Aqueous two-component clear paint and preparation method thereof
A two-component, clear paint technology used in coatings to solve problems such as lack of adhesion, poor stain and chemical resistance, easy yellowing, easy mixing, excellent gloss and appearance, stain resistance and chemical resistance high quality effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] a. According to weight, add 50 parts of polyacrylic acid polyol, 0.1 part of dispersant (BYK 194 from Germany), 0.1 part of anti-sedimentation agent (Disparon LA350), and defoamer (Dego Company) into the stirring container in sequence. Tego 902W) 0.1 parts, stir evenly, slowly add 5.0 parts of pigments and fillers under stirring at 700 rpm, adjust the stirring speed to 1200 rpm and stir for 10 minutes, then add leveling agent (BYK346 from Germany) 0.1 1 part, 0.1 part of film-forming aid, stir evenly under stirring at 700 rpm, clean the equipment with 1.0 part of water and adjust the viscosity to 120KU, filter to obtain component A.
[0020] b. According to the ratio of component A: component B: water = 1:0.2:0.3, the finished product is obtained. The component B is anion-modified HDI polyisocyanate.
Embodiment 2
[0022] a. According to the weight, add 60 parts of polyacrylic acid polyol, 0.5 parts of dispersant (Tego730W of Tego Company), 0.5 parts of anti-sedimentation agent (Disparon LA350) and defoaming agent (Germany BYK) into the stirring container in sequence. BYK028) 0.5 parts and stir evenly, slowly add 10.0 parts of pigments and fillers under stirring at 700 rpm, adjust the stirring speed to 1500 rpm and stir for 15 minutes, then add 0.5 parts of leveling agent (BYK346 from Germany) in turn, 2.0 parts of membrane aid, stirred evenly under 700 rpm stirring, 5.0 parts of water to clean the equipment and adjust the viscosity to 130KU, and filter to obtain component A.
[0023] b. According to the ratio of component A: component B: water = 1:0.3:0.5, the finished product is prepared evenly, and the component B is anion-modified HDI polyisocyanate.
Embodiment 3
[0025] a. According to weight, add 55 parts of polyacrylic acid polyol, 0.3 parts of dispersant (BYK194 from BYK, Germany), 0.3 parts of anti-sedimentation agent (DISPARON LA350), and defoamer (BYK from Germany) in the stirring container. BYK028) 0.3 parts and stir evenly, slowly add 8 parts of pigments and fillers under stirring at 700 rpm, adjust the stirring speed to 1400 rpm and stir for 12 minutes, then add 0.3 parts of leveling agent (EFKA3600 from Efka Company), 1 part of film-forming aid, stirred evenly under stirring at 700 rpm, cleaned the equipment with 3 parts of water and adjusted the viscosity to 125KU, filtered to obtain component A.
[0026] b. According to the ratio of component A: component B: water = 1:0.25:0.4, the finished product is obtained. The component B is anion-modified HDI polyisocyanate.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap