Buffing burnt-feeling water-based Yangbuck foaming resin and preparation method thereof

A foamed resin and water-sensitive technology, which is applied in the field of water-based yambar foamed resin and its preparation, can solve the problems of not being scratch resistant, not having a burnt feeling, and poor smoothing effect, etc., and achieve good scratch resistance, Imitation leather effect is good

Inactive Publication Date: 2013-04-17
SUZHOU DEERUN COMPOSITE MATERIALS
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although these two kinds of Yangbuck resins have a series of advantages as described above, the effect of down-smoothing wool is not good, it is not scratch-resistant, and does not have a burnt feeling, so the effect of imitation leather is not ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Buffing burnt-feeling water-based Yangbuck foaming resin and preparation method thereof
  • Buffing burnt-feeling water-based Yangbuck foaming resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] This example provides a water-based yangbuck foaming resin with a burnt skin texture. In parts by weight, its raw material formula is as follows: 50 parts of water-based acrylic resin; 45 parts of water; 1 part of modified silicone-based water-based defoamer; 3 parts of yangbuck powder; 6 parts of polyurethane water-based thickener; 3 parts of water-based scorching wax powder (polyethylene wax and amide wax mixture); 3 parts of water-based leveling agent (octylphenol polyoxyethylene ether); fungicide 0.8 parts of tetrachloroisophthalonitrile (TPN), 4 parts of organic bentonite.

[0019] The preparation method of the water-based yambuck foaming resin with scorching skin texture is as follows: disperse the organic bentonite with an equal amount of water; add the remaining amount of water, water-based leveling agent, yambuck powder, and water-based Rub scorched wax powder, stir until evenly dispersed, then add water-based defoamer, stir for a period of time (about 5 minute...

Embodiment 2

[0021] This example provides a kind of water-based yambuck foaming resin with a burnt skin texture, and its raw material formula is as follows in parts by weight: 50 parts of water-based acrylic resin; 45 parts of water; 1 part of water-based defoamer; 2 parts of fine yangbuck powder , 2 parts of coarse yangbuck powder; 6 parts of water-based thickener; 3 parts of water-based scorching wax powder; 3 parts of water-based leveling agent; 0.8 part of fungicide, 4 parts of organic bentonite. Among them: water-based defoamer is modified silicone defoamer, water-based thickener is polyurethane thickener, water-based scorching wax powder is a mixture of polyethylene wax and amide wax or purchased from Clariant, water-based leveling agent It is octylphenol polyoxyethylene ether, and the fungicide is tetrachloroisophthalonitrile (TPN). The preparation method of the scorched water-based yambuck foaming resin for dermabrasion is the same as that in Example 1.

Embodiment 3

[0023] This example provides a kind of water-based yambuck foaming resin with a burnt skin effect, and its raw material formula is as follows in parts by weight: 52 parts of water-based acrylic resin; 47 parts of water; 1.5 parts of water-based defoamer; 1 part of fine yambuck powder , 1 part of medium-sized yangbuck powder, 1 part of coarse yangbuck powder; 6 parts of water-based thickener; 3 parts of water-based scorching wax powder; 3 parts of water-based leveling agent; 0.5 part of fungicide, 5 parts of organic bentonite. Among them: water-based defoamer is modified silicone defoamer, water-based thickener is polyurethane thickener, water-based scorching wax powder is a mixture of polyethylene wax and amide wax or purchased from Clariant, water-based leveling agent It is octylphenol polyoxyethylene ether, and the fungicide is tetrachloroisophthalonitrile (TPN). The preparation method of the scorched-sensitivity water-based yangbuck foaming resin is the same as in Example 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
modulusaaaaaaaaaa
breaking strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention relates to a buffing burnt-feeling water-based Yangbuck foaming resin and a preparation method thereof. The water-based Yangbuck foaming resin comprises following raw material formula in part by weight: 48-52 parts of water-based acrylic resin, 43-47 parts of water, 0.5-2 parts of water-based foam killer, 2-4 parts of Yangbuck powder, 5-7 parts of water-based thickening agent, 2-4 parts of water-based rubbing-burnt paraffin powder, 2-4 parts of water-based leveling agent, 0-1 parts of disinfectant and 3-5 parts of organic bentonite. The water-based Yangbuck foaming resin provided by the invention is provided with very good scrape-resistance property, and can form strong hairy feeling by surface buffing; and at the same time the water-based Yangbuck foaming resin is also provided with strong burnt feeling and very delicate hand feeling, and the emulational effect of the leather is very good.

Description

technical field [0001] The invention relates to a water-based yangbuck foaming resin and a preparation method thereof. Background technique [0002] At present, leather-based products include bags, clothing, shoes, etc. The surface treatment methods are various, and the effect styles are varied: high-gloss high-solid, oily leather style, polished style, crazy horse discoloration, yangbuck, etc. Whether it is in surface effects, Still in terms of feel, we are still pursuing the effect of spinning genuine leather. [0003] Yangbuck foaming resin occupies a large proportion in the leather market in recent years. It uses Yangbuck powder to expand and foam, forming a fluffy effect on the surface of synthetic leather. The advanced post-production process can make different styles of leather products similar to real fur. Yangbuck foaming resin can be divided into two categories: solvent-based and water-based, and most of them are solvent-based. Compared with water-based Yangbuck ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/263D06M11/79
Inventor 王爱东
Owner SUZHOU DEERUN COMPOSITE MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap