Aqueous emulsion type nm adhesive for paper or plastics and its preparing process

A nano-paper, water-emulsion type technology, applied in adhesive types, rosin adhesives, ester copolymer adhesives, etc., can solve water resistance, moisture resistance, high and low temperature resistance, initial tack and adhesion Poor initial viscosity, poor high temperature resistance, poor high temperature resistance and other problems, to achieve the effect of good initial viscosity, good low temperature resistance and high drying performance

Inactive Publication Date: 2005-03-23
SUN YAT SEN UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Water-emulsion paper-plastic adhesives are favored for their safety and non-toxicity, especially polyvinyl acetate water-emulsion adhesives, but their shortcomings are water resistance, moisture resistance, high and low temperature resistance, initial tack and The adhesion is poor, and there is also a water-emulsion adhesive made of acrylate as a polymerized monomer. Although it has excellent low temperature resistance, broad adhesion and water resistance, its initial viscosity and high temperature resistance poor
In general, the existing water-emulsion paper-plastic adhesives generally have disadvantages such as poor initial tack, long drying time, and poor high temperature resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous emulsion type nm adhesive for paper or plastics and its preparing process
  • Aqueous emulsion type nm adhesive for paper or plastics and its preparing process
  • Aqueous emulsion type nm adhesive for paper or plastics and its preparing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The adhesive of embodiment 1 is applicable to the packaging box, bag, handicraft etc. that bonding requires excellent low temperature resistance;

Embodiment 2

[0027] The adhesive of embodiment 2 is applicable to the packaging box, bag, handicraft etc. that bonding need high temperature resistant purposes;

Embodiment 3

[0028] The adhesive of embodiment 3 is suitable for requiring good initial tack, the purposes of drying rapidly;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

An emulsion-type paper-plastic adhesive is prepared from emulsion base material (40-70 wt.%), viscosity increaser (25-50) and nm inorganic powder (5-15). The emulsion base material contains butyl acrylate (25-60 wt. portions), vinyl acetate (20-50), acrylic acid (0-10), hydroxypropyl acrylate (5-15), PVA (2-8) ammonium persulfate (0.8-3.2), emulsifier OP-10 (0.3-3), sodium laurylsulfate (0.3-3) and water (80-207). Its advantages include no poison, excellent resistance to low temp., high temp and water, good adhesion, and fast drying.

Description

technical field [0001] The invention relates to a non-toxic, emulsion-type nano paper-plastic adhesive with excellent comprehensive performance and a preparation method thereof. Background technique [0002] Paper-plastic adhesives are widely used in the printing and packaging industry, such as the bonding of packaging boxes, hand bags, stationery and handicrafts. At present, there are two main types of paper-plastic adhesives on the market: one is solvent-based (mainly using toluene as a solution), and the other is water-emulsion type (emulsion type). Solvent-based adhesives are mainly SBS glue and EVA glue. Among them, SBS glue has good frost resistance and punching resistance, but has disadvantages such as poor aging resistance, rapid adhesion decline, and poor high temperature resistance. EVA glue has excellent aging resistance and ink affinity, but its main disadvantages are poor frost resistance, stamping resistance, and high temperat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J133/04C09J193/04
Inventor 陈旭东许家瑞章明秋
Owner SUN YAT SEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com