Method for manufacturing black card hang tag

A production method and black card technology, applied in the field of hangtags and labels, can solve the problems of unreachable, easy to scratch the surface color of the hangtag, not enough black and not bright enough, etc., and achieve the effect of not easy to scratch, fresh in appearance, and bright in color.

Active Publication Date: 2014-08-06
MAXIM SMART MFG CO LTD
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The black card hang tag produced by this process has stable quality, bright spots on the surface, and the black card is easy to scratch after being covered with black film, and the surface color of the hang tag is not dark enough or bright enough to achieve satisfactory results.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] In step a, cut the matte black slippery black cardboard into a size of 360mm×390mm.

[0033] In step b, the thickness of the BOPP anti-scratch matte pre-coating film is 0.30mm, the diameter of the coating roller is 28CM, the rotation speed of the roller is 380Rpm, the coating pressure is 15Mpa, the coating temperature is 70°C, and the amount of coating glue 4g / m 2 .

[0034] In step c, the ink formula is 17.5% varnish, 5% matte oil, 17.5% black ink, and 60% thinner; the thickness of the printed ink is 1.1 microns, and the printing speed is 8000 sheets / hour.

[0035] In step d, the mesh of the plane silk screen is 300 mesh.

[0036] The results of the inspection of the black card hang tags obtained in this embodiment through observation, hand touch, and scratch tests are: the appearance is fresh, the surface color is black and bright, and the color is ideal; the touch surface is plump and moist; Slight friction is used to verify the ability not to be easily scratched,...

Embodiment 2

[0038] In step a, cut the matte black slippery black cardboard into a size of 360mm×390mm.

[0039] In step b, the thickness of the BOPP anti-scratch matte pre-coating film is 0.28mm, the diameter of the coating roller is 26CM, the rotation speed of the roller is 400Rpm, the coating pressure is 17Mpa, the coating temperature is 65°C, and the amount of coating glue 2g / m 2 .

[0040] In step c, the ink formula is 18% varnish, 6% matte oil, 18% black ink, and 58% thinner; the thickness of the printed ink is 0.9 microns, and the printing speed is 7500 sheets / hour.

[0041] In step d, the mesh of the plane silk screen is 280 mesh.

[0042] The results of the inspection of the black card hang tags obtained in this embodiment through observation, hand touch, and scratch tests are: the appearance is fresh, the surface color is black and bright, and the color is ideal; the touch surface is plump and moist; Slight friction is used to verify the ability not to be easily scratched, and...

Embodiment 3

[0044] In step a, cut the matte black slippery black cardboard into a size of 360mm×390mm.

[0045] In step b, the thickness of the BOPP anti-scratch matte pre-coating film is 0.32mm, the diameter of the coating roller is 30CM, the rotation speed of the roller is 350Rpm, the coating pressure is 13Mpa, the coating temperature is 75°C, and the amount of coating glue 5g / m 2 .

[0046] In step c, the ink formula is 16% varnish, 4% matte oil, 16% black ink, and 64% thinner; the thickness of the printed ink is 1.3 microns, and the printing speed is 8500 sheets / hour.

[0047] In step d, the mesh of the plane silk screen is 320 mesh.

[0048] The results of the inspection of the black card hang tags obtained in this embodiment through observation, hand touch, and scratch tests are: the appearance is fresh, the surface color is black and bright, and the color is ideal; the touch surface is plump and moist; Slight friction is used to verify the ability not to be easily scratched, and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for manufacturing a black card hang tag. The method includes the following steps that firstly, matted black sliding surface black card paper is selected and cut into a preset size; secondly, the cut matted black sliding surface black card paper is covered with a BOPP scratch-resistant matt pre-coating film, wherein the thickness of the BOPP scratch-resistant matt pre-coating film ranges from 0.28 mm to 0.32 mm, the diameter of a film covering roller ranges from 26 cm to 30 cm, the rotating speed of the roller ranges from 350 Rpm to 400 Rpm, the film covering pressure ranges from 13 Mpa to 17 Mpa, the film covering temperature ranges from 65 DEG C to 75 DEG C, and the film covering glue use amount ranges from 2 g / m<2> to 5 g / m<2>; thirdly, printing ink is printed on the surface of the film through a UV offset press, the thickness of printed printing ink ranges from 0.9 micrometer to 1.3 micrometers, and the printing speed ranges from 7500 sheets per hour to 8500 sheets per hour; fourthly, plane white ink screen printing is conducted; fifthly, die cutting is conducted to form finished products. The black card hang tag manufactured through the method has the advantages that the touch surface is plump and moist, the impression is fresh, the color is black and shiny, and the black card hang tag is not prone to scratch, and can satisfy customers.

Description

technical field [0001] The invention belongs to the technical field of hang tags and labels, and in particular relates to a method for making a black card hang tag. Background technique [0002] The hang tag is the business card of the product, and even plays the role of advertisement and manual. Through the tag, consumers can understand the brand, raw materials and other information of the product. Exquisitely made hang tags play a decisive role in improving the grade of products. [0003] Among them, a black card tag is widely used in clothing products. The production process of the existing black card hang tag is cutting, black film covering, flat screen printing, and die cutting in sequence. The black card hang tag produced by this process has stable quality, bright spots on the surface, and the black card is easy to scratch after being covered with black film, and the surface color of the hang tag is not dark enough or bright enough to achieve satisfactory results. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): G09F7/00B32B38/14
Inventor 翟所强
Owner MAXIM SMART MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com