Waterproof color building sealing adhesive and its prepn process

A technology for adhesives and construction, applied in the direction of adhesive types, cellulose adhesives, monocarboxylic acid ester copolymer adhesives, etc., can solve the problem of increasing cleaning labor and cost, easily polluting the surface of buildings, Waste of caulking materials and other problems, to achieve the effect of material saving, good waterproof and convenient operation

Inactive Publication Date: 2007-08-22
SOUTH CHINA UNIV OF TECH +1
View PDF1 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, many other shortcomings of cement mortar in the bonding of interior and exterior walls of buildings still cannot be solved; and because the bonding and caulking are divided into two processes, it is more complicated and time-consuming; Applying on a large area will not only waste 1 / 3~1 / 2 of the caulking material, but also easily pollute the surface of the building, increasing the labor and cost of cleaning

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] According to the following weight ratio, white cement, lignin, pigment, vinyl acetate copolymer latex powder are mixed uniformly to obtain mixture (1); quartz sand, water-based cellulose ether, and organic carboxylic acid metal salt are uniformly mixed to obtain mixture (2 ); the mixture of (1) and (2) obtained above is uniformly mixed to obtain a waterproof yellow caulking adhesive for construction.

[0026] The weight ratio is as follows:

[0027] 15kg white cement

[0028] Quartz sand 80 kg

[0029] Water-based cellulose ether (hydroxypropyl methylcellulose) 0.6 kg

[0030] Lignin 0.1 kg

[0031] Pigment (iron oxide yellow) 0.5 kg

[0032] Vinyl acetate copolymer latex powder 1.8 kg

[0033] Waterproofing agent (zinc ten-carbon carboxylate) 2 kg

[0034] Total 100kg

[0035] It is used for bonding and caulking of interior and exterior wall tiles. After 5 years, it will be waterproof, free from loosening and falling off, and without cracks.

Embodiment 2

[0037] According to the following weight ratio, white cement, lignin, pigment, vinyl acetate copolymer latex powder are mixed uniformly to obtain mixture (1); quartz sand, water-based cellulose ether, and organic carboxylic acid metal salt are uniformly mixed to obtain mixture (2 ); the mixture of (1) and (2) obtained above is uniformly mixed to obtain a waterproof white caulking adhesive for construction.

[0038] The weight ratio is as follows:

[0039] 50kg white cement

[0040] Quartz sand 45 kg

[0041] Water-based cellulose ether (hydroxyethyl methylcellulose) 0.1 kg

[0042] lignin 2 kg

[0043] Pigment (titanium dioxide) 0.05 kg

[0044] Vinyl acetate copolymer latex powder 1.85 kg

[0045] Waterproofing agent (sodium seventeen-carbon carboxylate) 1 kg

[0046] Total 100kg

[0047] Used for indoor and outdoor ground stone bonding and caulking, waterproof, no loosening and falling off, and no cracks after 5 years.

Embodiment 3

[0049] According to the following weight ratio, ordinary cement, lignin, pigment, vinyl acetate copolymer latex powder are mixed uniformly to obtain mixture (1); quartz sand, water-based cellulose ether, organic carboxylic acid metal salt are mixed uniformly to obtain mixture (2 ); The above obtained (1), (2) mixture is uniformly mixed to obtain a waterproof black caulking adhesive for construction.

[0050] The weight ratio is as follows:

[0051] Ordinary cement 25 kg

[0052] Quartz sand 67 kg

[0053] Water-based cellulose ether (hydroxyethyl methylcellulose) 0.4 kg

[0054] Lignin 0.5 kg

[0055] Pigment (carbon black) 2 kg

[0056] Vinyl acetate copolymer latex powder 5 kg

[0057] Waterproofing agent (aluminum carboxylate of 20 carbons) 0.1 kg

[0058] Total 100kg

[0059] It is used for bonding and caulking of interior and exterior wall tiles. After 5 years, it will be waterproof, free from loosening and falling off, and without cracks.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is one kind of waterproof color building sealing adhesive and its preparation process. The waterproof color building sealing adhesive is produced with cement, quartz sand, water soluble cellulase, lignin, pigment, ethyl acetate copolymer latex powder, organic carboxylic metal salt powder and through homogeneous mixing. The adhesive of the present invention can form waterproof surface and possesses the features of waterproofing, adhering, beautiful appearance, high durability and environment friendship. It has integral joint filling and adhering functions and low cost, and is suitable for both joint filling and adhering of outer wall tile, floor tile, inner wall tile, stone material and plaza tile.

Description

technical field [0001] The invention relates to the field of building materials, and relates to a waterproof color caulking adhesive for construction with integrated functions of waterproofing, bonding and caulking and a preparation method thereof. Background technique [0002] At present, cement mortar is used to bond the inner and outer walls of buildings with magnetic sheets, tiles, cultural bricks, stones, etc., but the bonding strength is low, especially the initial bonding performance is relatively poor, and thick layer construction is usually used. There are many disadvantages, such as: easy to sag, easy to fall off, crack, etc. during construction, especially because the current building walls are stipulated to use lightweight bricks, hollow bricks, fly ash bricks, etc., the walls are very permeable, and cement mortar is not waterproof. Once water seeps through the gaps between the magnetic sheets or tiles, it will cause water seepage and leakage in the entire buildi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J131/04E04B1/68C09J101/26
Inventor 彭峰刘德亮
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More