Kesterite structure Cu2ZnSnS4 powder material and liquid phase preparation method thereof

A powder material, kesterite technology, applied in the direction of microsphere preparation, chemical instruments and methods, tin compounds, etc., can solve few problems, achieve the effect of low cost, low temperature, and easy control of product properties

Inactive Publication Date: 2012-06-20
CENT SOUTH UNIV
View PDF2 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For the manufacture of Cu 2 ZnSnS 4 For solar cells, the first and critical step is to synthesize high-quality Cu 2 ZnSnS 4 nanocrystalline, however so far, Cu 2 ZnSnS 4 There are few reports on the preparation of nanocrystals

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Kesterite structure Cu2ZnSnS4 powder material and liquid phase preparation method thereof
  • Kesterite structure Cu2ZnSnS4 powder material and liquid phase preparation method thereof
  • Kesterite structure Cu2ZnSnS4 powder material and liquid phase preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Weigh 0.01mmolCuCl 2 2H 2 O, 0.005 mmol ZnCl 2 , 0.005mmolSnCl 4 ·5H 2 O, 0.02mmol sulfur powder, put into a three-necked round-bottomed flask, add 50ml of triethylenetetramine, and leave it for 3-5 minutes to obtain a uniform brick-red solution, feed nitrogen as a protective gas, and place the three-necked round-bottomed flask Heated to 200°C in a constant temperature oil bath and kept for 2 hours, then naturally cooled to room temperature, washed with anhydrous ethanol and ionized water for 3 times, then filtered, and dried at 60°C in a drying oven for 6 hours to obtain black solid.

Embodiment 2

[0032] Weigh 0.015mmolCuCl 2 2H 2 O, 0.008 mmol ZnCl 2 , 0.008mmolSnCl 4 ·5H 2 O, 0.04mmol sulfur powder, put into a three-necked round-bottomed flask, add 60ml of triethylenetetramine, leave it for 3-5 minutes to obtain a uniform brick-red solution, feed nitrogen as protective gas, and place the three-necked round-bottomed flask Heated to 150°C in a constant temperature oil bath and kept for 2 hours, then naturally cooled to room temperature, washed with absolute ethanol and ionized water for 3 times, then filtered, and dried at 60°C in a drying oven for 6 hours to obtain black solid.

Embodiment 3

[0034] Weigh 0.015mmolCuCl 2 2H 2 O, 0.008 mmol ZnCl 2 , 0.008mmolSnCl 4 ·5H 2O, 0.04mmol sulfur powder, put into a three-necked round-bottomed flask, add 60ml of triethylenetetramine, leave it for 3-5 minutes to obtain a uniform brick-red solution, feed nitrogen as protective gas, and place the three-necked round-bottomed flask Heated to 150°C in a constant temperature oil bath and kept for 6 hours, then cooled naturally to room temperature, washed with absolute ethanol and ionized water for 3 times, then filtered, and dried at 60°C in a drying oven for 6 hours to obtain black solid.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a kesterite structure Cu2ZnSnS4 powder material for a solar photovoltaic cell, and a liquid phase preparation method thereof; the liquid phase preparation method comprises the steps that: the material is weighed in the principle of CuCl2.2H2O:ZnCl2:SnCl4.5H2O:sulphur powder=2 (1 to 1. 5): (1 to 1. 5): (4 to 5) (molar ratio) and put into a round-bottom three-neck flask to be mixed, then organic solvent triethylene tetramine solution is added in, the mixture stays still for 3min to 5min, and uniform brick red solution is obtained; after nitrogen is fed in as protective gas, and the brick red solution is put into constant temperature oil bath to be heated to 120DEG C to 240DEG C, maintained for 0.5h to 12h, and then naturally cooled to room temperature; anhydrous ethanol and distilled water are used for sequentially washing a product, then the product is filtered and dried, and black powder is obtained. The liquid phase preparation method of the kesterite structure Cu2ZnSnS4 powder material is green, has no pollution, short reaction time and low required temperature, is convenient to operate, has low cost, and is applicable to the large-scale production of Cu2ZnSnS4 powder (for a photovoltaic cell absorption layer).

Description

technical field [0001] The invention belongs to the field of preparation methods of raw materials for solar photovoltaic cells, and relates to a kesterite structure Cu 2 ZnSnS 4 Powder material and liquid phase preparation method thereof, the kesterite structure Cu 2 ZnSnS 4 The powder is applied to the absorber layer of CZTS thin film solar cells. Background technique [0002] Facing the energy problem and the environmental pollution caused by the burning of fossil fuels, the development of solar cells has become an important way to solve energy and environmental problems. With the widespread use of photovoltaic modules, improving the photoelectric conversion efficiency of cells and reducing costs are the main issues of photovoltaic power generation at present. [0003] Among many solar cells, CuIn x Ga 1-x S(Se) 2 (CIGS) thin film solar cells have received extensive attention due to their high photoelectric conversion efficiency and good stability. However, the hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J13/02C01G19/00H01L31/18
CPCY02P70/50
Inventor 周继承游亮
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com