A tissue-guided regeneration collagen film and its preparation method

A technology that guides regeneration and collagen membranes, applied in surgery, medical science, etc., can solve problems such as unsuitable pore size and porosity, incomplete removal of immunogens, immune reactions, etc., and achieve long degradation cycle, excellent tissue repair effect, comprehensive effect comprehensive effect

Active Publication Date: 2022-04-12
TIANXINFU (BEIJING) MEDICAL APPLIANCE CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing technologies include: preparing animal dermis and pericardium through decellularization technology to guide tissue regeneration membrane materials, but this technology has the problem of incomplete removal of immunogens and postoperative immune reactions; another technology is through the method of purification Collagen is extracted from animal connective tissue, and then prepared by cross-linking and freeze-drying technology to guide tissue regeneration collagen film, but this technology has poor mechanical strength, short degradation cycle, pore size and porosity are not suitable for cell growth, resulting in poor repair effect. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A tissue-guided regeneration collagen film and its preparation method
  • A tissue-guided regeneration collagen film and its preparation method
  • A tissue-guided regeneration collagen film and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] This embodiment provides a method for preparing a tissue-guided regeneration collagen membrane, comprising the following steps:

[0026] (1) Swell type I collagen with a purity of 90% in an acetic acid solution with a concentration of 0.4% (v / v), and prepare it to obtain a collagen-acetic acid swelling solution with a concentration of 0.3% (w / v) Add chondroitin sulfate sodium and stir evenly, the concentration of chondroitin sulfate sodium is 0.02% (w / v), and after completion, collagen-chondroitin sulfate sodium slurry is obtained;

[0027] (2) Pour the collagen-sodium chondroitin sulfate slurry into a stainless steel freeze-drying tray to make a thickness of 1 mm, and then place the freeze-drying tray in a vacuum freeze dryer for vacuum freeze-drying to obtain a dried membrane;

[0028] (3) Mix the dry membrane with a cross-linking solution with a concentration of 0.01% (v / v), and the ratio of the area of ​​the dry membrane to the volume of the cross-linking solution i...

Embodiment 2

[0031] This embodiment provides a method for preparing a tissue-guided regeneration collagen membrane, comprising the following steps:

[0032] (1) Swell type I collagen with a purity of 92% in an acetic acid solution with a concentration of 0.7% (v / v), and prepare it to obtain a collagen-acetic acid swelling solution with a concentration of 1.0% (w / v) Add chondroitin sulfate sodium and stir evenly, the concentration of chondroitin sulfate sodium is 0.05% (w / v), and after completion, collagen-chondroitin sulfate sodium slurry is obtained;

[0033] (2) Pour the collagen-chondroitin sulfate sodium slurry into a stainless steel freeze-drying tray to make a thickness of 10 mm, and then place the freeze-drying tray in a vacuum freeze dryer for vacuum freeze-drying to obtain a dried membrane ;

[0034] (3) Mix the dry membrane with a cross-linking solution with a concentration of 1% (v / v), and the ratio of the area of ​​the dry membrane to the volume of the cross-linking solution i...

Embodiment 3

[0037] This embodiment provides a method for preparing a tissue-guided regeneration collagen membrane, comprising the following steps:

[0038] (1) Swell type I collagen with a purity of 91% in an acetic acid solution with a concentration of 0.5% (v / v), and prepare it to obtain a collagen-acetic acid swelling solution with a concentration of 0.6% (w / v) Add chondroitin sulfate sodium and stir evenly, the concentration of chondroitin sulfate sodium is 0.03% (w / v), and after completion, collagen-chondroitin sulfate sodium slurry is obtained;

[0039] (2) Pour the collagen-chondroitin sulfate sodium slurry into a stainless steel freeze-drying tray to make the thickness 5mm, then place the freeze-drying tray in a vacuum freeze dryer for vacuum freeze-drying to obtain a dried membrane;

[0040] (3) Mix the dry membrane with the cross-linking solution with a concentration of 0.5% (v / v), and the ratio of the area of ​​the dry membrane to the volume of the cross-linking solution is 2.5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a tissue-guided regeneration collagen film and a preparation method thereof. The preparation method is as follows: swell type I collagen in an acetic acid solution, then add sodium chondroitin sulfate and stir evenly to obtain a collagen-chondroitin sulfate sodium slurry; dry the collagen-chondroitin sulfate sodium slurry, Obtain a dry film; mix the dry film with the cross-linking liquid, carry out the cross-linking reaction, and obtain a cross-linked collagen film after completion; clean the cross-linked collagen film and perform secondary drying to complete Then repress it. In the preparation method, high-concentration type I collagen is first swelled in acetic acid solution, and sodium chondroitin sulfate is added to stir, followed by drying, cross-linking, and secondary drying, and the obtained tissue-guided regeneration collagen film has excellent mechanical properties , and the pore size and porosity are conducive to cell growth and repair; in addition, its degradation cycle is long and it is not easy to cause allergies. The comprehensive effect is comprehensive and the applicability is wide.

Description

technical field [0001] The invention belongs to the technical field of regenerative medical materials, and in particular relates to a tissue-guided regeneration collagen film and a preparation method thereof. Background technique [0002] Tooth loss caused by oral diseases such as periodontitis and dental caries has become a common oral disease. According to the survey, more than half of our population has tooth loss. With the continuous development of science, dental implant technology has become a common method for the restoration of tooth loss. However, clinically, due to the physiological bone resorption after tooth loss and the bone tissue defect in traumatic tooth loss, some alveolar ridges are often too low. , Too narrow or partially defective cases, 40% to 80% of the patients have insufficient bone mass. If not treated, lateral perforation often occurs during the implantation process, resulting in implant failure. With the clinical application of guided regeneration...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J9/28C08J9/36C08L89/00C08L5/08A61L31/04A61L31/14
CPCC08J9/28C08J9/36A61L31/148A61L31/041A61L31/146C08J2389/00C08J2405/08
Inventor 黄果张伟孙冰冰
Owner TIANXINFU (BEIJING) MEDICAL APPLIANCE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com