Manufacturing process for antistatic hard coating plastic film

A hard coating, plastic film technology, applied in conductive coatings, coatings, polyester coatings, etc., can solve the problem of short retention time of antistatic performance, and achieve short retention time of antistatic performance and excellent scratch resistance , the effect of high light transmittance

Active Publication Date: 2011-09-28
SUZHOU SIDIKE NEW MATERIALS SCI & TECH
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention provides a method for manufacturing an antistatic hard-coated plastic film, aiming to solve the problem that the antistatic performance of the existing film material is kept for a short time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment one: a kind of manufacture method of antistatic property hard-coated plastic film mainly is made up of following steps:

[0035] At first the surface of the plastic film substrate polyethylene terephthalate film with a thickness of 100 microns is cleaned, and then the following operations are carried out:

[0036] The first step: coating one deck antistatic hard coating on the surface of plastic film base material, thickness is 3 microns, and this antistatic hard coating is made up of the compound of following percentage by weight:

[0037] Silicone 4%;

[0038] Multifunctional acrylate monomer 39.5%;

[0039] Initiator 0.5%;

[0040] Solvent 56%;

[0041] The organosilicon is trimethylsilanol;

[0042] The multifunctional acrylate monomer is formed by mixing methyl acrylate, ethyl acrylate and alkoxylated lauryl acrylate in a mass ratio of 1:1:2;

[0043] The initiator is benzophenone;

[0044] The solvent is toluene;

[0045] The second step: irradia...

Embodiment 2 5

[0063] Embodiment two~five: the manufacture method of antistatic hard coating plastic film

[0064] One, the processing technology of embodiment two~five is with embodiment one.

[0065] Two, the formula of the antistatic hard coating of embodiment two~five is as follows:

[0066]

Silicone

Multifunctional Acrylate Monomer

Initiator

solvent

Embodiment two

3%

35%

0.2%

61.8%

Embodiment Three

5%

30%

0.5%

64.5%

Embodiment four

2%

43%

0.7%

54.3%

Embodiment five

2.5%

45%

1%

51.5%

[0067] Note:

[0068] 1. The percentage by mass indicated by the percentage sign in the above table.

[0069] 2, plastic film substrate: embodiment two, 90 micron thick polycarbonate; Embodiment three, 150 micron thick polyvinyl chloride plastic film; Embodiment four, 80 micron thick polyethylene terephthalate Film; Embodiment five, the polyethylene film after 200 microns.

[0070] 3. Organic si...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

Disclosed is a manufacturing process for an antistatic hard coating plastic film, comprising a first step of coating an antistatic hard coating onto the surface of a plastic film substrate and a second step of irradiating the antistatic hard coating with ultraviolet rays so as to react organosilicon with multifunctional acrylate monomers under the condition of an initiator. The antistatic hard coating plastic film provided in the invention has not only excellent antistatic performance, but also good sharpness and scratch resistance. Therefore, such antistatic hard coating plastic films can beused in liquid crystal display devices or be used as films for the protection of various image display devices.

Description

technical field [0001] The invention relates to a method for manufacturing an antistatic hard-coated plastic film, in particular to a method for endowing the film with antistatic and hard properties by a coating method. Background technique [0002] Plastic film is a film made of polyvinyl chloride, polyethylene, polypropylene, polystyrene, etc., and other resins, used for packaging, and as a coating layer. Plastic film is a macromolecular structure formed by polymerization and cross-linking of compounds, so it has a certain strength, and is an indispensable material with many types of products, easy processing, and abundant raw materials. [0003] However, the current plastic film has a small dielectric constant, generally belongs to non-conductor, and has high insulation performance. Therefore, the generation of static electricity cannot be avoided. Due to the accumulation of electrostatic charge on the surface of the plastic film, it is easy to cause the surface to absor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J7/04C08J3/28C09D4/02C09D167/06C09D5/24
Inventor 金闯
Owner SUZHOU SIDIKE NEW MATERIALS SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com