Polycarboxylic acid series water reducing agent using allyl polyglycol as raw material and synthesizing method thereof

A polyethylene glycol and polycarboxylic acid-based technology, applied in the field of novel polycarboxylic acid-based water reducing agent and its synthesis, can solve the problem of no synthesis process and the like, and achieve the effect of low cost

Inactive Publication Date: 2009-09-30
TONGJI UNIV
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are no domestic research results on the synthesis process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Example 1, the new polycarboxylate water reducer using allyl polyethylene glycol (molecular weight 1000) as raw material adopts the following synthesis process: APEG (molecular weight 1000) 31.00% (mass percentage, the same below), maleic anhydride Add 4.10%, 4.90% methyl acrylate, and 60.00% water to the reaction kettle in turn, pass through nitrogen protection, add ammonium persulfate with a total monomer mass of 8%, react at 90°C for 6 hours, and add 50% sodium hydroxide solution , adjust the pH to 7. Adding 1.0% of the water-reducing agent to the weight of the cement can make the fluidity of the cement paste with a water-cement ratio of 0.29 be 290mm, and there is no loss in 6 hours.

Embodiment 2

[0015] Example 2, the new polycarboxylate water reducer using allyl polyethylene glycol (molecular weight 2500) as raw material adopts the following synthesis process: APEG (molecular weight 2500) 28.50% (mass percentage, the same below), maleic anhydride Add 5.55%, 5.95% methyl acrylate, and 60.00% water to the reaction kettle in turn, pass through nitrogen protection, add stannous sulfate with 6% of the total mass of the monomer, react at 90°C for 6 hours, and add 50% sodium hydroxide solution , adjust the pH value to 7. Adding 1.2% of the water reducing agent by weight of the cement can make the fluidity of the cement paste with a water-cement ratio of 0.29 be 275mm, and there is no loss in 5 hours.

Embodiment 3

[0016] Example 3, the new polycarboxylate water reducer using allyl polyethylene glycol as raw material adopts the following synthesis process: APEG (molecular weight 1500) 33.50% (mass percentage, the same below), maleic anhydride 3.50%, acrylic acid Methyl ester 3.00%, water 60.00%, pass through nitrogen protection, add ammonium persulfate with 5% of total monomer mass, add stannous sulfate with 4% total monomer mass, react at 95°C for 7 hours, add 50% hydrogen Sodium oxide solution, adjust the pH value to 7. Adding 0.8% of the water-reducing agent to the weight of the cement can make the fluidity of the cement paste with a water-cement ratio of 0.29 be 270mm, and there is no loss in 5 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of building materials, and in particular relates to a polycarboxylic acid-based water reducer using allyl polyethylene glycol as a raw material and a synthesis method thereof. The water reducer is prepared from raw materials such as allyl polyethylene glycol, maleic anhydride, methyl acrylate, ammonium persulfate, stannous sulfate, sodium hydroxide and water in an appropriate mass ratio, protected by nitrogen, and heated for reaction. get. Compared with the prior art, the invention does not need two-step synthesis, the raw material is cheap, the performance of the craft product is stable, and has good market prospect.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a novel polycarboxylate water reducer using allyl polyethylene glycol (APEG) as a raw material and a synthesis method thereof. Background technique [0002] Adding an appropriate amount of water reducing agent to concrete can significantly improve the work performance of fresh concrete and the comprehensive performance of hardened concrete. Polycarboxylate superplasticizer, as a new generation of product, has unique advantages such as low dosage, high water reducing rate, no retardation, low slump loss, and environmental protection. It is suitable for ordinary concrete and special concrete such as high-strength, self-compacting and fair-faced concrete. [0003] At present, the synthesis process of polycarboxylate water reducer in the market is mainly composed of MPEG, methacrylic acid and other monomers, under the action of polymerization inhibitor and cat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/24C08F216/16C08F220/14C08F222/06C04B103/30
CPCC04B24/267C04B2103/302
Inventor 孙振平黄雄荣
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap