Production process of hot-rolled metal composite pipe
A metal composite pipe and production process technology, applied in the field of composite seamless pipe, can solve the problems of insufficient bonding strength of the inner cladding composite pipe, affecting product use, and high cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0029] A production process for a hot-rolled metal composite pipe, comprising the following steps:
[0030] A. Select the composite tube blank, the diameter of the composite tube blank is 210±1.6mm, the diameter tolerance of the ellipticity is 1.5mm, the inclination of the end face is not more than 5mm, the curvature is not more than 6mm per meter, and the double metal is tightly combined without delamination;
[0031] B. Inspect the selected composite tube blank, and punch the positioning hole on the composite tube blank. The positioning hole is located at the front end of the tube blank, with a diameter of 50mm, which improves the accuracy of the product wall thickness and reduces the length of the cutting head;
[0032] C. Heating the annular furnace, the heating rate is 10min / cm, and the heating temperature cannot exceed the specified maximum temperature by 10°C; Adjust to the temperature required by rolling; every time a piece of material is discharged, the bottom of the ...
Embodiment 2
[0042] A production process for a hot-rolled metal composite pipe, comprising the following steps:
[0043] A. Select the composite tube blank, the diameter of the composite tube blank is 210±1.6mm, the diameter tolerance of the ellipticity is 1.5mm, the inclination of the end face is not more than 5mm, the curvature is not more than 6mm per meter, and the double metal is tightly combined without delamination;
[0044] B. Inspect the selected composite tube blank, and punch the positioning hole on the composite tube blank. The positioning hole is located at the front end of the tube blank, with a diameter of 50mm, which improves the accuracy of the product wall thickness and reduces the length of the cutting head;
[0045] C. Heating the annular furnace, the heating rate is 10min / cm, and the heating temperature cannot exceed the specified maximum temperature by 10°C; Adjust to the temperature required by rolling; every time a piece of material is discharged, the bottom of the ...
Embodiment 3
[0055] A production process for a hot-rolled metal composite pipe, comprising the following steps:
[0056] A. Select the composite tube blank, the diameter of the composite tube blank is 210±1.6mm, the diameter tolerance of the ellipticity is 1.5mm, the inclination of the end face is not more than 5mm, the curvature is not more than 6mm per meter, and the double metal is tightly combined without delamination;
[0057] B. Inspect the selected composite tube blank, and punch the positioning hole on the composite tube blank. The positioning hole is located at the front end of the tube blank, with a diameter of 50mm, which improves the accuracy of the product wall thickness and reduces the length of the cutting head;
[0058] C. Heating the annular furnace, the heating rate is 10min / cm, and the heating temperature cannot exceed the specified maximum temperature by 10°C; Adjust to the temperature required by rolling; every time a piece of material is discharged, the bottom of the ...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap