Modified pure acrylic emulsion and preparation method thereof
A pure acrylic emulsion, modified technology, applied in the direction of coating, etc., can solve the problems of low hardness of coating film, high film forming temperature, low stability of emulsion, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0013] Example 1:
[0014] 1. Nano ZrO 2 The percentage content of each component of the modified pure acrylic emulsion is as follows:
[0015]
[0016]
[0017] 2. Nano ZrO 2 The preparation method of modified pure acrylic emulsion includes the following steps:
[0018] 1. Nano ZrO 2 Modification treatment: the nano ZrO 2 , Propylene glycol and 1 / 5 of the water were added to the vessel for ultrasonic dispersion for 40 minutes, then KH-570 silane coupling agent and oleic acid mixed modifier were added, and after the ultrasonic dispersion was continued for 40 minutes, the dispersion was placed in the reaction vessel and heated to 85 in a water bath. ℃, reflux for 3.5h, dry and grind after the reaction, to obtain modified nano ZrO 2 ;
[0019] 2. Respectively mix methyl methacrylate, butyl acrylate, methacrylic acid and modified nano ZrO 2 Mix and add to the container, stir with magnetic force for 1.5h, and then disperse by ultrasonic for 1.5h to prepare mixed nano-ZrO 2 The monomer mix...
Example Embodiment
[0023] Example 2:
[0024] 1. Nano ZrO 2 The percentage content of each component of the modified pure acrylic emulsion is as follows:
[0025]
[0026] 2. The preparation method is the same as in Example 1.
[0027] 3. The performance test results of the pure acrylic emulsion of this example are as follows:
[0028]
Example Embodiment
[0029] Example 3:
[0030] 1. Nano ZrO 2 The percentage content of each component of the modified pure acrylic emulsion is as follows:
[0031]
[0032] 2. The preparation method is the same as in Example 1.
[0033] 3. The performance test results of the pure acrylic emulsion of this example are as follows:
[0034]
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap