Straight arc casting machine alloy steel sheet billet continuous casting foot roller segment narrow surface cooling method

A low-alloy steel and slab continuous casting technology, which is applied in the field of metal continuous casting slab cooling and surface quality control, can solve the problems that the corner transverse crack defects cannot be completely eliminated, achieve the elimination of corner transverse crack defects, and improve cooling uniformity The effect of good plasticity and good ductility

Inactive Publication Date: 2009-04-08
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the deficiency that the continuous casting slab of the existing straight arc type casting machine cannot completely eliminate the defect of the transverse crack at the corner, the technical problem to be solved by the present invention is to provide a straight arc type casting machine low alloy steel slab continuously cast with a narrow foot roll section. Surface cooling method, which can effectively eliminate the generation of transverse crack defects at the corners of low-alloy steel slabs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Straight arc casting machine alloy steel sheet billet continuous casting foot roller segment narrow surface cooling method
  • Straight arc casting machine alloy steel sheet billet continuous casting foot roller segment narrow surface cooling method
  • Straight arc casting machine alloy steel sheet billet continuous casting foot roller segment narrow surface cooling method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A converter steelmaking plant adopts the technology of the present invention to control the transverse crack defect at the corner of the P510L steel billet for automobile beam plate. The chemical composition of P510L steel except Fe and a small amount of impurities is shown in Table 1. In continuous casting production, the use of figure 1 The nozzle structure shown is composed of three parts: nozzle 2, coupling screw 1 and coupling nut 3, and the nozzle is designed according to the nozzle pressure-flow characteristics shown in Table 2, and the schematic diagram of the vertical and horizontal layout of the narrow surface nozzle of the foot roller section See figure 2 with image 3 . Before casting, the width of the slab is set to 1050mm, the thickness of the slab is set to 200mm, the casting speed of the casting machine is 1.40m / min during continuous casting, and the water volume of the narrow surface of the foot roll section is set to 67.1L / min. After the casting i...

Embodiment 2

[0033] A converter steelmaking plant adopts the technology of the present invention to control the transverse crack defect at the corner of the P510L steel billet for automobile beam plate. The chemical composition of P510L steel except Fe and a small amount of impurities is shown in Table 1. In continuous casting production, the same nozzle as in Example 1 is used, and the schematic diagram of the arrangement of the narrow surface nozzles in the foot roll section along the longitudinal and transverse directions is shown in figure 2 with image 3 . Before casting, the width of the slab is set to 1300mm, the thickness of the slab is set to 200mm, the casting speed of the casting machine is 0.80m / min during continuous casting, and the water volume of the narrow surface of the foot roll section is set to 45.2L / min. After the casting is completed, the surface inspection and low-magnification inspection of the produced slab are carried out. The inspection shows that the depth of...

Embodiment 3

[0036] A converter steelmaking plant adopts the technology of the present invention to control the transverse crack defect at the corner of the P590L steel billet for automobile beam plate. The chemical composition of P590L steel except Fe and a small amount of impurities is shown in Table 3. In continuous casting production, the same nozzle as in Example 1 is used, and the schematic diagram of the arrangement of the narrow surface nozzles in the foot roll section along the longitudinal and transverse directions is shown in figure 2 with image 3 . Before casting, the width of the slab is set to 1100mm, the thickness of the slab is set to 200mm, the casting speed of the casting machine is 1.20m / min during continuous casting, and the water volume of the narrow surface of the foot roll section is set to 59.8L / min. After the casting is completed, the surface inspection and low-magnification inspection of the produced slab are carried out. The inspection shows that the depth of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a straight-curved type casting machine low-alloy steel slab continuous casting full-rolling section narrow face cooling method, and is aimed at solving the problem of that on the casting blank surface corner portion of low-alloy steel the transverse crack can be easily produced. Said invention belongs to the field of metal continuous casting blank cooling and surface quality control technology. Said method is characterized by that in the full-rolling section of continuous casting straight-curved type casting machine slab said invention utilizes the nozzles which are symmetrically mounted at left side and right side of casting blank pouring direction to cool the narrow face of said casting blank, and adopts rectangular nozzles to symmetrically and simultaneously cool the narrow faces of left and right two sides of casting blank. Said invention also discloses a kind of rectangular nozzle for said method, the water outlet hole of its sprayer is a hole with rectangular section. Said invention can reduce casting blank cooling strength of full-rolling section under the crystallizer and can improve casting blank cooling uniformity, so that it can eliminate casting blank surface corner portion transverse crack defect of continuously-cast high-strength low-alloy steel whose steel quality is P510L, P590L, J55 and X52, etc.

Description

technical field [0001] The invention relates to the technical field of metal continuous casting slab cooling and surface quality control, in particular to a metal continuous casting slab cooling method for eliminating transverse crack defects at corners of low alloy steel casting slabs. Background technique [0002] At present, vanadium-containing microalloyed steels are highly sensitive to cracks. In the process of continuous casting, because V in solid solution at high temperature is dynamically precipitated or statically precipitated at the austenite grain boundary in the form of V(CN) when the temperature is lowered, the crack sensitivity is increased. Especially for straight-arc caster slab casters, the slab is subjected to compressive stress and tensile stress on the inner and outer arc sides of the slab in the bending area, while in the straightening area, the inner and outer arc sides of the slab are subjected to compressive stress and tensile stress respectively. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22D11/22
Inventor 陈永赵代琼吴国荣曾建华杨素波
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com