Drinking water purification treatment material containing nano-germanium and preparation method thereof

A technology for purification and drinking water, applied in the direction of adsorption water/sewage treatment, light water/sewage treatment, additive water/sewage treatment, etc. Problems such as one or more times of pollution, to achieve the effect of activating human immune cells, improving filtering effect, and large market potential

Inactive Publication Date: 2010-02-10
张金松
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, the problems of the above-mentioned technology are: single function; or troublesome to use; or basically only have the function of changing the PH acid-base of water, and cannot be used with tea; in addition, sometimes the problem of secondary or multiple pollution will occur
However, there is no drinking water purification treatment material containing nano-germanium in the past.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040]With 0.5-0.8% (weight) of nano-germanium of 50-150nm, 5-10% (weight) of tourmaline nano-powder of 180-200nm, 5% (weight) of nano-silver antibacterial material, thermal melting point is at 80-100 ℃, Viscosity 6000-7500 centipoise, particle size 80-120 purpose hot-melt powder polyamide (PA) 8-10% (weight), and surplus 40-60 purpose activated carbon are added in the mixing tank of screw pump, while stirring, while mixing 4 After -6 minutes, extrude into one end of the filter core-shaped forming mold, and after forming, add a high temperature of 80-100 ° C for 30 seconds to 1 minute to obtain the drinking water purification treatment material containing nano-germanium of the present invention. The porosity of the formed drinking water purification treatment material containing nano germanium is 300-350nm.

Embodiment 2

[0042] In addition to 0.8-1.2% (weight) of nano-germanium of 150-200nm, 10-15% (weight) of tourmaline nano-powder of 200-300nm, 3% (weight) of nano-silver antibacterial material, thermal melting is at 80-100 ℃ , viscosity 5000-5500 centipoise, particle size 100-120 purpose hot-melt powder polyester amide (PEA) 10-15% (weight), and 70% (weight) 60-80 purpose activated carbon is added in the mixing tank of screw pump , the rest of the embodiments are the same as in Example 1, and the drinking water purification treatment material containing nano-germanium of the present invention is obtained. The porosity of the shaped drinking water purification treatment material containing nano-germanium is 300-400nm.

Embodiment 3

[0044] Except that 1.2-2% (weight) of nano-germanium of 250-300nm, 15-20% (weight) of tourmaline nano-powder of 300-400nm, 2.5% (weight) of nano-silver antibacterial material, thermal melting point is at 100-120 ℃ , viscosity 3000-3500 centipoise, particle size 100-120 purpose hot-melt powder polyethylene (CDPE) 15-20% (weight), and 60% (weight) 40-60 purpose active carbon is added in the mixing tank of screw pump, The other embodiments are the same as in Example 1, and the drinking water purification treatment material containing nano-germanium of the present invention is obtained. The porosity of the formed drinking water purification treatment material containing nano germanium is 400-500nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a drinking water purification treatment material containing nano-germanium, which contains active carbon and tourmaline nano-powder and comprises the following components in percentage by weight: 0.2 to 3 percent of nanometer germanium, 5 to 20 percent of tourmaline nano-powder, 3 to 5 percent of nano-silver antimicrobial material, 5 to 20 percent of hot-melt powder and the balance of active carbon. According to the drinking water purification treatment material, drinking water contains trace element germanium and has high activity, and can effectively absorb and filter iron rust, suspended substances, silt, peculiar smell, algae, flocculation chemicals, harmful conglutination substances and heavy metal in tap water; when antibiosis and disinfection are carried out, water processed by germanium filtering simultaneously has the function of regulating the abnormal electric potential and magnetic field of a human body, can capture the electronic magnetic field ofcancer cells so as to reduce the electric potential of the cancer cells and inhibit the deterioration of the state of illness of cancer, and is suitable for crowds lacking the germanium, middle and old aged groups and cancer and tumour patients of wide areas lacking the germanium.

Description

technical field [0001] The invention relates to a drinking water purification treatment technology, in particular, the invention relates to a drinking water purification treatment material containing nano-germanium (Ge) and a preparation method thereof. Background technique [0002] With the continuous progress and development of social economy and the improvement of people's increasing material life and health needs, people's requirements for drinking water safety standards are also getting higher and higher. [0003] For example, based on photocatalytic drinking water purification technology. After the tap water is chlorinated and sterilized, a large amount of carcinogenic organic chlorides are generated, which makes the water quality and taste of the tap water very poor. There is no purification treatment of organic matter in domestic tap water. Photocatalytic technology can sterilize and purify organic poisons; it can sterilize drinking water and purify organic polluta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/68C02F1/28C02F1/50C02F1/30
Inventor 张金松
Owner 张金松
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap