Novel underwater sound absorption rubber product and preparation method thereof

A sound-absorbing rubber, a new technology, applied in the direction of sound-generating devices and instruments, can solve the problems of increased use cost and reduced work efficiency, and achieve the effects of improving service life, maintaining water quality, and good sound-absorbing effect

Inactive Publication Date: 2007-09-26
TIANJIN RUBBER IND RES INST
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In order to keep the water clean, the pool must be changed regularly, so the cost of use increases and the work efficiency decreases

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] The weight ratio of each component is:

[0052] (1) Synthetic rubber:

[0053] Butyl rubber (grade 268 or 301) 1000g 100 parts,

[0054] (2) Compounding agent:

[0055] 5 parts of zinc oxide 50g,

[0056] Stearic acid 25g 2.5 parts,

[0057] Anti-aging agent 264 10g 1 part,

[0058] High wear-resistant carbon black N330 350g 35 parts,

[0059] Aromatic oil 250g 25 parts,

[0060] Paraffin wax 60g 6 parts,

[0061] HY-2056 resin 280g 28 parts,

[0062] A total of 1025g, 102.5 parts;

[0063] (3) Damping sound-absorbing filler:

[0064] 100 mesh vermiculite powder 100g 10 parts,

[0065] 20 mesh vermiculite powder 110g 11 parts,

[0066] 100 mesh mica 750g 75 parts,

[0067] A total of 960g 96 servings;

[0068] Total 2985g 298.5 servings.

[0069] The preparation method is:

[0070] 1. Mixing:

[0071] X(s)N-75 type internal mixer is used for mixing, and the order of feeding is: after the synthetic rubber is plasticized, add the dispersant stearic acid, act...

Embodiment 2

[0077] The weight ratio of each component:

[0078] (1) Synthetic rubber: basic quantity 100%

[0079] Butyl rubber (grade 268) 900g 90 parts,

[0080] Neoprene (grade 230) 100g 10 parts,

[0081] Total 1000g 100 servings;

[0082] (2) Compounding agent:

[0083] 5 parts of zinc oxide 50g,

[0084] 4 parts of stearic acid 40g,

[0085] Anti-aging agent (264) 10g 1 part,

[0086] High wear-resistant carbon black N330 350g 35 parts,

[0087] Aromatic oil 150g 15 parts,

[0088] 10 parts of naphthenic oil 100g,

[0089] Paraffin wax 60g 6 parts,

[0090] HY-2056 resin 250g 25 parts,

[0091] A total of 1010g 101 servings;

[0092] (3) Damping sound-absorbing filler:

[0093] Mica (100 mesh) 750g 75 parts,

[0094] 100 mesh vermiculite powder 100g 10 parts,

[0095] 20 mesh vermiculite powder 120g 12 parts,

[0096] Total 970g 97 servings,

[0097] Total 2980g 298 servings;

[0098] Using the preparation method of Example 1, the novel underwater sound-absorbing ru...

Embodiment 3

[0100] The weight ratio of each component:

[0101] (1) Synthetic rubber basic quantity 100%

[0102] Butyl rubber (grade 268) 900g 90 parts,

[0103] Chlorobutyl rubber (grade 1068) 100g 10 parts,

[0104] Total 1000g 100 servings,

[0105] (2) Compounding agent:

[0106] 5 parts of zinc oxide 50g,

[0107] Stearic acid 30g 3 parts,

[0108] Anti-aging agent (264) 10g 1 part,

[0109] High wear-resistant carbon black N330 350g 35 parts,

[0110] Talcum powder 100g 10 parts,

[0111] Aromatic oil 120g 12 parts,

[0112] Paraffin wax 60g 6 parts,

[0113] HY-2056 resin 220g 22 parts,

[0114] Accelerator Na22 2g 0.2 part,

[0115] Accelerator DM 2g 0.2 part,

[0116] A total of 944g 94.4 servings;

[0117] (3) Damping sound-absorbing filler:

[0118] Mica 700g 70 parts,

[0119] 100 mesh vermiculite powder 100g 10 parts,

[0120] 20 mesh vermiculite powder 100g 10 parts,

[0121] Total 900g 90 servings;

[0122] Total 2844g 284.4 servings.

[0123] Using the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sound absorption coefficientaaaaaaaaaa
Login to view more

Abstract

The invention discloses a new-typed underwater acoustic rubber product and making method, which comprises the following parts: 100g synthetic rubber, 1-10g zinc oxide, 1-5g stearic acid, 0.5-2g antiager 264, 30-45g high abrasion-proof carbon black N330, 0-90g light-weighted calcium carbonate, 0-50g talcum powder, 1-30g aromatic oil, 0-20g naphthenic oil, 1-10g paraffin, 15-40g HY-2056 resin, 0-3g Na22, 0-5g DM, 50-100g mica powder, 8-15g 100-order vermiculite powder and 8-15% 20-order vermiculite. The making method comprises the following steps: adding raw material to blend and melt; cooling; adding vulcanizer and accelerant to blend evenly; setting the roll distance at 8mm under not less than 65 deg.c; adding 20-order vermiculite; sulfurizing; moulding; fitting for making kinds of shape and standard underwater acoustic rubber product.

Description

Technical field: [0001] The invention relates to an underwater sound-absorbing rubber product and a preparation method. In particular, a novel underwater sound-absorbing rubber product and a preparation method thereof. Background technique: [0002] The anechoic pool is a free sound field created in the laboratory. It can simulate the marine environment, identify, calibrate and conduct acoustic navigation tests on underwater acoustic instruments. It is essential for the research and development of underwater acoustic science and the production of underwater acoustic testing instruments. One of the devices. The underwater sound-absorbing rubber product is the laying material of the anechoic pool. Its special underwater sound-absorbing performance makes the anechoic pool similar to an anechoic chamber, and it is the main component of the anechoic pool. [0003] Since the underwater sound-absorbing rubber products have been soaked in the muffler pool for a long time, it shoul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/00C08K5/09G10K11/162C08L11/00C08L91/06C08K3/26C08K3/36C08K3/04C08K3/22
Inventor 张景亮张立侠郑秀琴
Owner TIANJIN RUBBER IND RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap