Bentonite modified aluminate inorganic anticorrosive mortar for pipe network repair and preparation method thereof

A technology of bentonite slurry and aluminate, which is applied in the field of bentonite modified aluminate inorganic anticorrosion mortar and preparation for pipe network repair, and can solve the problems of long setting time, poor corrosion resistance, mortar bond strength, impermeability strength and mechanical strength Low-level problems, to achieve the effect of short setting time, strong corrosion resistance, thixotropy and strong adhesion

Active Publication Date: 2021-12-07
MUNICIPAL ENVIRONMENTAL PROTECTION ENG CO LTD OF CREC SHANGHAI GRP +1
View PDF16 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problems of low mortar bond strength, impermeability strength, mechanical strength, long setting time and poor corrosion resistance in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bentonite modified aluminate inorganic anticorrosive mortar for pipe network repair and preparation method thereof
  • Bentonite modified aluminate inorganic anticorrosive mortar for pipe network repair and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Preparation of dry powder: in parts by mass, 100 parts of P.O.42.5 Portland cement, 20 parts of high-resistance aluminate cement, 60 parts of quartz sand (70 mesh), 40 parts of river sand, early-strength polycarboxylate 1 part of acid superplasticizer powder, 1 part of steel fiber, and 1 part of polyanionic cellulose were uniformly mixed (stirring at 500 r / min for 10 minutes) to prepare dry powder.

[0024] Then add 50 parts of water while stirring, and stir at 300r / min for 10 minutes to prepare mortar; then add 2 parts of homemade bentonite, and stir at 300r / min for 30 minutes to form an anti-corrosion mortar product.

Embodiment 2

[0026] Preparation of dry powder: in parts by mass, 120 parts of P.O.42.5 Portland cement, 30 parts of high-resistance aluminate cement, 80 parts of quartz sand (80 mesh), 50 parts of river sand, early-strength polycarboxylate 5 parts of acid superplasticizer powder, 3 parts of steel fiber, and 3 parts of polyanionic cellulose were uniformly mixed (stirring at 500 r / min for 10 minutes) to prepare dry powder; the quartz sand was 70 mesh.

[0027] Then add 60 parts of water while stirring, and stir at 300r / min for 10 minutes to prepare mortar; then add 5 parts of homemade bentonite, and stir at 300r / min for 10 minutes to form an anti-corrosion mortar product.

Embodiment 3

[0029] Preparation of dry powder: In parts by mass, 110 parts of P.O.42.5 Portland cement, 25 parts of high-resistance aluminate cement, 70 parts of quartz sand (100 mesh), 45 parts of river sand, early-strength polycarboxylate 3 parts of acid superplasticizer powder, 2 parts of steel fiber, and 2 parts of polyanionic cellulose were uniformly mixed (stirring at 500 r / min for 10 minutes) to prepare dry powder; the quartz sand was 70 mesh.

[0030] Then add 60 parts of water while stirring, and stir at 300r / min for 10 minutes to prepare mortar; then add 4 parts of homemade bentonite, and stir at 300r / min for 10 minutes to form an anti-corrosion mortar product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses bentonite modified aluminate inorganic anticorrosive mortar for pipe network repair and a preparation method thereof. The preparation method comprises the following steps of preparing dry powder: mixing 100-120 parts by mass of Portland cement, 20-30 parts by mass of high-resistance aluminate cement, 60-80 parts by mass of quartz sand, 40-50 parts by mass of river sand, 1-5 parts by mass of a water reducing agent,1-3 parts by mass of steel fiber, and1-3 parts by mass ofpolyanionic cellulose, and uniformly stirring, continuously stirring the obtained dry powder, and adding 50-60 parts of water while stirring, adding 2-5 parts of self-made bentonite slurry, and stirring for 5-10 minutes at the speed of 200-400 r/min to form a mortar product. The self-made bentonite slurry is prepared by uniformly mixing 8-10 parts of high-viscosity bentonite, 0.2-0.5 part of sodium carbonate and 95-100 parts of water in proportion, stirring and puffing; the high-viscosity bentonite is high-viscosity organic bentonite prepared by modifying organic quaternary ammonium salt. By setting the components, the prepared mortar is higher in water-retaining property, thixotropy and adhesive capacity, shorter in setting time, higher in flexural and compressive strength and higher in corrosion resistance.

Description

technical field [0001] The invention relates to the field of pipeline repair, in particular to a bentonite-modified aluminate inorganic anti-corrosion mortar for pipeline network repair and a preparation method thereof. Background technique [0002] With the further advancement of national urbanization, the design of urban underground foundations is intricate, which puts forward higher requirements for underground pipe network systems. In particular, some underground drainage pipe networks constructed in the early stage have collapsed and damaged to varying degrees, and conventional excavation repairs have a certain impact on the urban traffic environment and other aspects. More and more trenchless repairs are being used in the repair of drainage pipe networks. under construction. Trenchless pipeline repair technology can well solve the problems of aging, corrosion, leakage, interface disconnection, deformation and other problems in urban pipelines, prolong the service life...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06
CPCC04B28/06C04B2111/00482C04B2201/50C04B22/00C04B14/06C04B14/48C04B24/383C04B2103/302C04B22/10C04B14/104Y02W30/91
Inventor 孙东晓陈钱宝刘学明苏炜斌姚松柏李瑾如梅晓君董志强
Owner MUNICIPAL ENVIRONMENTAL PROTECTION ENG CO LTD OF CREC SHANGHAI GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap