Oil and water-resistant and permeable fluorosilane protective cream and preparation method thereof

A fluorine-containing silane, oil-repellent and water-repellent technology, which is applied in the field of oil-repellent, water-repellent and air-permeable fluorine-containing silane protective cream and its preparation, can solve the problems of insufficient penetration capacity and construction performance of the concrete structure surface, high product viscosity and long reaction time etc. to achieve excellent oil-repellent and water-repellent effects, high chemical resistance stability, protective effect and long service life

Active Publication Date: 2010-06-16
ZHANGJIAGANG GUOTAI HUARONG NEW CHEM MATERIALS CO LTD
View PDF3 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This preparation method is complicated in process and long in reaction time. The polymer material obtained through the polymerization reaction has a high viscosity, and there are obvious deficiencies in the penetration ability and construction performance of the concrete structure surface.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] At a room temperature of 25°C, first add 2 grams of sodium lauryl sulfate emulsifier to 90 grams of deionized water, and stir at a speed of 1500 rpm to obtain an aqueous phase; then couple 40 grams of trifluoropropyltrimethoxysilane to agent, 80 grams of isobutyl triethoxysilane coupling agent, 50 grams of dodecyl trimethoxysilane, 5 grams of MOA-9, 3 grams of Pingpingjia O-5, 15 grams of methyl hydrogen silicone oil oligomerization Mixture, 10 grams of xylene and 5 grams of petroleum ether, and stir at 1500rpm to obtain an oil phase; finally, at 1500rpm, drop the above-mentioned oil phase into the water phase while stirring. Continue to stir until the material in the reactor turns into a viscous paste, and then the product of the present invention can be obtained.

Embodiment 2

[0032] At room temperature at 5°C, first add 4 grams of sodium dodecylbenzenesulfonate emulsifier to 80 grams of deionized water, and stir at a speed of 1500 rpm to obtain an aqueous phase; then add 50 grams of trifluoropropyltriethoxysilane Coupling agent, 60 grams of n-octyltriethoxysilane coupling agent, 55 grams of hexadecyltrimethoxysilane, 4 grams of SPAN-80 emulsifier, 2 grams of Pingpingjia O-3 emulsifier, 25 grams of formazan Hydrogen-containing silicone oil, 15 grams of petroleum ether and 5 grams of xylene were mixed, and stirred at a speed of 1800 rpm to obtain an oil phase; finally, at a speed of 1800 rpm, the above oil phase was dropped into the water phase while stirring, and after the oil phase was added dropwise Continue stirring at 2500rpm until the material in the reactor becomes a viscous paste, the product of the present invention can be obtained.

Embodiment 3

[0034]At room temperature at 22°C, first add 3 grams of sodium lauryl sulfate emulsifier into 50 grams of deionized water, stir at 1500 rpm to obtain a water phase; then couple 80 grams of isooctyltriethoxysilane agent, 20 grams of trifluoropropyltriethoxysilane coupling agent, 30 grams of trifluoropropylmethyldiethoxysilane coupling agent, 10 grams of SPAN-60, 7 grams of MOA-15 ​​emulsifier, 15 grams Polymethyltriethoxysiloxane oligomer, 30 grams of methyl-terminated polydimethylsiloxane oligomer, 15 grams of n-octane and 40 grams of petroleum ether are mixed, and stirred evenly at 1500 rpm to obtain Oil phase; finally, at a rotating speed of 1500rpm, drop the above oil phase into the water phase while stirring, and continue stirring at 2500rpm after the oil phase is added until the material in the reactor becomes a viscous paste, which can be obtained Product of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses oil and water-resistant and permeable fluorosilane protective cream and a preparation method thereof. The fluorosilane protective cream is prepared from raw materials of a fluorosilane coupling agent, a long-chain alkyl silane coupling agent with a carbon chain length of between 4 and 16, a siloxane oligomer with a viscosity of between 10 and 2,000 mm2 / S, an organic solvent, an emulsifier and deionized water under the conditions that the temperature is between 1 and 40 DEG C, and the stirring speed is between 1,500 and 2,000 rpm. The method for preparing the oil and water-resistant and permeable fluorosilane protective cream comprises the following steps: firstly, stirring the deionized water and 2 to 80 percent of emulsifier uniformly to obtain an aqueous phase; then, stirring the fluorosilane coupling agent, the long-chain alkyl silane coupling agent, residual emulsifier, the siloxane oligomer, and the organic solvent uniformly to obtain an oil phase; finally, dripping the oil phase into the aqueous phase with stirring, and continuously stirring at a speed of 2,500 rpm after finishing dripping the oil phase until the materials in the reactor are changed into viscous paste. The oil and water-resistant and permeable fluorosilane protective cream has the advantages of advanced technology, and capacity of obviously improving the durability and the service life of a concrete structure, and is suitable for protecting various concrete infrastructures.

Description

technical field [0001] The invention belongs to special protective coating materials, and in particular relates to an oil-repellent, water-repellent and air-permeable fluorine-containing silane protective paste and a preparation method thereof. Background technique [0002] The global construction industry consumes 40% of the world's total resources, and the value of infrastructure in the United States accounts for 70% of its total social wealth. my country's infrastructure construction accounts for a larger proportion of the national economy. Judging from the current development trend, this trend is still Will keep for a long time. A large number of damage examples at home and abroad show that the concrete structure is not destroyed due to insufficient design strength, but prematurely destroyed due to insufficient concrete durability, which has caused an astonishing amount of maintenance and reconstruction funds and waste of resources. At present, the whole society is advoc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/49
CPCC04B41/4961C04B2111/27C04B26/32C04B41/009C04B2103/40
Inventor 戴建才李建中施苏萍王一明岳立方剑慧
Owner ZHANGJIAGANG GUOTAI HUARONG NEW CHEM MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com