Polishing brick with natural cave stone imitated lines

A technique of polishing tiles and imitating nature, which is applied in the field of polished tiles, and can solve problems such as hardness, monotonous surface changes of ceramic products, and unrealistic texture textures, etc.

Active Publication Date: 2010-09-01
GUANGDONG JIAJUN CERAMICS
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In order to pursue natural style, the existing architectural ceramic materials carry out different processing on the surface during the manufacturing process of ceramic products, such as forming natural decorative effects such as stone grain, flowing water grain, wood grain, etc. through mold pressing or glazing, but these These processing methods all have obvious artificial factors, which make the surface changes of ceramic products monotonous, and the texture texture is not realistic and stiff.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0006] This embodiment has bottom layer material and surface layer material the same as common polished brick, and bottom layer material accounts for 60%~70% of whole brick weight composition, and surface layer material accounts for 30%~40% of whole brick weight; The difference is that the surface material contains 20% to 25% by weight of low-temperature albite, calcite and clay, and the other 80% to 75% by weight is the same as that of ordinary polished tiles. Wherein, the weight components of low-temperature albite, calcite, and clay respectively account for 55%-65%, 20%-25%, and 15%-20% of the total content of low-temperature albite, calcite, and clay in the surface material, The content of sodium in low temperature albite is required to be above 9%.

[0007] The production process of the polished brick with imitation natural travertine texture of the present embodiment is:

[0008] 1. The low-temperature albite feldspar, 20%-25% calcite, and 15%-20% clay with a weight rat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

A polishing brick with imitated natural stone veins consists of bottom material 60-70 wt% and face material 30-70 wt%, face material comprises cryogenic albite 20-25 wt%, calcite 20-25 wt% and clay 15-20 wt% and cryogenic albite includes sodium above 9 wt%. The surface of ceramic tiles has holes with irregular sizes and shapes, maximum-hole diameter is not more than 5 mm and has good imitated natural stone veins effect.

Description

Technical field: [0001] The invention relates to the technical field of ceramic bricks for architectural decoration, in particular to a polished brick with texture imitating natural travertine. Background technique: [0002] In order to pursue natural style, the existing architectural ceramic materials carry out different processing on the surface during the manufacturing process of ceramic products, such as forming natural decorative effects such as stone grain, flowing water grain, wood grain, etc. through mold pressing or glazing, but these These processing methods all have obvious artificial factors, which make the surface changes of ceramic products monotonous, and the texture texture is not realistic and stiff. Can not reflect the realistic natural style. Invention content: [0003] The object of the present invention is to overcome the disadvantages of the prior art, and provide a polished tile with realistic texture and texture imitating natural travertine, which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/16
Inventor 叶荣崧陈耀强
Owner GUANGDONG JIAJUN CERAMICS