Compound corrosion and scale inhibitor

A corrosion and scale inhibitor, high-quality technology, applied in the field of high-efficiency composite corrosion and scale inhibitor, to achieve the effect of solving corrosion, wide application, good corrosion and scale inhibition performance

Inactive Publication Date: 2011-05-11
XIAN XIELI POWER TECH
View PDF5 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to overcome the shortcomings of the above scale and corrosion inhibitors, and provide a composite corrosion and scale inhibitor that is less corrosive to water cooling system equipment and less polluting to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compound corrosion and scale inhibitor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Take 100g of raw materials used in the preparation of composite corrosion and scale inhibitor as an example and its mass ratio is as follows:

[0039] Hydroxyethylene diphosphonic acid 25g

[0040] Polyacrylic acid 20g

[0041] Hydrolyzed Polymaleic Anhydride 5g

[0042] Benzotriazole 2g

[0043] Triethylenetetramine hexamethylenesulfonate 18g

[0044] Alcohol 4g

[0045] water 26g

[0046] The molecular weight of above-mentioned polyacrylic acid is 2000~10000, and solid content is 30%, and the molecular weight of hydrolyzed polymaleic anhydride is 400~800, and solid content is 48%, and the active component of hydroxyethylene diphosphonic acid is 60%, , the active ingredient of triethylenetetramine hexamethylenesulfonate is 50%.

[0047] Its preparation method is as follows:

[0048] Stir and mix hydroxyethylene diphosphonic acid, polyacrylic acid, hydrolyzed polymaleic anhydride, triethylenetetramine hexamethylene sulfonate, alcohol, and water, and then add dissol...

Embodiment 2

[0050] Take the raw material 100g used for preparing composite corrosion and scale inhibitor as an example and its preparation method is as follows:

[0051] Hydroxyethylene diphosphonic acid 21g

[0052] Polyacrylic acid 20g

[0053] Hydrolyzed Polymaleic Anhydride 2g

[0054] Benzotriazole 1g

[0055] Triethylenetetramine hexamethylenesulfonate 15g

[0056] Alcohol 6g

[0057] water 35g

[0058] The molecular weight of above-mentioned polyacrylic acid is 2000~10000, and solid content is 30%, and the molecular weight of hydrolyzed polymaleic anhydride is 400~800, and solid content is 48%, and the active component of hydroxyethylene diphosphonic acid is 60%, , the active ingredient of triethylenetetramine hexamethylenesulfonate is 50%.

[0059] Its preparation method is identical with embodiment 1.

Embodiment 3

[0061] Take the raw material 100g used for preparing composite corrosion and scale inhibitor as an example and its preparation method is as follows:

[0062] Hydroxyethylene diphosphonic acid 30g

[0063] Polyacrylic acid 10g

[0064] Hydrolyzed Polymaleic Anhydride 10g

[0065] Benzotriazole 3g

[0066] Triethylenetetramine hexamethylenesulfonate 15g

[0067] Alcohol 4g

[0068] water 28g

[0069] The molecular weight of above-mentioned polyacrylic acid is 2000~10000, and solid content is 30%, and the molecular weight of hydrolyzed polymaleic anhydride is 400~800, and solid content is 48%, and the active component of hydroxyethylene diphosphonic acid is 60%, , the active ingredient of triethylenetetramine hexamethylenesulfonate is 50%.

[0070] Its preparation method is identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
solid contentaaaaaaaaaa
Login to View More

Abstract

The invention relates to a compound corrosion and scale inhibitor which comprises the following raw materials according to mass ratio: 15%-30% of organic phosphonic acid, 10%-20% of acrylic acid or acrylic acid copolymer, 2%-10% of poly-maleic acid, 1%-3% of azole ramifications, 15%-30% of multivariate organic sulfonate, 2%-6% of dimethyl formamide and 20%-35% of water. The compound corrosion andscale inhibitor of the invention is used for a system which employs normal water as circulating cooling water, so as to solve corrosion problem caused by circulating water of normal-water to equipment. Corrosion rate of copper product is lower than the national standard of 0.005mm / a, thereby generating no equipment scaling caused by calcium phosphate deposition. Compared with corrosion inhibitorsof the same kind, the compound corrosion and scale inhibitor has a lower dosage and is effective in corrosion and scale inhibiting. The compound corrosion and scale inhibitor is simple in operation, convenient, quick, safe and efficient.

Description

technical field [0001] The invention relates to a high-efficiency composite corrosion and scale inhibitor for circulating cooling water. Especially reclaimed water is used as circulating cooling water, corrosion and scale inhibitors used in circulating cooling water systems with large chlorine radicals and high pH. Background technique [0002] my country is a country seriously short of water resources and one of the 13 water-poor countries in the world. Among them, the per capita water resources of 18 provinces, municipalities, and autonomous regions are lower than the 2000m per capita water resources reviewed by the United Nations Sustainable Development Commission. 3 , less than 1000m in 10 provinces, municipalities and autonomous regions 3 It is predicted that the total water supply capacity in China in 2010 will be (6.2~6.5)×1011m 3 The total water demand is 7.3×1011m 3 , the gap between supply and demand is nearly 1×1011m 3 . The serious shortage of water supply w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C02F5/14
Inventor 张全根马宏良贺科峰田美宁
Owner XIAN XIELI POWER TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com