Large-specification fine-grain isotropic isostatic-pressing graphite

An isotropic, fine-grained technology, applied in the direction of graphite, can solve the problems of unsatisfactory physical and chemical indicators of mechanical properties, poor strength, density and elastic properties, uneven bulk density, etc., and achieve excellent physical and chemical indicators of mechanical properties, density and Good elasticity, uniform and delicate structure

Inactive Publication Date: 2012-06-20
雅安恒圣高纯石墨科技有限责任公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the deficiency of existing isostatic graphite materials, provide a new type of isotropic isostatic graphite with large-scale fine particles, overcome the small production specifications of traditional graphite materials, and cannot realize the production of large-scale graphite products Poor strength, density and elastic properties, unsatisfactory physical and chemical indicators of mechanical properties; high porosity in graphite materials, which affects material quality; rough particle size of component structure, uneven and low volume density, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Large-specification fine-grain isotropic isostatic-pressing graphite
  • Large-specification fine-grain isotropic isostatic-pressing graphite
  • Large-specification fine-grain isotropic isostatic-pressing graphite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] [Example 1] Large-scale fine particle isotropic isostatic graphite, which is mainly composed of the following components by weight:

[0026] Powder 52

[0027] Modified bitumen 35;

[0028] Wherein, described material powder is made of the component of following weight ratio:

[0029] Premade coke powder 75

[0030] Graphite powder 2

[0031] Additive 2;

[0032] Described prefabricated crushed coke powder is made of the following components in weight ratio:

[0033] Prefabricated Powder 52

[0034] Modified bitumen 35;

[0035] Described prefabricated powder is made of the following components by weight ratio:

[0036] Petroleum coke 55

[0037] Graphite powder 16

[0038] Carburizer 26

[0039] fine powder 3.

Embodiment 2

[0040] [Example 2] Large-scale fine particle isotropic isostatic graphite, which is mainly composed of the following components by weight:

[0041] Powder 65

[0042] modified bitumen 48;

[0043] Wherein, described material powder is made of the component of following weight ratio:

[0044] Premade coke powder 94

[0045] Graphite powder 6

[0046] Additive 2;

[0047] Described prefabricated crushed coke powder is made of the following components in weight ratio:

[0048] Prefabricated Powder 65

[0049] modified bitumen 48;

[0050] Described prefabricated powder is made of the following components by weight ratio:

[0051] Petroleum coke 85

[0052] Graphite powder 6

[0053] Carburizer 7

[0054] fine powder 2.

Embodiment 3

[0055] [Example 3] Large-scale fine particle isotropic isostatic graphite, which is mainly composed of the following components by weight:

[0056] Powder 60

[0057] Modified asphalt 40;

[0058] Wherein, described material powder is made of the component of following weight ratio:

[0059] Premade coke powder 85

[0060] Graphite powder 10

[0061] Additive 5;

[0062] Described prefabricated crushed coke powder is made of the following components in weight ratio:

[0063] Prefabricated Powder 60

[0064] Modified asphalt 40;

[0065] Described prefabricated powder is made of the following components by weight ratio:

[0066] Petroleum coke 70

[0067] Graphite powder 8

[0068] Carburizer 20

[0069] fine powder 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses large-specification fine-grain isotropic isostatic-pressing high-purity graphite mainly composed of components of, by weight: 52-65 parts of material powder, and 35-48 parts of modified pitch. The material powder is composed of components of, by weight: 75-94 parts of prefabricated crushed coke powder, 2-18 parts of graphite powder, and 2-8 parts of an additive. The prefabricated crushed coke powder is composed of components of, by weight: 52-65 parts of prefabricated material powder, and 35-48 parts of modified pitch. The prefabricated material powder is composed of components of, by weight: 52-85 parts of petroleum coke, 2-20 parts of graphite powder, 6-45 parts of a carburant, and 3-12 parts of fine powder. The production specification of the graphite is large. According to the invention, production of graphite with a large-specification of phi900 can be realized. The graphite is advantaged in high strength, high density, good elasticity, excellent mechanical properties, and excellent physical chemical index. The graphite material is advantaged in low porosity, good quality, uniform and delicate structure, and relatively high volume density.

Description

technical field [0001] The invention relates to a large-scale fine particle isotropic isostatic graphite. Background technique [0002] Isostatic graphite material has good electrical and thermal conductivity, high temperature resistance, good corrosion resistance, self-lubricating, high bulk density, easy for technicians, etc., and is closely connected with today's high-tech cutting-edge technology. It has been widely used in economic, chemical, aerospace and nuclear energy sectors and industries, especially in various nuclear fusion devices. The existing graphite production industry generally believes that the graphite material prepared from graphite powder as a raw material has low strength and cannot meet the high requirements for use strength, and materials such as petroleum coke and pitch coke are used instead of graphite powder. [0003] The existing isostatic graphite materials have the following disadvantages: (1) The production specifications are small, and the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01B31/04C01B32/20
Inventor 叶有发
Owner 雅安恒圣高纯石墨科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap