Rubber gloves with anti-inflammation function

A rubber glove, functional technology, applied in the field of surgical gloves, can solve the problems of infection and inflammation without any positive effect, hindering wound healing speed, no maintenance, etc., to avoid allergy problems, avoid poor stretch performance, and avoid allergies The effect of symptoms

Inactive Publication Date: 2014-08-13
GUILIN HBM HEALTHCARES
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the various gloves currently used basically only have an isolation effect, especially the surgical gloves are only for protection, and have no positive effect on the infection and inflammation of the wound, and the medical gloves are close to the human body. The skin of the hands, if the hands are accidentally scratched by a surgical knife, and then put on the current medical gloves, it is easy to cause wound inflammation
At the same time, when there are wounds or wounds on the skin of the hands, it is not suitable to wear these gloves directly. These gloves do not have the effect of maintaining and promoting wound healing. They also prevent the wound from contacting with the air, which hinders the speed of wound healing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber gloves with anti-inflammation function
  • Rubber gloves with anti-inflammation function
  • Rubber gloves with anti-inflammation function

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of rubber glove with anti-inflammatory function, wherein, described rubber latex is made up of following composition, by weight:

[0028]

[0029] The anti-inflammatory active ingredient is composed of Polygonum cuspidatum extract and Sophora flavescens extract with a weight ratio of 1:2.

[0030] Its preparation method is as follows:

[0031] A, prepare the rubber latex that dipping is used, with natural rubber, emulsified liquid paraffin, colloidal sulfur, zinc oxide, promotor ZDBC, promotor ZMBT, anti-inflammatory active ingredient, fully mix, adjust solid content to be 25-32%;

[0032] B, after the mold is dried, impregnate the coagulant first, and the coagulant is calcium nitrate or calcium chloride solution of 15% by weight;

[0033] C. Dry the mold, then dip the mold into the rubber latex prepared above, then crimp, then immerse in warm water at 45°C for 2 minutes, take it out, and dry it at a high temperature of 140°C for 20 minutes;

[0034] D, cool...

Embodiment 2

[0036] A kind of rubber glove with anti-inflammatory function, wherein, described rubber latex is made up of following composition, by weight:

[0037]

[0038]

[0039] The anti-inflammatory active ingredient is composed of Polygonum cuspidatum extract and Sophora flavescens extract with a weight ratio of 3:4.

[0040] Its preparation method is as follows:

[0041] A, prepare the rubber latex that dipping is used, with natural rubber, emulsified liquid paraffin, colloidal sulfur, zinc oxide, promotor ZDBC, promotor ZMBT, anti-inflammatory active ingredient, fully mix, regulate solid content to be 32%;

[0042] B, after the mold is dried, impregnate the coagulant first, and the coagulant is calcium nitrate or calcium chloride solution of 8% by weight;

[0043] C. Dry the mold, then dip the mold into the rubber latex prepared above, then crimp, then immerse in warm water at 45°C for 2 minutes, take it out, and dry it at high temperature at 120°C for 40 minutes;

[0044]...

Embodiment 3

[0046] A kind of rubber glove with anti-inflammatory function, wherein, described rubber latex is made up of following composition, preferably, by weight:

[0047]

[0048] The anti-inflammatory active ingredient is composed of Polygonum cuspidatum extract and Sophora flavescens extract with a weight ratio of 2:3.

[0049] Its preparation method is as follows:

[0050] A, prepare the rubber latex that impregnation is used, with natural rubber, emulsified liquid paraffin, colloidal sulfur, zinc oxide, promotor ZDBC, promotor ZMBT, anti-inflammatory active ingredient, fully mix, regulate solid content to be 28%;

[0051] B. After the mold is dried, first impregnate the coagulant, which is 10% by weight of calcium nitrate or calcium chloride solution;

[0052] C. Dry the mold, then dip the mold into the rubber latex prepared above, then crimp it, then immerse it in warm water at 45°C for 2 minutes, take it out, and dry it at a high temperature of 130°C for 30 minutes;

[005...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a pair of rubber gloves with an anti-inflammation function. The pair of rubber glove comprises rubber latex and anti-inflammation active ingredients, and is characterized in that the rubber latex comprises following components by weight: 70-80 parts of natural rubber, 20-30 parts of nitrile rubber, 5-8 parts of emulsified liquid paraffin, 0.6-1.2 parts of colloid sulphur, 0.4-1.0 part of zinc oxide, 0.2-0.4 part of accelerant ZDBC, 0.3-0.5 part of accelerant ZMBT, and 0.7-1.5 parts of anti-inflammation active ingredients, wherein the anti-inflammation active ingredients comprise a polygonum cuspidatum extract and a matrine extract at a weight ratio of (1-3):(2-4). Based on operation gloves, the pair of rubber gloves is added with the anti-inflammation active ingredients in the matrix, and thus is capable of diminishing inflammation in use, and improving the safety performance of the operation gloves.

Description

technical field [0001] The invention relates to surgical gloves, in particular to a rubber glove with anti-inflammatory function. Background technique [0002] Gloves have been widely used in people's production and life because of their barrier protection and can well protect the safety of users. According to its different uses, it can be divided into medical gloves, industrial gloves and household gloves; according to the different materials used in manufacturing, it can be divided into natural rubber gloves, nitrile gloves, PVC gloves and so on. [0003] However, among the disposable surgical gloves currently used in hospitals, the vast majority are still natural rubber gloves. There are two main reasons for this: 1. The tensile properties and elasticity of nitrile rubber gloves are worse than those of natural rubber latex; the national standard GB7543-2006 "Disposable Sterilized Rubber Surgical Gloves" also stipulates the stretching properties of gloves. Performance re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/02C08K13/02C08K3/06C08K3/22C08K5/39C08K5/47A61B19/04
Inventor 胡智强
Owner GUILIN HBM HEALTHCARES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap