Magnesium waste slag building brick and producing method

A technology for magnesium slag and building bricks, which can be used in solid waste management, sustainable waste treatment, climate sustainability, etc., and can solve problems such as air and water pollution, land occupation, and magnesium slag hazards.

Inactive Publication Date: 2011-09-28
肖力光 +1
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since there is no feasible way of harmless treatment and reuse of magnesium slag, the discharge of solid waste that is higher than the proportion of the product not only needs to occupy land, but also pollutes air and water sources with the wind and rain.
The quantity and harm of magnesium slag are a big burden for magnesium production enterprises

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Take 100 parts by weight of magnesium slag; 2 parts by weight of composite activator; 50 parts by weight of foundry sand; 50 parts by weight of slag; 20 parts by weight of slag powder; 20 parts by weight of diatomite; 20 parts by weight of cement; 5 parts by weight of acrylonitrile fiber; 5 parts by weight of polyvinyl formal water-soluble polymer.

[0023] Chenfu in magnesium slag water for 3 days, after drying, grind into powder, powder particle size 2000cm 2 / g. Diatomaceous earth was calcined at 600°C for 2 hours, and ground into 1500cm 2 / g particle size powder. The slag is ground into 3000cm 2 / g of powder. Slag or broken into particles with a particle size of 5-20mm. The straw is broken into pieces with a length of 5-20mm.

[0024] Add the required materials into the mixing container according to the above dosage ratio, add appropriate amount of water, stir evenly, pour into the brick mold, and demould after solidification. According to the conventional cu...

Embodiment 2

[0026] 100 parts by weight of magnesium slag; 50 parts by weight of composite activator; 500 parts by weight of sand; 500 parts by weight of stone powder; 100 parts by weight of cement; 40 parts by weight of straw; 20 parts by weight of polypropylene fiber; 50 parts by weight of cellulose.

[0027] Chenfu in magnesium slag water for 10 days, after drying, grind into powder, powder particle size 8000cm 2 / g. Stone powder particle size 5-20mm. The straw is broken into pieces with a length of 5-20mm. Other processes are with embodiment 1.

Embodiment 3

[0029] Take 100 parts of magnesium slag; 30 parts by weight of composite activator; 200 parts by weight of foundry sand; 200 parts by weight of slag; 200 parts by weight of stone powder; 50 parts by weight of slag powder; 20 parts by weight of permanent polymer.

[0030] Diatomaceous earth was calcined at 750°C for 1 hour, and ground into 6000cm 2 / g particle size powder. The slag is ground into 8000cm 2 / g of powder. Other processes are with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

A brick as building material is prepared from magnesium dregs, composite trigger, sand or casting sand, slag or stone powder, water, and optional slag powder, ground diatomite, cement, and surface treated straw, stalk, fibers or polymer through respective grinding, mixing, stirring, moulding, demoulding, and curing.

Description

technical field [0001] The invention belongs to the field of construction, and in particular relates to wall masonry materials. Background technique [0002] Magnesium slag is the waste slag produced during the smelting of metal magnesium. For every ton of magnesium produced, there are 20 tons of magnesium slag and 10 tons of slag. Since there is no feasible way of harmless treatment and reuse of magnesium slag at present, the discharge of solid waste that is higher than the proportion of products not only needs to occupy land, but also pollutes air and water sources with wind and rain. The quantity and harm of magnesium slag are a great burden for magnesium production enterprises. In today's society where the voice of environmental protection is getting higher and higher, the treatment and utilization of magnesium slag and the elimination of the pollution caused by magnesium slag to the environment are problems that every magnesium production enterprise must solve as soon ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B18/14C04B14/06C04B18/06C04B18/12C04B14/08C04B28/00C04B18/24
CPCY02W30/91
Inventor 肖力光
Owner 肖力光