Bright alkyd resin for interior decoration and furniture coating and preparation method thereof

An alkyd resin and interior decoration technology, used in coatings, polyurea/polyurethane coatings, etc., can solve the problems of large solvent usage, poor gloss and color retention, and easy yellowing of the paint film, and achieve the fullness of the paint film. Good, good weather resistance, not easy to return to yellow effect

Inactive Publication Date: 2011-12-07
四川巴德士新材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the specific construction conditions and environmental requirements, the prepared interior decoration and furniture coating needs to be diluted with a large amount of solvent if the viscosity is too high, the gloss is low, the adhesion is not good, the paint film is easy to yellow, low hardness, and is not resistant Grinding, poor gloss and color retention, and a large amount of solvent are used, resulting in the above reasons. The performance of alkyd resin plays a key role. Therefore, the preparation of high-solid, low-viscosity and high-performance alkyd resin is the key technology to solve many defects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bright alkyd resin for interior decoration and furniture coating and preparation method thereof
  • Bright alkyd resin for interior decoration and furniture coating and preparation method thereof
  • Bright alkyd resin for interior decoration and furniture coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] This example is used for interior decoration and furniture coating bright alkyd resin, which includes the following raw materials:

[0035] 1. Glycerin 16g

[0036] 2. Palmitoleic acid 15g

[0037] 3. Benzoic acid 0.5g

[0038] 4. Adipic acid 0.5g

[0039] 5. Neopentyl glycol 7.4g

[0040] 6. Phthalic anhydride 45.6g

[0041] 7. Pentaerythritol 3g

[0042] 8. Xylene 12g

[0043] Put the raw materials in the above 1-7 and 0.42g of xylene into the reactor at one time, and start stirring when it is heated to 50°C; pass carbon dioxide gas in the reactor to protect the temperature, and raise the temperature to 130°C at a heating rate of 8°C / hour, and keep warm for 1 At this time, there is xylene reflux, continue to rise to 200±5°C at a rate of 8°C / hour, and keep warm for 4 hours; take samples from the reaction kettle and use a 25°C Grignard tube to measure the viscosity. When the viscosity is 160s / 25°C , rapidly cooled to 130° C. to obtain a modified alkyd resin; tran...

Embodiment 2

[0045] This example is used for interior decoration and furniture coating bright alkyd resin, which includes the following raw materials:

[0046] 1. Glycerin 28g

[0047] 2. Palmitoleic acid 17.4g

[0048] 3. Benzoic acid 3.6g

[0049] 4. Adipic acid 3.2g

[0050] 5. Neopentyl glycol 10g

[0051] 6. Phthalic anhydride 25g

[0052] 7. Pentaerythritol 6.8g

[0053] 8. Xylene 6g

[0054] Put the raw materials in the above 1-7 and 0.21g of xylene into the reactor at one time, and start stirring when it is heated to 100°C; pass carbon dioxide gas in the reactor to protect the temperature, and raise the temperature to 180°C at a heating rate of 12°C / hour, and keep warm for 3 At this time, there is xylene reflux, continue to rise to 200±5°C at a rate of 12°C / hour, and keep warm for 8 hours; take samples in the reaction kettle and use a 25°C Grignard tube to measure the viscosity. When the viscosity is 160s / 25°C , rapidly cooled to 180° C. to obtain a modified alkyd resin; tra...

Embodiment 3

[0056] This example is used for interior decoration and furniture coating bright alkyd resin, which includes the following raw materials:

[0057] 1. Glycerin 17g

[0058] 2. Palmitoleic acid 25.8g

[0059] 3. Benzoic acid 0.6g

[0060] 4. Adipic acid 0.8g

[0061] 5. Neopentyl glycol 6g

[0062] 6. Phthalic anhydride 39.3g

[0063] 7. Pentaerythritol 3.5g

[0064] 8. Xylene 7g

[0065] Put the raw materials in the above 1-7 and 0.245g of xylene into the reactor at one time, and start stirring when it is heated to 80°C; pass carbon dioxide gas in the reactor to protect the temperature, and raise the temperature to 150°C at a heating rate of 9°C / hour, and keep warm for 2 At this time, there is xylene reflux, continue to rise to 200±5°C at a rate of 9°C / hour, and keep warm for 5 hours; take samples from the reaction kettle and use a 25°C Grignard tube to measure the viscosity. When the viscosity is 160s / 25°C , rapidly cooled to 150° C. to obtain a modified alkyd resin; tr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bright alkyd resin for interior decoration and furniture coating, which is composed of the following raw materials: glycerin, palmitoleic acid, benzoic acid, adipic acid, neopentyl glycol, phthalic anhydride, pentaerythritol and xylene . Its preparation method comprises the steps of: a. putting palmitoleic acid, benzoic acid, adipic acid, glycerin, neopentyl glycol, phthalic anhydride, pentaerythritol and xylene into a reactor at one time, heating and starting stirring; b. Zhongtong carbon dioxide gas protects the temperature, raises the temperature to 130°C-180°C, and keeps it warm for 1-3 hours. ; c, take a sample to measure the viscosity in step b, when the viscosity reaches a predetermined value, rapidly cool to 130°C-180°C to obtain a modified alkyd resin; d, transfer the modified alkyd resin in step c to another Add 2.5-8.5% xylene into the kettle, and mix evenly to obtain the product water-white alkyd resin liquid of the present invention.

Description

technical field [0001] The invention relates to a bright alkyd resin used for interior decoration and furniture coating, and also relates to a method for preparing the bright alkyd resin. Background technique [0002] Polyurethane paint is a kind of coating with excellent performance. Widely used in furniture decoration, painting, architectural decoration, equipment anti-corrosion, etc. Polyurethane paint is usually formulated from the adduct or trimer of polyester or alkyd resin and toluene diisocyanate, plus additives. Due to the specific construction conditions and environmental requirements, the prepared interior decoration and furniture coating needs to be diluted with a large amount of solvent if the viscosity is too high, the gloss is low, the adhesion is not good, the paint film is easy to yellow, low hardness, and is not resistant Grinding, poor gloss and color retention, and a large amount of solvent are used, resulting in the above reasons. The performance of alk...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G63/49C08G63/78C09D175/14
Inventor 方学平方道钧
Owner 四川巴德士新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com