Medium-deep-layer carburization or carbonitriding thermal processing technology for bearings or clutch parts

A carbonitriding and parts technology, applied in the field of heat treatment, can solve the problems of unsuitable to bear heavy loads, high labor intensity of workers, low production efficiency, etc., to reduce frequent opening and closing actions, achieve non-oxidative treatment, and increase production capacity. Effect
CN102154652BActive Publication Date: 2012-11-28JIANG SU NAN FANG BEARING CO LTD
0 Cites 1 Cited by

Patent Information

Authority / Receiving Office
CN Β· China
Patent Type
Patents(China)
Current Assignee / Owner
JIANG SU NAN FANG BEARING CO LTD
Publication Date
2012-11-28

Smart Images

  • Figure 1
    Figure 1
Patent Text Reader

Abstract

The invention relates to a medium-deep-layer carburization or carbonitriding thermal processing technology for bearings or clutch parts. In the invention, the carburization or carbonitriding is carried on parts by utilizing a continuous production line of a carrier roller type mesh belt furnace with a controllable atmosphere, and the technology comprises the following steps in sequence: strong permeation, diffusion, quenching, cleaning, low-temperature tempering, discharging and air cooling. In the invention, the continuous production line of the carrier roller type mesh belt furnace with thecontrollable atmosphere is used for carrying out the medium-deep-layer carburization or carbonitriding, thus continuous production is realized, the production efficiency is improved, the productivityis increased, frequent opening and closing actions of a gap furnace can be reduced, non-oxidization treatment is realized, and the labor intensity is reduced; and in addition, carbon potentials in all areas of the mesh belt furnace are respectively controlled so as to guarantee the quality stability.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to the technical field of heat treatment, in particular to a middle-deep carburizing or carbonitriding heat treatment process for bearing or clutch parts. Background technique

[0002] Carburizing is a chemical heat treatment process in which the steel is heated and kept warm in a carburizing medium to increase the carbon content and a certain carbon concentration gradient on the surface of the steel so that carbon atoms can penetrate into the surface. Quenching and tempering after carburizing can improve the surface hardness and wear resistance of the parts, while the core has good toughness. Carbonitriding is a heat treatment process in which nitrogen and carbon are infiltrated into the surface of the workpiece, and nitriding is the main method. The infiltration layer has lower hardness and less brittleness. The main advantage is that the deformation of the workpiece is small, and it is not limited by the steel type. However,...