Method for synthesizing titanium silicon zeolite material

A technology of titanium silicalite and zeolite, which is applied in the field of synthetic titanium silicalite materials, can solve the problems of poor activity stability, easy deactivation, low activity of titanium silicalite, etc., and achieve increased selectivity of reaction products, reduced preparation costs, and good The effect of catalytic activity stability

Active Publication Date: 2012-05-30
CHINA PETROLEUM & CHEM CORP +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the titanium silicalite obtained by the current synthesis method has problems such as low activity, poor activity stability and easy deactivation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for synthesizing titanium silicon zeolite material
  • Method for synthesizing titanium silicon zeolite material
  • Method for synthesizing titanium silicon zeolite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032]Add 20 grams of all silicalite S-1 into tetrapropyl ammonium hydroxide aqueous solution and stir to mix evenly, then add tetrabutyl titanate and mix well to obtain a mixture consisting of: all silicalite (gram): titanium source (mol ): alkali source (mol): water (gram)=100: 0.2: 0.2: 600. Then put it into a sealed stainless steel reaction kettle, hydrothermally treat it at 150°C and autogenous pressure for 48 hours, filter the resultant, wash with water, dry it naturally, and roast it at 550°C for 5 hours to obtain titanium silicalite material A. Its XRD crystal phase diagram is as follows figure 1 Shown in (B), similar to comparative example; Fourier transform infrared spectrogram is as figure 2 As shown in (b), it is also similar to the comparative example, at 960cm -1 The infrared absorption peak that all-silicon molecular sieves do not have appears nearby, indicating that titanium has entered the molecular sieve framework, and the 960cm -1 Absorption peak at and ...

Embodiment 2

[0034] Add 20 grams of all-silica zeolite S-1 into an aqueous solution of sodium hydroxide and stir to mix evenly, then add tetrapropyl titanate and mix well to obtain a mixture consisting of: all-silica zeolite (g): titanium source (mol): base Source (mole):water (gram)=100:5.0:1.2:3500. Then put it into a sealed stainless steel reaction kettle, hydrothermally treat it at 180°C and autogenous pressure for 24 hours, filter the resultant, wash with water, dry it naturally, and roast it at 550°C for 5 hours to obtain titanium silicalite material B. Its XRD crystal phase diagram is as follows figure 1 Shown in (C), similar to comparative example; Fourier transform infrared spectrogram is as figure 2 Shown in (c), also similar to the comparative example, in the infrared spectrum at 960cm -1 The infrared absorption peak that all-silicon molecular sieves do not have appears nearby, indicating that titanium has entered the molecular sieve frame, 960cm -1 Absorption peak at and 55...

Embodiment 3

[0036] Add 20 grams of all silicalite S-1 into tetrapropyl ammonium hydroxide aqueous solution and stir to mix evenly, then add tetraethyl titanate and mix to obtain a mixture consisting of: all silicalite (gram): titanium source (mol ): alkali source (mol): water (gram)=100: 2.0: 1.0: 1200. Then put it into a sealed stainless steel reaction kettle, hydrothermally treat it at a temperature of 150°C and autogenous pressure for 48 hours, filter the resultant, wash with water, dry it naturally, and roast it at 550°C for 5 hours to obtain titanium silicalite material C. In its ultraviolet-visible spectrum, there is a strong absorption band near the wavelength of 210nm, but there is no absorption near 340nm, indicating that all titanium enters the skeleton, and no non-skeleton titanium is produced. Its infrared spectrum is 960cm -1 Absorption peak at and 550cm -1 Absorption peak intensity ratio I 960 / I 550 The data are listed in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for synthesizing a titanium silicon zeolite material, which comprises the following steps of: adding all silicone zeolite and / or boron silicon zeolite in an alkaline aqueous solution, mixing uniformly, adding a titanium source, mixing uniformly, treating under hydro-thermal treatment conditions, and recovering the products to obtain the titanium silicon zeolite material. The method has the characteristics of low cost and good repeatability. Compared with the prior art, the obtained zeolite material has high oxidative activity in an oxidizing reaction and goodselectivity of the target product.

Description

technical field [0001] The invention relates to a method for synthesizing titanium silicalite material. Background technique [0002] Titanium silicalite is a new type of heteroatom zeolite developed in the early 1980s. At present, TS-1 with MFI structure, TS-2 with MEL structure, MCM-22 with MWW structure and TS-48 with larger pore structure have been synthesized. Among them, the titanium silicalite TS-1 developed and synthesized by Italy Enichem Company is a new type of titanium silicalite with excellent catalytic selective oxidation performance formed by introducing transition metal element titanium into the zeolite framework with ZSM-5 structure. TS-1 not only has the catalytic oxidation effect of titanium, but also has the shape-selective effect and excellent stability of ZSM-5 zeolite. Using titanium silicalite as a catalyst can catalyze various types of organic oxidation reactions, such as epoxidation of alkenes, partial oxidation of alkanes, oxidation of alcohols, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01B39/08
Inventor 史春风朱斌林民汝迎春
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap