Flame-proof armored rope core conveyer belt

A steel cord core and conveyor belt technology, which is applied in the field of improved design of the rubber compound formulation for the flame-retardant covering rubber layer, can solve the problems of low performance of the rubber layer, inability to effectively reduce friction, and the temperature of the friction drum exceeding the index, etc., to achieve improvement The effects of carbonization speed, prevention of excessive temperature rise, and easy mixing and processing

Active Publication Date: 2009-02-04
QINGDAO RUBBER SIX CONVEYER BELT
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] As mentioned above, the covering rubber layer of the existing flame-retardant tape can play flame-retardant and antistatic effects to a certain extent, but the performance of the rubber layer is low, and the wear resistance, tensile performance, and flame-retardant properties of the rubber material are relatively low. And other comprehensive properties are far below the requirements of the MT668-1997 standard, especially when there are technical problems such as sticking to the car during the rubber mixing process, because there is no corresponding method to solve it, the physical properties of the mixed rubber have to be reduced to meet the production process. Require
In addition, since the existing flame-retardant adhesive layer does not contain solid flame-retardant lubricants, the flame-retardant tape cannot effectively reduce the friction force during the friction drum test, resulting in the temperature of the friction drum exceeding the target.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Embodiment 1, the flame-retardant steel cord conveyor belt of the present invention includes a steel cord core and a flame-retardant covering rubber layer. in:

[0047] The formula of the flame retardant covering adhesive layer rubber compound, its ratio by weight:

[0048] Neoprene, 90 parts;

[0049] Zinc oxide, 8 parts;

[0050] Accelerator diphenylguanidine, 7 parts;

[0051] Conductive carbon black, 14 parts;

[0052] Antimony trioxide, 40 parts;

[0053] Triaryl phosphate, 6 parts;

[0054] Chlorinated polyethylene, 5 parts;

[0055] White carbon black, 20 parts;

[0056] Wear-resistant flame retardant MB-202, 4 parts;

[0057] Butadiene gum, 10 parts;

[0058] 3 other servings.

Embodiment 2

[0059] Embodiment 2, the described flame-retardant steel cord conveyor belt, the material formula of its flame-retardant covering rubber layer rubber is by weight:

[0060] Neoprene, 95 parts;

[0061] Magnesium oxide, 12 parts;

[0062] Accelerator hexamethylenetetramine, 5 parts;

[0063] Conductive carbon black, 10 parts;

[0064] Decabromodiphenyl ether, 35 parts;

[0065] Triaryl phosphate, 12 parts;

[0066] Chlorinated polyethylene, 10 parts;

[0067] White carbon black, 15 parts;

[0068] Wear-resistant flame retardant melamine cyanurate complex salt, 6 parts;

[0069] Natural rubber, 5 parts;

[0070] 3 other servings.

Embodiment 3

[0071] Embodiment 3, the flame-retardant steel cord conveyor belt, the material formula of its flame-retardant covering rubber layer rubber is by weight:

[0072] Neoprene, 100 parts;

[0073] Magnesium oxide, 16 parts;

[0074] Accelerator tetramethylthiuram disulfide, 3 parts;

[0075] Conductive carbon black, 8 parts;

[0076] Pentaerythritol, 30 parts;

[0077] Triaryl phosphate, 15 parts;

[0078] Chlorinated polyethylene, 15 parts;

[0079] White carbon black, 10 parts;

[0080] Wear-resistant flame retardant tripolyamine cyanurate complex salt, 8 parts;

[0081] 3 other servings.

[0082] The above-mentioned content is the basic content of the flame-retardant steel cord conveyor belt of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a flame-proof steel belt conveyor, which is based on the adhesive property between the flame-proof layer and the steel wire to improve the flame-proof, anti-abrasion, and conducting static electricity property of glue material by adjusting the proportion of raw material, adding flame-proof lubricant and using new conducting carbon black, to improve the whole property of invention and meet the standard of MT668-1997. Said invention mainly comprises steel wires and flame-proof covering glue layer. Wherein, the formulation of flame-proof covering glue layer comprises: neoprene in 80-100 deals; zinc oxide in 4-20 deals; accelerant (as melaniline) in 2-8 deals; conducting carbon black in 4-15 deals; solid flame-proof agent (as antimony oxide) in 20-59 deals; liquid flame-proof agent (as triaryl phosphate) in 5-20 deals; white carbon black in 5-20 deals; and solid frame-proof lubricant MB-202 in 3-8 deals.

Description

technical field [0001] The invention is a new type of flame-retardant steel cord conveyor belt, in particular, it is mainly aimed at the improved design of the formula of the flame-retardant covering rubber layer of the conveyor belt. Background technique [0002] At present, in various coal mine enterprises, flame-retardant steel cord conveyor belts are mostly used in long-distance transportation in order to improve safety. Especially when working underground in coal mines, it is required to ensure flame retardant safety, and the conveyor belt used must have a relatively high flame retardant performance. [0003] The flame-retardant covering rubber layer of the existing flame-retardant steel cord conveyor belt is generally made of rubber, vulcanizing agent, anti-aging agent, stabilizer, flame retardant, antistatic agent and other materials. After cold pressing and bonding with the steel wire rope, a flame-retardant conveyor belt with upper and lower flame-retardant coverin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B65G15/38
Inventor 孙连生逄健由世峰臧学昌
Owner QINGDAO RUBBER SIX CONVEYER BELT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap