Waterproof crack-resistant inorganic heat-insulating mortar and preparation method thereof

The technology of inorganic thermal insulation mortar and ceramic sand is applied in the field of building thermal insulation, which can solve the problems of high water absorption rate and easy cracking, and achieve the effects of reducing water absorption rate, increasing strength and improving impermeability.

Inactive Publication Date: 2012-04-25
上海英硕聚合材料股份有限公司
View PDF4 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention can solve the problems of high water absorption rate, water seepage and easy cracking of traditional inorganic expansion vitrified microbead thermal insulation mortar by using pottery sand and permeable crystalline waterproofing agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof crack-resistant inorganic heat-insulating mortar and preparation method thereof
  • Waterproof crack-resistant inorganic heat-insulating mortar and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The components and parts by weight of Examples 1-3 are shown in Table 1. Wherein, the viscosity of hydroxypropyl methylcellulose ether in embodiment 1 is 40000mPa·S, and the bulk density of expanded vitrified microspheres is 90kg / m 3 The particle diameter of described pottery sand is 5mm, and the grade of ordinary portland cement is 42.5; The viscosity of hydroxypropyl methyl cellulose ether is 70000mPa·S among the embodiment 2, and the bulk density of expanded vitrified microbead is 100kg / m 3 The particle diameter of described pottery sand is 3mm, and the grade of ordinary portland cement is 42.5; The viscosity of hydroxypropyl methyl cellulose ether is 100000mPa·S among the embodiment 3, and the bulk density of expanded vitrified microbead is 110kg / m 3 ; The particle size of the pottery sand is 1mm, and the grade of ordinary Portland cement is 52.5.

[0033] Table 1

[0034]

[0035] The ordinary Portland cement, silica fume, slaked lime, hydroxypropyl methyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to waterproof crack-resistant inorganic heat-insulating mortar and a preparation method thereof. The mortar comprises 5-10 m<3> of small expended and vitrified balls, 0-1 m<3> of pottery sand, 750-850 kg of ordinary portland cement, 50-100 kg of calcium powder, 35-70 kg of hydrated lime, 30-55 kg of siliceous dust, 15-20 kg of dispersible polymer powder, 4-8 kg of hydroxypropyl methyl cellulose ether, 1-2 kg of mekralon, 0.5-1 kg of capillary crystalline waterfroof agent, and 3-5 kg of wood fiber. The preparation method comprises the following steps: loading ordinary portland cement, siliceous dust, hydrated lime, hydroxypropyl methyl cellulose ether, dispersible polymer powder, calcium powder, mekralon, capillary crystalline waterfroof agent and wood fiber at one time, and stirring for 3 min; adding small expended and vitrified balls and pottery sand in the stirred powder blend, and continuously stirring for 2 min; and packaging and storing the finished productsin warehouse. Compared with the prior art, by using the pottery sand and capillary crystalline waterfroof agent, the problems of large water absorption, easy cracking when water seepage occurs and the like of traditional inorganic small expended and vitrified ball heat-insulating mortar are solved.

Description

technical field [0001] The invention relates to a waterproof and crack-resistant inorganic thermal insulation mortar. The material can be used for thermal insulation of external walls, and is particularly suitable for internal thermal insulation of external walls, internal walls and household walls, and belongs to the field of thermal insulation of buildings. Background technique [0002] Due to the upgrading of fireproof performance requirements of building insulation materials, inorganic insulation materials have become the mainstream materials of insulation materials. Among them, inorganic thermal insulation mortar has a Class A combustion grade and has become one of the main products of building energy-saving materials in hot summer and warm winter regions. After searching the literature of the prior art, it was found that the patent number is CN101863639, and the patent name is an invention patent for an inorganic thermal insulation mortar used for building exterior wal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
Inventor 尧璟云辛春华阮丰乐成时亮陈精键方强
Owner 上海英硕聚合材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap