Production process for famille-rose peony porcelain

A production process, peony porcelain technology, applied in the field of porcelain production, to achieve the effect of lifelike image, artistic value and beautiful shape

Active Publication Date: 2013-09-11
李学武
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] It can be seen from the above that ceramics, as a kind of utensils that can be preserved for a long time, can keep flowers blooming forever if they are combined with flower making. After searching, no combination of ceramics and flowers has been found.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] The invention relates to a manufacturing process of famille rose peony porcelain, which is fired by using porcelain clay base material, glaze raw material and colored china clay, wherein the colored china clay includes red china clay, pink china clay, yellow china clay and green china clay,

[0064] The china clay base material is composed of aluminum oxide, iron oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, titanium dioxide and quartz, and the weight percentage of each raw material is: 20% of aluminum oxide, 0.3% of iron oxide, 0.3% of Calcium 0.01%, Magnesium Oxide 0.01%, Potassium Oxide 2.5%, Sodium Oxide 0.14%, Titanium Dioxide 0.04% and Quartz 77%;

[0065] Using white feldspar, quartz, calcite, kaolin, alumina, white clay, porcelain stone and potassium feldspar as glaze raw materials, the weight ratio of each raw material is: white feldspar 6%, quartz 10%, calcite 4%, kaolin 15% %, alumina 5%, clay 30%, porcelain stone 15%, potassium feldsp...

Embodiment 2

[0085] The invention relates to a manufacturing process of famille rose peony porcelain, which is fired by using porcelain clay base material, glaze raw material and colored china clay, wherein the colored china clay includes red china clay, pink china clay, yellow china clay and green china clay,

[0086] The china clay base material is composed of aluminum oxide, iron oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, titanium dioxide and quartz, and the weight percentage of each raw material is: 30% of aluminum oxide, 0.3% of iron oxide, 0.3% of Calcium 0.01%, magnesium oxide 0.01%, potassium oxide 2.4%, sodium oxide 0.14%, titanium dioxide 0.04% and quartz 67%;

[0087] Using white feldspar, quartz, calcite, kaolin, alumina, white clay, porcelain stone and potassium feldspar as glaze raw materials, the weight ratio of each raw material is: white feldspar 10%, quartz 4%, calcite 6%, kaolin 17% %, alumina 3%, white clay 25%, porcelain stone 17%, potassium ...

Embodiment 3

[0107] The invention relates to a manufacturing process of famille rose peony porcelain, which is fired by using porcelain clay base material, glaze raw material and colored china clay, wherein the colored china clay includes red china clay, pink china clay, yellow china clay and green china clay,

[0108] The china clay base material is composed of aluminum oxide, iron oxide, calcium oxide, magnesium oxide, potassium oxide, sodium oxide, titanium dioxide and quartz, and the weight percentages of each raw material added are: aluminum oxide 26.7%, iron oxide 0.36%, oxide Calcium 0.01%, magnesium oxide 0.01%, potassium oxide 2.7%, sodium oxide 0.18%, titanium dioxide 0.04% and quartz 70%;

[0109] Using white feldspar, quartz, calcite, kaolin, alumina, white clay, porcelain stone and potassium feldspar as glaze raw materials, the weight ratio of each raw material added is: white feldspar 4%, quartz 6%, calcite 10%, kaolin 20% %, alumina 4%, clay 18%, porcelain stone 18%, potassi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A production process for famille-rose peony porcelain is disclosed, wherein a porcelain clay matrix, a glaze material and colour porcelain clays are used for being fired, and the colour porcelain clays comprise red clay, pink clay, yellow clay and green clay. The production process for famille-rose peony porcelain comprises the following steps of: step 1, producing a clay base; step 2, producing a colour clay; step 3, producing a glaze; step 4, producing a semi-finished product; step 5, biscuiting; step 6, glazing; step 7, moulding and making patterns; step 8, calcining; and step 9, firing again, taking out, staying to a room temperature, and then producing the finished product. The porcelain produced by the process can be fired by combining with porcelain flowers and porcelain, so as to product peony porcelain with overglaze colour drawing.

Description

technical field [0001] The invention relates to a method for making porcelain, in particular to a method for making ornamental flower peony porcelain by using pigments for overglaze color painting. Background technique [0002] As we all know, peonies, roses, chrysanthemums, peonies and other ornamental flowers have a short flowering period, but the flowers are very bright, which can add a lot of bright spots to indoors or celebrations, but as the saying goes: "Flowers don't always bloom, youth doesn't always exist" , which means that although flowers are good, they only bloom for a limited time, and the flowering period is very short; flowers need corresponding ecological conditions to grow and open. [0003] It is known that ceramics, as a common utensil "including daily necessities such as cups, teapots, and bowls", have existed for thousands of years. In my country, pottery was invented as early as about 8000-2000 BC (Neolithic Age). . The main components of ceramic mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/18C04B41/86
Inventor 李学武
Owner 李学武
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap