Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A method for measuring the sheath-core structure of carbon fiber pre-oxidized silk

A skin-core structure, pre-oxygen wire technology, which is used in the preparation of test samples and the use of measurement of secondary emissions for material analysis, etc., can solve the problems of large human factors, large interference of background pixel analysis, and high difficulty in operation.

Active Publication Date: 2017-12-29
NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The traditional solidified slice electron microscope observation method can only qualitatively characterize the existence of the skin-core structure, and human factors have a great influence. The distinction between the cortex and the core depends entirely on the operator.
Raman spectroscopy calculates the skin-core factor to determine its severity, which largely depends on the determination of the Raman test location, and cannot visually express the boundary between the cortex and the core
The optical density method can also test the fiber skin-core structure, but the method needs to undergo strict ultra-thin section processing with a thickness of about 70nm, and must ensure that the cut surface is flat and free of knife marks. Secondly, the obtained photos need to be analyzed professionally to obtain Data, the overall processing steps are cumbersome, the operation is difficult, and the shooting background interferes greatly with pixel analysis

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for measuring the sheath-core structure of carbon fiber pre-oxidized silk
  • A method for measuring the sheath-core structure of carbon fiber pre-oxidized silk
  • A method for measuring the sheath-core structure of carbon fiber pre-oxidized silk

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0101] In this embodiment, the bulk density is 1.2343 / cm 3 The pre-oxidized wire was cured in the curing agent for 1 hour at room temperature, and then dipped and etched with 98% concentrated sulfuric acid for 10 minutes. The obtained SEM photos are as follows: figure 1 shown. The calculated core ratios are shown in Table 1.

Embodiment 2

[0103] In this embodiment, the bulk density is 1.3240g / cm 3 The pre-oxidized wire was cured in the curing agent for 1 hour at room temperature, and then dipped and etched with 98% concentrated sulfuric acid for 3 minutes. The obtained SEM photos are as follows: figure 2 shown. The calculated core ratios are shown in Table 1.

Embodiment 3

[0105] In this embodiment, the bulk density is 1.3240g / cm 3 The pre-oxidized wire was cured in the curing agent for 1 hour at room temperature, and then dipped and etched with 25% concentrated sulfuric acid for 48 hours. The obtained SEM photos are as follows: image 3 shown. The calculated core ratios are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for detecting the skin-core structure of carbon fiber pre-oxidized silk. The method utilizes an etchant to etch the pre-oxidized silk fiber, so that the internal loose linear structure is corroded into holes. Fiber diameter, thereby quantitatively characterizing the severity of the skin-core. The method of the invention is easy to operate, less affected by external interference, low in cost, short in test time and can quantitatively calculate the proportion of the core, avoiding the interference of human factors.

Description

technical field [0001] The invention relates to the field of carbon fiber material testing. Specifically, the invention relates to a method for measuring the sheath-core structure of carbon fiber pre-oxidized silk. Background technique [0002] Carbon fiber is a high-strength, high-modulus material successfully developed in the 1960s. It is an inorganic polymer fiber with a carbon content of more than 90%. It has excellent properties such as high tensile strength, high modulus, high temperature resistance, wear resistance, corrosion resistance, and fatigue resistance. It is widely used in automobile manufacturing, energy chemical industry, sports, etc. Supplies, aerospace, military development and other fields. [0003] Pre-oxidation is an essential and important link in the carbon fiber preparation process. It acts as a link between the past and the future, transforming the linear molecular chain structure of the PAN precursor into a heat-resistant trapezoidal structure,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N23/22G01N1/28
Inventor 朱小龙王雪飞管建敏严庆
Owner NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com