Sandwich layer slow-release birth control material

A sandwich layer, slow-release technology, applied in the field of medical materials, can solve the problems of breakage and falling off of IUDs, fast corrosion rate, uncontrollable release rate of copper ions, etc., and achieve the effect of controllable release rate

Inactive Publication Date: 2013-03-20
HUAZHONG UNIV OF SCI & TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The release of copper ions from metal copper IUDs mainly has the following three problems: First, the initial violent release of copper ions is serious
Third, the release rate of copper ions in the metal copper IUD is uncontrollable, and the part that is in sufficient contact with oxygen and water will corrode quickly, which will easily cause the IUD to break and fall off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sandwich layer slow-release birth control material
  • Sandwich layer slow-release birth control material
  • Sandwich layer slow-release birth control material

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0031] Upper surface layer: Weigh 5g of polyvinyl alcohol (referred to as PVA, the same below), add 2.14g of SiO 2 , add distilled water to 100g, stir at 90°C for 1 hour to obtain uniform PVA / SiO 2 The solution was cast into a film on a smooth 20cm×30cm glass plate.

[0032] Middle layer: Weigh 5g of PVA, add 2.14g of SiO 2 , add distilled water to 100g, stir at 90°C for 1 hour to obtain uniform PVA / SiO 2 The solution was cooled to 40° C., 4.76 g of copper chloride was added, and stirred for 0.5 hour to obtain a uniform film solution. A film was cast on the above dried film.

[0033] Lower surface layer: Prepare the same PVA / SiO as the method for preparing the upper surface layer 2 solution. A film was cast on the above dried film.

[0034] Take it off after drying, immerse in simulated human body fluid, and measure the release of copper ions. Such as figure 1 Curve a in, i.e. 30% SiO 2 / PVA, 30% SiO 2 / 40%CuCl 2 / PVA, 30% SiO 2 / PVA.

example 2

[0036] Upper surface layer: Weigh 5g of PVA, add 2.14g of SiO 2 , add distilled water to 100g, stir at 90°C for 1 hour to obtain uniform PVA / SiO 2 The solution was cast into a film on a smooth 20cm×30cm glass plate.

[0037] Middle layer: Weigh 5g of PVA, add 3.33g of SiO 2 , add distilled water to 100g, stir at 90°C for 1 hour to obtain uniform PVA / SiO 2 The solution was cooled to 40° C., 5.55 g of copper chloride was added, and stirred for 0.5 hour to obtain a uniform film solution. A film was cast on the above dried film.

[0038] Lower surface layer: Prepare the same PVA / SiO as the method for preparing the upper surface layer 2 solution. A film was cast on the above dried film.

[0039] Take it off after drying, immerse in simulated human body fluid, and measure the release of copper ions. Such as figure 1 Curve b in ie 30% SiO 2 / PVA, 40% SiO 2 / 40%CuCl 2 / PVA, 30% SiO 2 / PVA. figure 1 The surface composition of curve a and curve b is the same, and the conten...

example 3

[0041] Upper surface layer: Weigh 5g of PVA, add 3.33g of SiO 2 , add distilled water to 100g, stir at 90°C for 1 hour to obtain uniform PVA / SiO 2 The solution was cast into a film on a smooth 20cm×30cm glass plate.

[0042] Middle layer: Weigh 5g of PVA, add 2.14g of SiO 2 , add distilled water to 100g, stir at 90°C for 1 hour to obtain uniform PVA / SiO 2 The solution was cooled to 40° C., 4.76 g of copper chloride was added, and stirred for 0.5 hour to obtain a uniform film solution. A film was cast on the above dried film.

[0043] Lower surface layer: Prepare the same PVA / SiO as the method for preparing the upper surface layer 2 solution. A film was cast on the above dried film.

[0044] Take it off after drying, immerse in simulated human body fluid, and measure the release of copper ions. Such as figure 1 Curve c in the 40% SiO 2 / PVA, 30% SiO 2 / 40%CuCl 2 / PVA, 40% SiO 2 / PVA. figure 1 The composition of the middle layer of curves a and c is the same, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a sandwich layer slow-release birth control material, which is formed by superposing hybrid material layers and complexing polymer-matrix composite material layers in a staggered mode, and the bottom layer and the top layer are the hybrid material layers consisting of polyving akohol and 10 to 40 weight percent of SiO2; the complexing polymer-matrix composite material layers consist of the polyving akohol, 10 and 40 weight percent of SiO2 and 10 and 40 weight percent of copper salt. The sandwich layer slow-release birth control material can release copper ions slowly, reduces the phenomenon of the burst release of the copper ions caused by the conventional metal copper birth-control device and the nanometer copper / low-density polyethylene birth-control device, and eliminate side effects such as massive hemorrhage, underbelly pain, pelvic inflammatory disease and the like caused by the burst release of the copper ions during initial implantation. The release process comprises that the copper ions dissociated in an intermediate layer of a composite material are diffused towards a surface layer under the action of concentration gradient; the copper ions diffused to the surface layer are diffused to an interface where the material is contacted with body fluid of a human body; and finally, the copper ions are diffused to the body fluid of the human body through the interface. The sandwich layer slow-release birth control material prolongs a path for diffusing medicaments, increases the resistance of medicament release, and slows down the release speed of the copper ions.

Description

technical field [0001] The invention belongs to the technical field of medical materials, in particular to a controllable slow-release birth control material. technical background [0002] The population issue is related to national livelihood and is a major issue affecting economic and social development. Over the past 30 years, my country's economic and social development has achieved world-renowned achievements, people's living standards have improved significantly, and the structure and quality of the population have undergone profound changes. Family planning work has made important contributions to scientific development. Improving the reproductive health of the people has become an important part of improving the quality and level of population and family planning work under the new historical conditions. Among them, the intrauterine device (IUD) is a safe, effective, economical and convenient contraceptive tool, and it is also one of the most widely used birth cont...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61L31/12A61L31/16
Inventor 李娟索进平
Owner HUAZHONG UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap