Silane coupling agent-modified epoxy resin, and preparation method and application thereof

A silane coupling agent, epoxy resin technology, applied in epoxy resin coatings, coatings, anti-corrosion coatings, etc., can solve the problems of limiting the application of epoxy protective coatings, poor chemical resistance, poor aging resistance, etc. Achieve the effect of small strength drop, good chemical resistance and high adhesion

Active Publication Date: 2013-12-25
JIANGSU SOBUTE NEW MATERIALS +1
View PDF3 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing epoxy protective coatings have many shortcomings such as organic solvents, high paint film brittleness, poor chemical resistance, poor aging resistance, and difficult facade construction, which severely limits the application of epoxy protective coatings in the field of protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silane coupling agent-modified epoxy resin, and preparation method and application thereof
  • Silane coupling agent-modified epoxy resin, and preparation method and application thereof
  • Silane coupling agent-modified epoxy resin, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Prepare the epoxy resin modified by the silane coupling agent of structural formula (I) by each substituting group of table 1 respectively,

[0029]

[0030] Table 1 Structure of epoxy resin modified by silane coupling agent

[0031] code name

R1

R2

R3

R4

R5

R6

R7

SiEP01

CH 3

CH 3

CH 3

CH 3

C 2 h 5

C 2 h 5

C 2 h 5

SiEP02

CH 3

CH 3

H

H

C 2 h 5

C 2 h 5

C 2 h 5

SiEP03

H

H

H

H

C 2 h 5

C 2 h 5

C 2 h 5

SiEP04

CH 3

CH 3

CH 3

CH 3

CH 3

CH 3

CH 3

SiEP05

H

H

CH 3

CH 3

C 2 h 5

CH 3

CH 3

SiEP06

CH 3

H

H

CH 3

CH 3

C 2 h 5

C 2 h 5

[0032] Its preparation method is: mix the epoxy resin monomer represented by the formula (II) with the molar ratio ...

Embodiment 2

[0043] According to the formula of Table 3, the epoxy protective paints numbered as sample 1 to sample 6, comparative example 1 and comparative example 2 were prepared respectively, and the following steps were adopted: modifying epoxy resin, diluent, functional filler, thixotropic agent, Add the dispersant, defoamer and pigment into the reaction kettle in order at room temperature, raise the temperature to 40-60°C and stir for 0.5-1.5 hours to prepare component A of epoxy protective coating; put the curing agent and accelerator at room temperature Put them into the reaction kettle in sequence, stir at room temperature for 0.5-1.5 hours, and prepare the B component of epoxy protective coating. Before use, mix components A and B according to the formula ratio and stir well to obtain the epoxy protective coating described herein.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a silane coupling agent-modified epoxy resin. The structural formula of the epoxy resin is represented by formula (I). The invention further provides an epoxy protective paint including the silane coupling agent-modified epoxy resin. A preparation method for the silane coupling agent-modified epoxy resin is simple; after a reaction of the silane coupling agent-modified epoxy resin with an amine curing agent, the structure of the molecular chain of the cured resin is stable, compatibility between the epoxy resin and the interface of a pigment is high, and the strength of the cured resin is slightly reduced; and the epoxy protective paint prepared from the silane coupling agent-modified epoxy resin has the advantages of good film glossiness, good toughness, high bonding strength on a substrate, good resistance to chemicals, environment friendliness, moderate cost, etc.

Description

technical field [0001] The invention belongs to the field of protective coatings, in particular to a silane coupling agent-modified epoxy resin and a preparation method thereof, and also to a silane coupling agent-modified epoxy resin for use on surfaces such as metals and concrete. Protective epoxy protective coatings and methods for their preparation. Background technique [0002] Epoxy protective coating is a commonly used coating in building materials. Because epoxy resin has good bonding performance on the surface of various materials, has very comprehensive chemical resistance, and has good protective and chemical properties, it has become a protective field. The most widely used polymer material, the coating with epoxy resin as the main material is widely used in various fields, especially to protect steel structures such as bridges, mechanical equipment, tanks, or metal products such as steel plates and steel pipes from external corrosion A function of environmental...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/02C09D7/12C09D4/06C09D5/08C08G59/50
Inventor 乔敏俞寅辉高南箫冉千平刘加平
Owner JIANGSU SOBUTE NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap