Normal temperature three-in-one phosphorizing agent capable of cleaning and derusting synchronously and preparing process thereof

A rust-removing phosphating agent, a three-in-one technology, applied in the direction of metal material coating process, etc., can solve the problems affecting the quality, output or cost of coating production, secondary discharge of waste residue pollution, unsatisfactory phosphating effect, etc. problem, to achieve the effect of low price, many times of repeated use, and low production cost

Inactive Publication Date: 2004-11-17
赵惠霖
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still problems such as unsatisfactory phosphating effect to varying degrees, many restrictions on the use of phosphating agents, high temperature requirements for the use e

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Example 1. Follow the steps below to make a three-in-one cleaning, rust, and phosphating agent at room temperature.

[0022] a. Add 30Kg of water, 2Kg of phosphoric acid and 4Kg of ethanol in the reaction kettle, add 5Kg of acetone under the stirring of the mixer, and obtain liquid A after mixing well;

[0023] b. Add 0.1Kg of non-ionic active agent (such as Tx-10) into the emulsifier, add 1Kg of water for emulsification, and obtain liquid B after emulsification for 3-5 minutes;

[0024] c. Add liquid B to liquid A, add 0.5Kg of hydroquinone after stirring, and mix well to obtain the finished product.

Embodiment 2

[0025] Example 2. Follow the steps below to make a three-in-one cleaning, rust, and phosphating agent at room temperature.

[0026] a. Add 24Kg of water, 5Kg of phosphoric acid and 7Kg of ethanol into the reaction kettle, add 3Kg of acetone under stirring with a mixer, and mix well to obtain liquid A;

[0027] b. Add 0.2Kg of non-ionic active agent (such as Tx-10) into the emulsifier, add 2Kg of water for emulsification, and obtain liquid B after emulsification for 3-5 minutes;

[0028] c. Add liquid B into liquid A, add 0.8Kg of hydroquinone after stirring, and mix well to obtain the finished product.

Embodiment 3

[0029] Example 3. Follow the steps below to make a three-in-one cleaning, rust, and phosphating agent at room temperature.

[0030] a. Add 25Kg of water, 8Kg of phosphoric acid and 3Kg of ethanol into the reaction kettle, add 8Kg of acetone under stirring with a mixer, and mix well to obtain liquid A;

[0031] b. Add 0.5Kg of non-ionic active agent (such as Tx-10) into the emulsifier, add 5Kg of water for emulsification, and obtain liquid B after emulsification for 3-5 minutes;

[0032] c. Add liquid B into liquid A, add 0.7Kg of hydroquinone after stirring, and mix well to obtain the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a normal temperature three-in-one phosphorizing agent capable of cleaning and derusting synchronously and preparing process thereof, wherein the bonderite comprises phosphorus acid, methyl ketone, ethanol, hydroquinone, non-ionic active agent and water as raw material, which is prepared through the steps of agitating, emulsifying and restirring.

Description

technical field [0001] The invention relates to a phosphating agent used in the steel surface coating process and a preparation method thereof. Background technique [0002] Phosphating treatment on the surface of steel objects is an important process in the steel coating process. At present, various phosphating agents (also known as phosphating solutions) used in surface treatment of steel objects can basically meet the needs of coating production. However, there are still problems such as unsatisfactory phosphating effect to varying degrees, many restrictions on the use of phosphating agents, high temperature requirements for the use environment, and high energy consumption; Pollution problems caused by secondary discharge of waste residues. The above problems directly affect the quality, output or cost of coating production. Contents of the invention [0003] The object of the present invention is to provide a three-in-one cleaning, derusting and phosphating agent at...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/07C23G1/08
Inventor 赵惠霖
Owner 赵惠霖
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap