Micromachining method of textures on metal surface

A metal surface and micro-machining technology, which is applied in the fields of craft and decorative art for producing decorative surface effects, can solve problems such as complex lines or patterns, and achieve the effect of good lines and textures

Active Publication Date: 2013-04-10
BYD CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is currently no way to obtain complex textures or patterns on metal surfaces by CNC micromachining

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Micromachining method of textures on metal surface
  • Micromachining method of textures on metal surface
  • Micromachining method of textures on metal surface

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] (1) Metal substrate

[0035] The aluminum plate (model 5052) is punched into the shape of the mobile phone shell (84mm×54mm×0.5mm) by stamping technology.

[0036] (2) Production of jigs

[0037] According to the shape of the stamped mobile phone case, a jig is made, and the material is aluminum alloy, which is used to clamp the stamped mobile phone case.

[0038] (3) Spindle path design and programming

[0039] Use CAD software to draw a V-shaped path with an included angle of 30°. According to the drawn CAD path, use G code to program and import it into numerical control equipment.

[0040] (4) Texture processing

[0041] Put the stamped mobile phone case on the jig prepared in step (2) to fix it, spray a small amount of WD-40 universal anti-rust lubricant on the aluminum material, press the start button, and the programmed processing can be performed program. The machining depth is 0.05mm, the spacing is 0.2mm, the spindle speed is 2000r / min, the feed speed of X...

Embodiment 2

[0043] (1) Metal substrate

[0044] Use wire cutting technology to cut the aluminum alloy (model 5052) into a ring-shaped mobile phone photo frame (the inner frame is a square with a side length of 7.85mm, and the chamfering radius of the four vertices of the square is R1.64mm; the outer frame is a square with a side length of 12.75mm. The chamfering radius of the four vertices of this square is R3.0mm.

[0045] (2) Production of jigs

[0046] According to the shape of the cut ring-shaped mobile phone photo frame, a jig is made, and the material is aluminum alloy, which is used to clamp the cut ring-shaped mobile phone photo frame.

[0047] (3) Spindle path design and programming

[0048] Use CAD software to draw a V-shaped path with an included angle of 45°. According to the drawn CAD path, use G code to program and import it into CNC equipment.

[0049] (4) Texture processing

[0050] Put the punched mobile phone case on the jig prepared in step (2) to fix it, spray a sm...

Embodiment 3

[0052] (1) Metal substrate

[0053] The aluminum plate (model 5056) is punched into the shape of the mobile phone shell (84mm×54mm×0.5mm) by stamping technology.

[0054] (2) Production of jigs

[0055] According to the shape of the stamped mobile phone case, a jig is made, and the material is aluminum alloy, which is used to clamp the stamped mobile phone case.

[0056] (3) Spindle path design and programming

[0057] Use CAD software to draw a V-shaped path with an included angle of 90°. According to the drawn CAD path, use G code to program and import it into CNC equipment.

[0058] (4) Texture processing

[0059] Put the stamped mobile phone case on the jig prepared in step (2) to fix it, spray a small amount of WD-40 universal anti-rust lubricant on the aluminum material, press the start button, and the programmed processing can be performed program. The machining depth is 0.01mm, the spacing is 0.3mm, the spindle speed is 3000r / min, the feed speed of X-axis and Y-ax...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
angleaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a micromachining method of textures on a metal surface. The method comprises the following steps of: putting a metal base material on a machining face plate of a numerical control machine which has the linkage of an X axle, a Y axle and a Z axle, wherein the X axle controls the left and right movement in a horizontal direction of the numerical control machine; the Y axle controls the forward and backward movement in the horizontal direction of the numerical control machine; the Z axle controls the movement in the vertical direction of the numerical control machine; and a circular cutter head is arranged on the numerical control machine, and a cutter is arranged on an edge of the circular cutter head; and controlling a motion path of the circular cutter head of the numerical control machine, wherein the circular cutter head drives the cutter to cut so as to form a cutting path, the textures can be obtained on the surface of the metal base material by repeating the cutting path, and the circular cutter head performs uniform motion along the horizontal direction in the cutting process when the motion path of the circular cutter head is one of a V type, an X type and a circular arc shape. By the method, various novel textures can be formed on the metal base material, a three-dimensional (3D) effect can be achieved, and the textures have good handfeel.

Description

technical field [0001] The invention relates to a micro-machining method for textures on metal surfaces, which belongs to the field of surface treatment of metal materials. Background technique [0002] During the processing of metal materials, micro-machining methods are often used to form patterns with decorative effects on the metal surface, such as chemical etching, laser engraving, etc. Compared with the above-mentioned chemical etching and laser engraving and other processing methods, the CNC machine tool (CNC) micro-machining method has a high degree of automation, and the processed pattern has a strong three-dimensional effect and a good hand feel. At the same time, it has the advantages of high gloss effect, no pollution, and high production efficiency. However, at present, CNC micromachining mainly forms some simple lines on flat metal materials, or just mills off a layer of the surface to achieve a high-gloss effect. At present, there is no way to obtain complex ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B23P9/00B44C1/22B44C1/00
Inventor 包小营周飞陈云
Owner BYD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap