication, the requirements for low delay and reliability of signal transmission are getting higher and higher, and microwave dielectric ceramic materials with low dielectric constant and excellent temperature coefficient stability have received more and more attention. Typical applications, such as filters in 5G base stations, usually require that the frequency temperature coefficient of -40°C to 110°C be within ±5ppm / °C, s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/20C04B35/64
CPCC04B35/20C04B35/64C04B2235/3208C04B2235/3284C04B2235/3224C04B2235/3225C04B2235/3227C04B2235/3217C04B2235/3267C04B2235/442C04B2235/3258C04B2235/3229C04B2235/3232C04B2235/96
Inventor 刘顺国童建喜刘强黄丹胥金华史雪斌
Owner JIAXING GLEAD ELECTRONICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap