Yarn for preparing fabric with bundling structure and preparation method thereof

A yarn and sliver technology, which is applied in the field of yarn and its preparation, can solve problems such as limited performance, easy exposure, and many fiber ends, and achieve the effects of reducing pilling, saving costs, and reducing hairiness

Active Publication Date: 2011-01-26
JIANGSU JIANLU WOOLEN +5
View PDF5 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because fibers with shorter length and thicker fineness usually have lower yarn strength, the strength of the product is too low after untwisted or low-twisted production, and the performance of the product is limited; and because the fibers are thick and short, there are many fiber ends and It is easy to be exposed, and the simple untwisted or low-twisted yarn structure will cause shortcomings such as puncture and fluffing, so there has been no report of processing this kind of fiber into untwisted or low-twisted fabrics so far

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Yarn for preparing fabric with bundling structure and preparation method thereof
  • Yarn for preparing fabric with bundling structure and preparation method thereof
  • Yarn for preparing fabric with bundling structure and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] figure 2 It is a schematic diagram of the preparation method of the yarn of the present invention. As shown in the figure, at first, the primary twist twist a is applied to the sliver A, and the twist direction can be Z direction or S direction; and the water-soluble vinylon B1 is combined with a fine-denier chemical fiber filament B2 to form a sliver B, and the The sliver B can be untwisted, or the initial twist twist b is applied, and the twist direction is the same as that of the sliver A; then the sliver A and the sliver B are combined and reverse twisted, and the double twist twist applied by the reverse twist is c, thus obtaining the yarn C of the present invention.

[0034] image 3 The structure of the yarn in the fabric after the weaving process is shown. As shown in the figure, after the water-soluble vinylon B1 is dissolved by the fiber removal process, the fine-denier chemical fiber filament B2 is wound on the sliver A to form a bundled structure, and th...

Embodiment 1

[0037] Example 1: Preparation of untwisted crepe fabric from ramie / cotton blended yarn

[0038] Sliver A is ramie / cotton 50 / 5032s yarn with 600 twists / m and the twist direction is Z direction; A side-by-side body of polyester FDY (B2), untwisted (b=0). The sliver A and the sliver B are combined by a doubling machine and wound on the endless metal bobbin, and then 600 twists / m are applied by a two-for-one twister, and the twist direction is S twist. The yarn C thus obtained adopts the general warping, weft winding, and air-jet loom weaving process. After the gray cloth is obtained, it is washed at 90°C for 30 minutes in an overflow dyeing machine with a bath ratio of 1:25. Then clean it, and then enter the conventional dyeing and finishing process, and give sufficient overfeeding and weft shrinkage in the shaping process, and finally make a fabric with special wrinkles in appearance, good elasticity in warp and weft, and soft hand feeling, which is especially suitable for It ...

Embodiment 2

[0039] Embodiment 2: prepare low-twisted woolen fabric by wool / polyester blended yarn

[0040] In order to use thicker wool to achieve a better hand feel and provide good elasticity, 64 wool tops are used to spin wool / polyester 70 / 3034Nm yarns with a twist of 550 twists / m, Z direction (sliver A), and 85°C water-soluble 14.6tex water-soluble vinylon yarn and a 50dtex / 24fPTT filament, twist 400 twist / m, Z direction (sliver B). Sliver A and sliver B are combined by a doubling machine, and then 400 twists are added by a two-for-one twister, S-direction (thereby making sliver C), and the warping, weft winding and arrow shaft are carried out after 24 hours of fixed twisting After weaving on a loom, after the gray fabric is made, it is firstly de-dimensionalized in an overflow dyeing machine at a bath ratio of 1:30 at 90°C×25min, and then conventional wet and dry finishing is performed. In the setting process, a large warp and weft tension is applied so that no wrinkles appear on th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a yarn for preparing a fabric with a bundling structure and a preparation method thereof. The yarn is prepared by the doubling and back twisting of a sliver A and a sliver B, wherein a first twist of the sliver A is a, the sliver B does not have a twist or has a first twist b, and a second twist of the back twisting is c. The yarn is characterized in that: the sliver B is a conjunct of water soluble vinylon and a fine denier chemical fiber long yarn. The preparation method of the yarn comprises the following steps of: applying the first twist a to the sliver A; combining the water soluble vinylon with the fine denier chemical fiber long yarn to form the sliver B, and not twisting the sliver B or applying the first twist b to the sliver B, wherein the twisting direction is the same as that of the sliver A; and doubling the sliver A and the sliver B on a doubling and twisting machine and then performing back twisting on a two-for-one twisting machine to obtain the yarn, wherein the second twist c is applied during the back twisting. When the yarn of the invention is used to prepare the fabric, the water soluble vinylon is dissolved by a vinylon dissolving process, the sliver A does not have a twist or has a low twist, and the fine denier chemical fiber long yarn is wound on the sliver A to form the bundling structure.

Description

technical field [0001] The present invention relates to a yarn and its preparation method. In particular, untwisted or low-twisted fabrics with bundled structures can be produced using the yarns of the invention. Background technique [0002] In recent years, with the continuous improvement of people's requirements for fabric comfort and the continuous development of textile technology, the development of untwisted or low-twisted fabrics has attracted more and more attention from fabric designers. [0003] Compared with ordinary fabrics, untwisted or low-twisted fabrics have the advantages of fluffy, soft, good air permeability and strong comfort. At present, the yarns for preparing untwisted or low-twisted fabrics are mainly made of single yarns spun from cotton fibers and single yarns spun from water-soluble vinylon fibers, which are reversely twisted after plying. In order to make the final untwisted or low-twisted fabric fluffy and soft, the raw material grade of the y...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04D02G3/26
Inventor 施楣梧王竹林高惠芳崔志山刘庆年肖群锋赵寿岭唐守荣姜爱娟耿灏张萍陈作芳
Owner JIANGSU JIANLU WOOLEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com