A valve compound

A valve and rubber material technology, which is applied in the field of valve rubber material, can solve the problems of product quality fluctuation, great harm to human body, and easy volatility.

Active Publication Date: 2016-01-20
TAICANG GUANLIAN POLYMERIC MATERIAL
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Many domestic manufacturers need to soak or paint a layer of adhesive on the metal core when producing valve rubber, so that the rubber and the metal core are firmly connected, so as to have practical performance, but coating the adhesive will cause There are a lot of toxic and harmful gases in the production site, which is very harmful to the human body, and most of the adhesives have a lot of volatile and flammable solvents. Poor ventilation can easily cause fires, and the production process is cumbersome, and the adhesive performance is affected. The influence of the mixture is greater, and the product quality is prone to large fluctuations. In addition, it is necessary to purchase special equipment or personnel for the glue brushing operation. After the glue brushing operation, special equipment is required for drying and baking, which takes up a large area And personnel, it also causes a large investment burden for the production enterprise, and the valve rubber is mostly produced by ethylene propylene rubber, the price of this type of rubber is relatively high, causing a large cost burden for the valve production enterprise

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A valve compound
  • A valve compound

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A valve rubber material, comprising the following components by weight percentage:

[0025] Natural rubber 20%;

[0026] Ethylene propylene rubber 8%;

[0027] SBR 7%;

[0028] Carbon black 45%;

[0029] p-Phenylenediamine antioxidant 1.3%;

[0030] Anti-aging agent RD0.5%;

[0031] Wax antioxidant 0.75%;

[0032] Ketoamine anti-aging agent BLE-W1.45%;

[0033] Cobalt salt 0.6%;

[0034] White carbon black 3.8%;

[0035] Adhesive RS0.72%;

[0036] Adhesive A0.18%;

[0037] Naphthenic oil softener 6%;

[0038] Vulcanization system 2.1%;

[0039] Zinc oxide 2.2%;

[0040] Stearic acid 0.4%.

[0041] The preparation steps of the above-mentioned valve sizing material are as follows:

[0042] (1) Prepare materials, prepare the natural rubber, ethylene-propylene rubber, carbon black, p-phenylenediamine anti-aging agent, cobalt salt system, white carbon black, binder RS, binder A, ring Paraffin oil softener, vulcanization system, zinc oxide, stearic acid and sty...

Embodiment 2

[0050] All the other are identical with described embodiment 1, and difference is that above-mentioned valve compound comprises the following components by weight percentage:

[0051] Natural rubber 35%;

[0052] Ethylene propylene rubber 5%;

[0053] SBR 6%;

[0054] Carbon black 35%;

[0055] p-Phenylenediamine antioxidant 1.3%;

[0056] Anti-aging agent RD0.5%;

[0057] Wax antioxidant 0.45%;

[0058] Ketoamine antioxidant BLE-W0.25%;

[0059] Cobalt salt 0.4%;

[0060] White carbon black 3.9%;

[0061] Adhesive RS0.4%;

[0062] Adhesive A0.2%;

[0063] Naphthenic oil softener 5.7%;

[0064] Vulcanization system 3%;

[0065] Zinc oxide 2%;

[0066] Stearic acid 0.4%.

Embodiment 3

[0068] All the other are identical with described embodiment 1, and difference is that above-mentioned valve compound comprises the following components by weight percentage:

[0069] Natural rubber 39.49%;

[0070] Ethylene propylene rubber 6%;

[0071] SBR 5%;

[0072] Carbon black 35%;

[0073] p-phenylenediamine antioxidant 1%;

[0074] Anti-aging agent RD0.3%;

[0075] Wax antioxidant 0.45%;

[0076] Ketoamine antioxidant BLE-W0.25%;

[0077] Cobalt salt 0.5%;

[0078] White carbon black 3.5%;

[0079] Adhesive RS0.8%;

[0080] Adhesive A0.21%;

[0081] Softener 4%;

[0082] Vulcanization system 1%;

[0083] Zinc oxide 2.1%;

[0084] Stearic acid 0.4%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rubber matrix for an inflating valve, which comprises the following components in percentage by weight: 20-40% of natural rubber, 5-8% of ethylene-propylene rubber, 5-7% of styrene-butadiene rubber, 35-45% of filler reinforcement system, 2-4% of antiaging system, 0.4-0.6% of cobalt salt, 4.5-4.7% of resorcinol-hexamethylenetetramine-white carbon black system, 4-6% of softening agent, 1-3% of vulcanization system and 2.4-2.6% of activator system. According to the invention, a part of rubber matrix in an inflating valve is replaced with natural rubber, thus greatly lowering the cost of the rubber matrix and providing better physical and mechanical properties for the rubber; the originally needless antiaging system is added and combined in the composition, and the antiaging system can overcome the decrease of static / dynamic ozone resistance and aging resistance of the rubber matrix for an inflating valve and can promote the bonding between the rubber matrix and a metal core at the same time; a small amount of cobalt salt and resorcinol-hexamethylenetetramine-white carbon black system are added in the composition, thereby increasing the bonding force of the rubber matrix; and a large amount of filler reinforcement agent is used in the composition, thereby ensuring the physical and mechanical properties of the rubber matrix, and further lowering the cost.

Description

technical field [0001] The invention relates to a rubber material, in particular to a valve rubber material. Background technique [0002] Many domestic manufacturers need to soak or paint a layer of adhesive on the metal core when producing valve rubber, so that the rubber and the metal core are firmly connected, so as to have practical performance, but coating the adhesive will cause There are a lot of toxic and harmful gases in the production site, which is very harmful to the human body, and most of the adhesives have a lot of volatile and flammable solvents. Poor ventilation can easily cause fires, and the production process is cumbersome, and the adhesive performance is affected. The influence of the mixture is greater, and the product quality is prone to large fluctuations. In addition, it is necessary to purchase special equipment or personnel for the glue brushing operation. After the glue brushing operation, special equipment is required for drying and baking, whic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/00C08L23/16C08L9/06C08K13/02C08K3/04C08K3/36C08K5/01C08K3/22C08K5/09C08K3/26
Inventor 詹才福苏怀生
Owner TAICANG GUANLIAN POLYMERIC MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products