A technology of diatom mud coating and coating method, which is applied in the direction of architecture, building structure, covering/lining, etc., can solve the problems of unsuitable diatom mud coating, etc., and achieve beautiful and changeable texture effects, simple process, and texture effects long-lasting real results

Active Publication Date: 2014-05-28
福建皓尔宝新材料科技有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Under the condition of no external energy, M + The cycle repeatedly catalyzes negative oxygen ions to oxidize harmful gases such as formaldehyde, ammonia and nitrogen oxides from the room to make them harmless, and neutralizes and settles positively charged air dust to purify the indoor air, and has moisture absorption, Mildew-proof, bactericidal and other functions, but the coating method in the prior art is not suitable for this diatom mud coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Jade-imitated texture coating method for diatom ooze coating
  • Jade-imitated texture coating method for diatom ooze coating
  • Jade-imitated texture coating method for diatom ooze coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The diatom mud coating, batch coating and spot coating used in the following Example 2 are all prepared by the process of this example.

[0028] (1) Weigh each component according to the following weight percentages, and sequentially pass through crushing, vibrating screening, automatic metering, stirring, first blending, adding premix and second blending to prepare the diatom mud coating:

[0029]

[0030]

[0031] Different inorganic colorants can be added to form different colors.

[0032] (2) Mix the above-mentioned diatom mud coating with clean water in a ratio of 1:0.9 to obtain batch coatings, as follows: Measure the amount of clear water and diatom mud coating required for each stirring, first measure 90% of the clean water Pour it into the corresponding stirring container, then slowly put the measured diatom mud coating, fully mix it with a manual high-speed mixer to form a paste, the stirring time is not less than 10 minutes, and let it stand for 10 minu...

Embodiment 2

[0035] a. Use a batch knife to coat the batch paint on the wall twice. The thickness of the second coat is 1.5-2.0mm, and the thickness of the second coat is greater than the thickness of the first coat.

[0036] b. Use a pineapple roller to roll out the surface that has just been coated evenly, showing a concave-convex shape;

[0037] c. Use a rectangular sponge block of 80×100mm to apply the roller paint at intervals of 100-150mm, and then spray with water mist and trowel. On the coating surface, the diatom mud coatings of different colors are scattered and blended together, deep and shallow, far and near, and have a strong visual sense. ;

[0038] d. After 90% of the surface is dry, use a plastic polishing knife to polish, use a brush to clean the edges and corners, and wipe the surface with a white clean towel to clean up the powder particles that may be left in the polishing process to obtain imitation jade patterns.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a jade-imitated texture coating method for a diatom ooze coating. The jade-imitated texture coating method comprises the following steps: firstly, weighing various components according to the weight percentage and sequentially carrying out crushing, vibration screening, automatic metering, stirring, primary matching, premix addition and secondary matching on the components to obtain the diatom ooze coating; secondly, uniformly mixing and stirring the diatom ooze coating with clear water according to the proportion of 1:0.9 to form a paste shape and obtaining batch coating; thirdly, uniformly mixing and stirring the diatom ooze coating with clear water according to the proportion of 1:1.2 to form a paste shape and obtaining point coating; fourthly, producing jade-imitated textures on the wall surface by using the batch coating and the point coating. The jade-imitated texture coating method disclosed by the invention is very suitable for the diatom ooze coating; the diatom ooze coating can be used for preparing jade-imitated textures and can be directly used for construction of concrete, bricks, gypsum boards, compositeboards, old wall bodies and other wall surfaces.

Description

technical field [0001] The invention belongs to the field of interior decoration, and in particular relates to a method for coating a jade-like texture of a diatom mud coating. Background technique [0002] On the basis of Chinese invention patent ZL200510129955.8, a diatom mud coating with diatomite as the main raw material was invented. The coating consists of the following components: [0003] [0004] [0005] The above-mentioned diatom mud coating forms a network structure and a reversible electric double layer by connecting the active groups with -Si-O-Si-bonds, and adopts nano-silica, permanent electrode materials, high-efficiency catalysts M + The breathing paint constructed of high-tech material systems continuously generates micro-current electrolyzed water, which can automatically and permanently release negative ions. Without the need for external energy, M + Repeatedly catalyzes negative oxygen ions to oxidize harmful gases such as formaldehyde, ammonia ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00E04F13/02E04F21/06C04B14/08
Inventor 叶飞朱皓林联荣
Owner 福建皓尔宝新材料科技有限公司