Low-temperature solidifying electroplating surface screen printing ink

A surface silk and ink technology, applied in ink, household utensils, applications, etc., can solve the problem that the electroplating surface screen printing ink cannot be cured at low temperature, and achieve the effects of high hardness, convenient use, and excellent adhesion

Inactive Publication Date: 2014-02-26
深圳市美丽华科技股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above-mentioned deficiencies in the prior art, the purpose of the present invention is to provide a low-temperature curable electroplating surface silk screen printing ink, aiming to solve the problem that the existing electroplating surface silk screen printing ink cannot be cured at low temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-temperature solidifying electroplating surface screen printing ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Under normal temperature and pressure, take 35 parts (weight) of ether solvent, add 30 parts (weight) of acrylic resin, 20 parts (weight) of epoxy resin, mix with a mixer, and stir at a speed of 600-1000RPM for 10-20MIN to dissolve After completion, add 1 part (weight) of dispersant and 12.5 parts (weight) of pigment, stir evenly, and then grind it with a three-roller machine to a fineness below 10 μm, then add 1.5 parts (weight) of defoamer, stir and disperse evenly to obtain the finished product.

Embodiment 2

[0051] Under normal temperature and pressure, take 30 parts (weight) of ether solvent, add 30 parts (weight) of acrylic resin, 25 parts (weight) of epoxy resin, mix with a mixer, and stir at a speed of 600-1000RPM for 10-20MIN to dissolve After completion, add 1 part (weight) of dispersant and 12.5 parts (weight) of pigment, stir evenly, and then grind it with a three-roller machine to a fineness below 10 μm, then add 1.5 parts (weight) of defoamer, stir and disperse evenly to obtain the finished product.

[0052] The low-temperature curing electroplating surface screen printing ink obtained in the above examples is shown in the effect of 300 mesh screen printing and the state of physical and chemical indicators on the electroplating surface material. figure 1 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low-temperature solidifying electroplating surface screen printing ink, which is composed of the following components in percentage by weight: 20-40% of acrylic resin, 10-30% of epoxy resin, 25-35% of solvent, 5-35% of pigment, 0.1-5% of dispersing agent and 0.1-5% of defoamer. The solvent used in the ink disclosed by the invention is environmentally-friendly, is free of PAHS (polycyclic aromatic hydrocarbon), can be solidified at low temperature and is naturally volatilized. Surface drying time is 5-10min, hard drying time is 24 hours, or the solvent can be completely solidified if being baked at 80DEG C for 20min. In addition, the solvent has the advantages of high hardness, excellent adhesive force, chemical resistance, high efficacy and energy saving, is environmentally friendly and is convenient to use.

Description

technical field [0001] The invention relates to silk screen printing ink, in particular to a low-temperature curing electroplated screen printing ink. Background technique [0002] The process of some electroplating products includes spraying, blistering, etc., which cannot be baked at high temperature. However, most of the electroplated screen printing inks and coatings on the market are high-temperature curing systems, and the baking temperature is 120-180°C. Higher temperatures are required to achieve high hardness, adhesion, and chemical resistance. This not only leads to waste of resources, but also runs counter to the social development theme of promoting high efficiency, energy saving, and environmental protection. [0003] Therefore, the prior art needs to be perfected and developed. Contents of the invention [0004] In view of the above deficiencies in the prior art, the purpose of the present invention is to provide a screen printing ink that can be cured at lo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/10C09D11/102C09D11/107
Inventor 胡萍
Owner 深圳市美丽华科技股份有限公司