Abstract

A Platinum temperature sensor comprises a ceramic substrate and a platinum thin-film resistor applied to said ceramic substrate, a ceramic cover layer and a connecting layer generated from a ceramic green layer by pressure and temperature treatment. The ceramic cover layer is connected with the ceramic substrate in such a way via the connecting layer that the platinum thin-film resistor is sealingly encapsulated with regard to the environment.

Description

[0001] 1. Field of the Invention[0002] The present invention relates to a platinum temperature sensor and a method for producing the same, and in particular to a platinum temperature sensor in the case of which a platinum thin-film resistor, which is applied to a ceramic substrate, is used for temperature detection.[0003] 2. Description of Prior Art[0004] A known platinum temperature sensor is shown in FIG. 3. In this known platinum temperature sensor, a platinum thin-film resistor 2 is applied to a ceramic substrate 4 which normally consists of aluminum oxide Al.sub.2O.sub.3. In the area in which the platinum thin-film resistor 2 is formed, a protective glaze 6 is provided on the surface of the ceramic substrate 4. The platinum layer, in which the platinum thin-film resistor 2 is normally formed in a meandering shape, is additionally patterned so as to include connecting areas 8 having lead wires 10 connected thereto in an electrically conductive manner for taking the sensor signal...

AI Technical Summary

Benefits of technology

[0026] The present invention is based on the knowledge that ceramic materials, especially aluminum oxide Al.sub.20.sub.3 are in-sensitive to the above-described current induced decomposition, and thus this material that in addition is used in thin-film platinum temperature sensors as substrate material for the platinum film can advantageously also be used as protective material for capsulation of the platinum film layer. Thus, the problems of electrochemical decomposition and the connected deterioration of properties of the platinum temperature sensors are prevented, even when the protective cover is realized from a ceramic material.

Problems solved by technology

The field of use of the platinum temperature sensor, which is shown in FIG. 3 and which is implemented in thin-film technology, is normally limited to 600.degree. C.

By purposefully selecting the composition of the protective glaze 6, it has already been possible to find satisfactory solutions for some cases of use, whereas in very particular fields of application, e.g. in special cases of use in the field of automotive engineering, the results do not satisfy all requirements.

The resultant material migration has a negative influence on the properties of the platinum so that the sta-bility of the sensors and, consequently, the measuring accuracy are impaired.

By purposefully selecting the composition of the protective glazes, improvements could be achieved to a certain extent, but it was impossible to find protective glazes that withstand the electrochemical decomposition by the measurement current in the case of continuous loads in a temperature range of 1,000.degree. C. or more than 1,000.degree. C.

On the other hand the inventive platinum temperature sensor supplies reliable measurement results even in the case of continuous loads in a high temperature range of for example 1000.degree. C. or more than 1000.degree. C., since the above-described disadvantageous decomposition phenomenons do not occur in the case of the inventive platinum film temperature sensor.