Environment-friendly high-iron-flux baking-free tapping channel ramming material and preparation method thereof

A baking-free and iron-tapping trough technology, which is applied in the field of refractory materials, can solve problems such as affecting the normal production of blast furnaces, burning out equipment in front of the furnace, and uneven quality parameters, so as to improve performance, increase service life, and eliminate harmful substances. The effect of low content

Inactive Publication Date: 2014-07-23
渑池金华新材料有限公司
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] At present, the quality of non-baking ramming materials for domestic blast furnace iron tapping is uneven, the service life is short, the environment is polluted, the labor intensity is high, and even iron leakage, burnout of front equipment and other problems occur, which seriously affect the normal production of blast furnaces.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly high-iron-flux baking-free tapping channel ramming material and preparation method thereof
  • Environment-friendly high-iron-flux baking-free tapping channel ramming material and preparation method thereof
  • Environment-friendly high-iron-flux baking-free tapping channel ramming material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] Carbon-containing resin, brownish-red liquid, purchased from Tianjin Kefulai Commercial Development Co., Ltd. (requirements: 50 °C Engler's viscosity is 14-16, and the residual carbon content is greater than 55%);

[0037] Vegetable oil, dark brown liquid, purchased from Zibo Taichang Lubricating Oil Co., Ltd. (requirements: 50°C Engler's viscosity is 7-9, carbon residue is greater than 30%);

[0038] Melamine urea-formaldehyde resin, purchased from Zhengzhou Chunming Trading Co., Ltd. (PH value 7.0-8.0, Engler viscosity: 7-9, carbon residue greater than 40%);

[0039] The carbon powder is in the form of black powder, purchased from Tianjin Kefulai Commercial Development Co., Ltd. (requirements: particle size less than 0.088mm, carbon residue greater than 80%).

[0040] Table 1: Chemical Composition of Main Raw Materials (wt%)

[0041]

[0042] The technical solutions of the present invention will be described in further detail below in conjunction with specific exa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to an environment-friendly high-iron-flux baking-free tapping channel ramming material and a preparation method thereof, belonging to the field of refractory materials. The environment-friendly high-iron-flux baking-free tapping channel ramming material is prepared from the following raw materials in parts by weight: 45-55 parts of brown corundum, 19-27 parts of dense corundum, 11-23 parts of SiC, 0-8 parts of Si powder, 0-12 parts of Si3N4, 3-6 parts of active alpha-Al2O3 powder, 1-5 parts of flake graphite and 3-8 parts of a bonding agent, wherein the total parts of all the other raw materials except the bonding agent is 100 parts; the bonding agent comprises the following components in parts by weight: 40-80 parts of carbon-containing resin, 10-40 parts of vegetable oil and fat, 5-15 parts of melamine urea-formaldehyde resin and 2-8 parts of carbon powder. An environment-friendly anhydrous tamping plug disclosed by the invention has the advantages that (1) the anhydrous tamping plug has small content of harmful substances, so that harms to the human body can not be caused; and (2) the anhydrous tamping plug does not have smoke and dust, so that the influence to the environment is small; (3) the anhydrous tamping plug has high iron flux and long service cycle, and can be used for reducing the labor intensity of workers.

Description

technical field [0001] The invention belongs to the technical field of refractory materials, and in particular relates to an environment-friendly, high-iron-throughput, non-baking iron ditch ramming material and a preparation method thereof. Background technique [0002] At present, there are few reports abroad on the research and development of environment-friendly, high-throughput, non-baking iron trench ramming materials and related products. There are still a large number of single-taphole blast furnaces in my country for quite a long time, and the tap channel materials used are traditional ramming materials, which contain many harmful components and cause certain harm to human health and the environment. Many users' understanding of the environment-friendly high-throughput iron-free baking-free ramming material is limited to no smoke or less smoke and dust, so the environment-friendly tapping channel ramming material should have the following three requirements: [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 刘志明王国华
Owner 渑池金华新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products