Isomerization catalyst and preparation thereof

A catalyst and isomerization technology, applied in refined hydrocarbon oil, petroleum industry, etc., can solve problems such as unsatisfactory anti-coking ability, intensified cracking reaction, and small stability range, etc., and achieve octane recovery function Strong, inhibit polymerization coking reaction, reduce the effect of carbon deposition

Inactive Publication Date: 2004-04-14
CHINA PETROLEUM & CHEM CORP +1
View PDF2 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the anti-coking ability of the acidic zeolite impregnated oxide catalyst is not ideal, and the range of improving the octane number to restore the stability of the catalyst is not large.
In addition, the increase in the amount of L acid also intensifies the cracking reaction, generating more C 3 -C 4 On the one hand, it reduces the yield of isomerized hydrocarbons, especially high-octane multi-branched isomeric hydrocarbons, and also reduces the yield of gasoline products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0036] In this example, nano-HBeta with a grain size of about 70nm was used to prepare the n-paraffin hydroisomerization zeolite catalyst carrier.

[0037] Weigh 229.6g nano-HBeta, 140.0g Al 2 o 3 , and grind and mix them evenly, add 150ml of dilute nitric acid solution with a concentration of 3.6g / 100ml, and grind them into a powder cake with suitable humidity. Extrude into rods with a diameter of 2.0 mm on a rod extruder. After air drying at room temperature, it was dried at 120° C. for 10 hours and calcined at 520° C. for 8 hours to prepare an isomerization catalyst carrier. The number is NIS-1.

example 2

[0039] This example prepares 3.0m%NiO / nano HBeta n-paraffin hydroisomerization catalyst with a grain size of about 70nm

[0040] Weigh 100 g of the carrier in Example 1 and put it into the spray tank, and start the rotary pump. A solution containing 3 g of NiO, 52 ml of nickel nitrate, was sprayed onto the catalyst support within 30 minutes. After air drying at room temperature, it was dried at 120°C for 10 hours and calcined at 500°C for 8 hours to prepare a catalyst intermediate. The number is NIC-1.

[0041] Weigh 100ml of the above-mentioned catalyst intermediate and put it into a vertical catalyst activation furnace, treat it with water vapor at a water agent volume ratio of 3:1 and a temperature of 480° C. for 8 hours, and stop the water inlet. then use N 2 After displacing water vapor with 95% nitrogen-oxygen mixed gas for 4 hours, control the temperature at 30° C. / hour to cool down to room temperature, discharge, and make an isomerization catalyst. The number is NI...

example 3

[0052] In this example, the n-alkane hydroisomerization zeolite catalyst carrier was prepared by nano-HBeta with a grain size of about 110 nm.

[0053] Weigh 229.6g nano-HBeta, 140.0g Al 2 o 3 , and grind and mix them evenly, add 150ml of dilute nitric acid solution with a concentration of 3.6g / 100ml, and grind them into a powder cake with suitable humidity. Extrude into rods with a diameter of 2.0 mm on a rod extruder. After air drying at room temperature, it was dried at 120° C. for 10 hours and calcined at 520° C. for 8 hours to prepare an isomerization catalyst carrier. The number is NIS-2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
grain sizeaaaaaaaaaa
grain sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a normal paraffin hydrocarbon hydrogenation isomerization catalyst using nano HBeta zeolite as carrier, and the grain size of nano HBeta is 30.0nm-180.0 nm. Said invented catalyst can shorten the dwell time of n-carbonionic intermediate in catalyst channel, raise selectivity of isomerization product and at the same time can inhibit the secondary reaction of polymeric coking, etc. Said invention also provides the preparation method of said catalyst.

Description

1. Technical field [0001] The invention relates to an isomerization catalyst and its preparation, which is applied in a combination process of hydrogenation and upgrading of inferior catalytic cracking (FCC) gasoline. While greatly reducing the content of harmful sulfur compounds and olefin compounds in low-quality FCC gasoline, the resulting low-sulfur, low-olefin content clean gasoline has a small loss in antiknock index ((R+M) / 2). 2. Background technology [0002] With the rapid development of my country's automobile industry, the air pollution caused by automobile exhaust has attracted more and more attention. Due to the reduction of sulfur and olefin content in gasoline, CO and NO in automobile exhaust can be reduced X Therefore, the "Control Standards for Hazardous Substances in Motor Gasoline" formulated by the State Environmental Protection Administration of my country requires that the sulfur content of motor gasoline in my country is less than 800 μg / g, and the ol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10G45/60
Inventor 赵乐平庞宏周勇段为宇张丽娟
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap