Method for low temperature brazing aluminium alloy to obtain brazed joint with high temperature use performance

A technology for welding joints and aluminum alloys, which is applied in the direction of welding/welding/cutting items, welding media, welding equipment, etc., and can solve problems such as high operating costs, difficulty in welding complex structural parts, and corrosion of workpieces

Active Publication Date: 2007-12-19
哈尔滨工大光电科技有限公司
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims to solve the problem that the existing TIG welding, MIG welding, laser welding, electron beam welding, diffusion welding and instantaneous liquid phase welding methods have large deformation after welding, and it is difficult to realize welding of complex structural parts, and there is residual flux after welding in the brazing method. There are problems of corrosion to the workpiece, high operating cost, long welding cycle, low strength of soldered brazed joints, and poor high-temperature serviceability of welded joints. A method for low-temperature brazing aluminum alloys to obtain high-temperature serviceable welded joints is proposed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0004] Specific Embodiment 1: In this embodiment, the method for brazing aluminum alloys at low temperature to obtain high-temperature serviceable welded joints is realized through the following steps: 1. The brazing filler metal is made into thin slices of 50-500 μm or rods or wires with a diameter of 1000-5000 μm Put it into the weld gap of two parts to be welded or the gap port; 2. Under the conditions of ultrasonic frequency of 20-100kHz, amplitude of 1-50μm, and brazing temperature of 190-450℃, perform ultrasonic brazing on the brazing part Welding for 0.1-60s, complete the preliminary brazing and form a welded joint at the welding place; 3. Adjust the temperature of the welded joint part to 190-550°C and keep it for 1-60 minutes, and then use an ultrasonic frequency of 20-100kHz and an amplitude of Ultrasonic vibration is carried out on the welded joint under the condition of 1-50 μm, that is, the method of realizing low-temperature brazing aluminum alloy to obtain high-t...

specific Embodiment approach 2

[0006] Specific embodiment 2: The difference between this embodiment and specific embodiment 1 is that in step 1, the solder for brazing aluminum alloy at low temperature is a Sn-Zn alloy, Zn-Al with a mass percentage of Zn of 50% to 99.99%. One of alloy or pure zinc. Other steps are the same as in the first embodiment.

specific Embodiment approach 3

[0007] Specific embodiment three: the difference between this embodiment and specific embodiment one is that in step one, the brazing material is made into a thin sheet of 100-400 μm or a rod or wire with a diameter of 2000-4000 μm is put into the welding of two parts to be welded. slot gap or gap port. Other steps are the same as in the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The method for low temperature brazed aluminum alloy to obtain brazed joint with high temperature use performance includes the following steps: 1. setting the brazing alloy inside the brazed gap; 2. primary brazing; and 3. ultrasonic treatment. The said brazing process has no any etching on the aluminum alloy workpiece, short brazing period, low brazing temperature, low operation cost, and capacity of obtaining brazed joint with high strength and high temperature use performance.

Description

technical field [0001] The invention relates to a welding method. Background technique [0002] Aluminum alloy has the advantages of low density, high strength and corrosion resistance, so it is widely used in automobiles, high-speed railway vehicles, and aerospace industries. In particular, the price of copper metal materials is soaring. Many traditional copper alloy structural parts have been replaced by aluminum alloys, which makes the application range of aluminum alloys wider than before. As a result, more and more attention is paid to the welding technology of aluminum alloys. The requirements are also more stringent. For aluminum alloy structural parts, ensuring a small amount of denaturation is the key point, so people expect that the lower the welding temperature, the better, TIG welding, MIG welding, laser welding, electron beam welding, diffusion welding and instantaneous liquid phase welding methods There are problems of large deformation after welding and diff...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K1/06B23K35/14B23K35/24B23K35/28B23K103/10
Inventor 闫久春赵维巍马志鹏许志武杨士勤
Owner 哈尔滨工大光电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka