Silicon dioxide surface treating method by precipitation method and use thereof

A technology of silica and surface treatment, applied in the direction of dyeing organosilicon compound treatment, fibrous filler, etc., can solve the problems of increased viscosity, unfavorable flow of liquid silicone rubber, and inconsistency, and achieve good fluidity, simple use, and easy industrialization Effect

Active Publication Date: 2012-11-28
BLUESTAR SILICONES (SHANGHAI) CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In both cases, the thermal treatment at elevated temperatures, i.e. between 200 and 400 °C, after the hydrophobization step has the disadvantage that such a hydrophobization of the precipitated silica not only places higher demands on the equipment but also From the perspective of preparing liquid silicone rubber products, it is not a simpler, easier to industrialize and economical method
[0005] To prepare a mixture of reactive silicone oil with silica, it is necessary to mix powdered silica into the silicone oil. It is very important to obtain uniform distribution of silica in this process; in addition, another The problem to overcome is the fluidity of the suspension; the introduction of small particles of silicon dioxide into the silicone oil will lead to a significant increase in its viscosity; too high a viscosity will not be conducive to the flow of liquid silicone rubber, mixing molding, extrusion and processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silicon dioxide surface treating method by precipitation method and use thereof
  • Silicon dioxide surface treating method by precipitation method and use thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] (1) Surface treatment method of precipitated silica

[0023] Add 100 parts of 350cp methylpolysiloxane and 8 parts of hexamethyldisilazane to the stirring tank under nitrogen atmosphere, divide 100 parts of precipitated silica into 6 times and decrease the amount each time The method is to add methyl polysiloxane, and the stirring time is controlled to be 30 minutes each time, and the reaction is carried out at a temperature below 130°C for 10 hours, and then vacuumed at 140°C for 12 hours to remove small molecules, and finally add 100 parts of 50000cp hydroxyl silicone oil, After mixing evenly, it is ground by a three-roll mill to obtain a suspension of silicon dioxide and polysiloxane.

[0024] (2) Application of silica

[0025] Add 17 parts of hydroxy silicone oil with a viscosity of 14000 cp and 8.5 parts of methyl silicone oil with a viscosity of 14000 cp to 100 parts of the suspension of silicon dioxide and polysiloxane prepared above. After 69 reactions, the si...

Embodiment 2

[0029] (1) Surface treatment method of precipitated silica

[0030] Add 100 parts of 350cp methylpolysiloxane and 9 parts of hexamethyldisilazane to the stirring tank under nitrogen atmosphere, and divide 100 parts of precipitated silica into 6 times, each time according to the amount of addition The method is to add to the kettle, control the stirring time for 20 minutes each time, react at 120°C for 10 hours, then vacuumize at 150°C for 12 hours to remove small molecules, then add 100 parts of 50000cp hydroxyl silicone oil, mix and pass Three-roll mill grinding to obtain a suspension of silica and polysiloxane.

[0031] (2) Application of silica

[0032] Add 25 parts of hydroxy silicone oil with a viscosity of 3500 cp, 5 parts of methyl silicone oil of 350 cp and 9 parts of quartz powder to 100 parts of the suspension of silicon dioxide and polysiloxane prepared above, and mix well to obtain the mixture Viscosity and after reacting with vulcanizing agent Catalyst 69F, obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for treating the surface of precipitation silicon dioxide and the application of the method. In the circumstance of nitrogen, 70-100 parts of nonreactive polysiloxane (silicon oil) is mixed with compatibilizer which accounts for 8-20% of the weight of the silicon dioxide; 70-100 parts of precipitation silicon dioxide are added in terms of an amount reduced step by step, the time for stirring is 20-60 minutes at each time of precipitation silicon dioxide addition, and then a mixture is obtained and undergoes reaction lasting 3-12 hours at a temperature lower than 130 DEG C; the obtained mixture undergoes vacuuming, wherein, the temperature is 130-160 DEG C and the time is 3-12 hours; and reactive hydroxyl-terminated polysiloxane is added, and then even stirring is carried out; and obtained suspension is ground by a three-roller so as to obtain even suspension of the silicon dioxide and polysiloxane. The invention has the advantages that the silicon dioxide is evenly distributed in the silicon oil, the suspension is good in fluidity, stability is realized in the storage process, and an elastomer has good mechanical property, the use is simple, the method is economical, and easy industrialization can be achieved.

Description

【Technical field】 [0001] The invention relates to the technical field of silicon dioxide, in particular to a method for surface treatment of precipitated silicon dioxide and its application. 【Background technique】 [0002] The molecular chain of raw silicone rubber is very soft, and the interaction between bonds is weak. After crosslinking, its strength is very low, and its tensile strength is only a few kg / cm 2 , must be reinforced with reinforcing materials to have available mechanical strength. Microsilica is a commonly used material, and the addition of silica fillers can greatly improve the mechanical properties of silicone rubber. [0003] There are OH on the surface of silica, which makes it possible to form hydrogen bonds with silicone rubber. On the one hand, this hydrogen bond helps to improve the mechanical properties of silicone rubber; on the other hand, the OH on silica also makes It has poor wettability with silicone rubber, and the viscosity of the rubber i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09C1/28C09C3/12
Inventor 贾丽亚杨一力李培
Owner BLUESTAR SILICONES (SHANGHAI) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap