Process for printing characters on polytetrafluoroethylene workpiece
A polytetrafluoroethylene and workpiece technology, used in printing, printing devices, etc., can solve the problems of character adhesion ink temperature resistance and solvent resistance not meeting the requirements for use, and improve product appearance quality and thin character lines. The effect of uniformity and improvement of printing quality
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] The technique of printing characters on the polytetrafluoroethylene workpiece described in the present embodiment comprises the following steps:
[0021] a. Mechanically process the PTFE material to obtain the PTFE workpiece, and control the smoothness of the printing surface of the PTFE workpiece to 1.6 μm;
[0022] B, adopt chloroform solvent to clean the polytetrafluoroethylene workpiece gained in the step a, remove the oil stain and impurity on the printed surface of the polytetrafluoroethylene workpiece, and dry naturally;
[0023] c. Use a manual roller printing tool to evenly coat the high-temperature ribbon ink with a color difference ΔE of 120 from the PTFE workpiece substrate on the surface of the PTFE workpiece to be printed to form a layer of ink ribbon printing layer;
[0024] d. Put the polytetrafluoroethylene workpiece prepared in step c into an oven and bake at a temperature of 150° C. for 1 hour to solidify the ink;
[0025] e, adopt laser printing mod...
Embodiment 2
[0027] The technique of printing characters on the polytetrafluoroethylene workpiece described in the present embodiment comprises the following steps:
[0028] a. Mechanically process the PTFE material to obtain the PTFE workpiece, and control the smoothness of the printing surface of the PTFE workpiece to 2.0 μm;
[0029] B, adopt chloroform solvent to clean the polytetrafluoroethylene workpiece gained in the step a, remove the oil stain and impurity on the printed surface of the polytetrafluoroethylene workpiece, and dry naturally;
[0030] c. Use a manual roller printing tool to evenly coat 7224 light blue imported high-temperature ribbon ink on the surface of the PTFE workpiece to be printed to form a layer of ink ribbon printing layer;
[0031] d. Put the polytetrafluoroethylene workpiece prepared in step c into an oven and bake at a temperature of 170° C. for 1 hour to solidify the ink;
[0032] e. Printing characters on the printed surface of the polytetrafluoroethyle...
Embodiment 3
[0034] A kind of technique of printing characters on polytetrafluoroethylene workpiece described in the present embodiment, comprises the following steps:
[0035] a. Mechanically process the PTFE material to obtain the PTFE workpiece, and control the smoothness of the printed surface of the PTFE workpiece to 3.2 μm;
[0036] B, adopt chloroform solvent to clean the polytetrafluoroethylene workpiece gained in the step a, remove the oil stain and impurity on the printed surface of the polytetrafluoroethylene workpiece, and dry naturally;
[0037] c. Use a manual roller printing tool to evenly coat the high-temperature ribbon ink with a color difference ΔE of 250 from the PTFE workpiece substrate on the surface of the PTFE workpiece to be printed to form a layer of ink ribbon printing layer;
[0038] d. Put the polytetrafluoroethylene workpiece prepared in step c into an oven and bake at a temperature of 160° C. for 1.5 hours to cure the ink;
[0039] e, adopt laser printing mo...
PUM
Property | Measurement | Unit |
---|---|---|
surface smoothness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap