A kind of manufacturing process of candy effect ceramic brick
A manufacturing process and technology for ceramic tiles, applied in the field of manufacturing process of candy-effect ceramic tiles, can solve the problems of poor fluidity of dry particles, high production cost and high cost, and achieve uniform distribution of dry particles, low manufacturing cost and good gloss effect. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0036] Surface glaze: 1000 parts of imported glaze, 120 parts of zirconium silicate, 1.344 parts of methyl, 1.12 parts of sodium tripolyphosphate, 2.4 parts of sodium humate; the fineness of glaze slurry is 300g. 1.0g, the specific gravity of the glaze is 1.50g / cm 3 ;
[0037] Candy dry granule glaze: dry granule: printing oil = 1:3, the particle size of the dry granule is -80 ~ +120 mesh, the flow rate of the printing oil is 40 seconds; the flow rate of the candy dry granule glaze is 25 seconds, pass through a 60 mesh sieve After that, the residue after sieving was 0 grams;
[0038] 1) On the surface of the dried green body, the surface glaze is applied by water knife spraying glaze, and the amount of spraying glaze is 50g / 330mm×330mm;
[0039] 2) Use inkjet printing equipment to print stone patterns on the glaze;
[0040] 3) On the printed green body, use a linear glazer to apply dry candy glaze, and the amount of glaze applied is 50g / 330mm×330mm;
[0041] 4) firing the ...
Embodiment 2
[0045] Surface glaze: 1000 parts of imported glaze, 120 parts of zirconium silicate, 1.344 parts of methyl, 1.12 parts of sodium tripolyphosphate, 2.4 parts of sodium humate; the fineness of glaze slurry is 300g. 1.6g, the specific gravity of the glaze is 1.48g / cm 3 ;
[0046] Candy dry granule glaze: dry granule:printing oil=1.2:3; the particle size of dry granule is -80~+150 mesh; the flow rate of printing oil is 40 seconds; the flow rate of candy dry granule glaze is 26 seconds; the candy dry granule glaze After passing through a 60-mesh sieve, the sieve residue is 0 grams;
[0047] 1) On the surface of the dried green body, the surface glaze is applied by water jet glaze spraying method, and the spray glaze amount is 48g / 330mm×330mm;
[0048] 2) Use inkjet printing equipment to print sandstone patterns on the glaze;
[0049] 3) On the printed green body, use a linear glazer to apply dry candy glaze, and the amount of glaze applied is 80g / 330mm×330mm;
[0050] 4) firing...
Embodiment 3
[0054] Surface glaze: 1000 parts of imported glaze, 120 parts of zirconium silicate, 1.344 parts of methyl, 1.12 parts of sodium tripolyphosphate, 2.4 parts of sodium humate; the fineness of glaze slurry is 300g. 0.8g, the specific gravity of the top glaze is 1.52g / cm;
[0055] Candy dry granule glaze: dry granule:printing oil=1.2:3; the particle size of dry granule is -80~+150 mesh; the flow rate of printing oil is 40 seconds; the flow rate of candy dry granule glaze is 26 seconds; the candy dry granule glaze After passing through a 60-mesh sieve, the sieve residue is 0 grams;
[0056] 1) On the surface of the dried green body, the surface glaze is applied by water jet glaze spraying method, and the spray glaze amount is 45g / 330mm×330mm;
[0057] 2) Use inkjet printing equipment to print wood grain patterns on the glaze;
[0058] 3) On the printed green body, use a linear glazer to apply dry candy glaze, and the amount of glaze applied is 35g / 330mm×330mm;
[0059] 4) firing ...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size (mesh) | aaaaa | aaaaa |
| particle size (mesh) | aaaaa | aaaaa |
| particle size (mesh) | aaaaa | aaaaa |