Benzene and ketone free high temperature resistant table printing ink

A high-temperature-resistant ink, benzene-free and ketone-free technology, used in inks, household appliances, applications, etc., can solve problems such as human injury and environmental pollution, and achieve the effect of reducing waste, improving easy discoloration, and maintaining no color change.

Active Publication Date: 2014-08-20
SUZHOU ZHONGYA INK
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] For a long time, printing inks in the packaging industry have mostly been based on benzene-based solvent-based gravure plastic film inks, and benzene-based solvents will not only pollute the environment, but also cause harm to the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Benzene and ketone free high temperature resistant table printing ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] In this embodiment, the benzene-free and ketone-free surface printing high-temperature resistant ink of the present invention includes ink and curing agent, and the curing agent is polyisocyanate, wherein the ink is composed of the following components in parts by mass: 30 parts of polyurethane resin, polyethylene 12 parts of vinyl acetate, 35.7 parts of ester alcohol solvent, 0.8 part of propylene glycol methyl ether acetate, 10 parts of pigment, 0.5 part of polyester polyamide copolymer (dispersant), 0.5 part of polyethylene wax powder, modified chlorinated polypropylene ( Adhesion promoter) 1 part, antistatic agent 1 part, matting agent 8 parts, defoamer 0.5 part and polytetrafluoroethylene wax (high temperature resistance additive) 0.5 part, the mass part of polyisocyanate is 1.5 parts. Among them, the polyurethane resin in the composition refers to the polymer composed of isophorone diisocyanate and polypropylene-1,2-ethylene glycol ether; the ester alcohol solvent ...

Embodiment 2

[0026] In this embodiment, the benzene-free and ketone-free surface printing high-temperature-resistant ink of the present invention includes ink and curing agent, and the curing agent is polyisocyanate, wherein the ink is composed of the following components in parts by mass: 32.5 parts of polyurethane resin, polyethylene 12 parts of vinyl acetate, 40 parts of ester alcohol solvent, 0.82 parts of propylene glycol methyl ether acetate, 12 parts of pigment, 0.55 parts of polyester polyamide copolymer (dispersant), 0.55 parts of polyethylene wax powder, modified chlorinated polypropylene ( Adhesion promoter) 1.2 parts, antistatic agent 1.2 parts, matting agent 8 parts, defoamer 0.55 parts and polytetrafluoroethylene wax (high temperature resistance additive) 0.55 parts, the mass fraction of polyisocyanate is 1.5 parts. Among them, the polyurethane resin in the composition refers to the polymer composed of isophorone diisocyanate and polypropylene-1,2-ethylene glycol ether; the es...

Embodiment 3

[0029] In this embodiment, the benzene-free and ketone-free surface printing high-temperature resistant ink of the present invention includes ink and curing agent, and the curing agent is polyisocyanate, wherein the ink is composed of the following components in parts by mass: 30 parts of polyurethane resin, polyethylene 10 parts of vinyl acetate, 33 parts of ester alcohol solvent, 0.75 parts of propylene glycol methyl ether acetate, 9.5 parts of pigment, 0.46 parts of polyester polyamide copolymer (dispersant), 0.48 parts of polyethylene wax powder, modified chlorinated polypropylene ( Adhesion promoter) 0.95 parts, antistatic agent 0.95 parts, matting agent 8 parts, defoamer 0.46 parts and polytetrafluoroethylene wax (high temperature resistance additive) 0.55 parts, the mass number of polyisocyanate is 1.6 parts. Among them, the polyurethane resin in the composition refers to the polymer composed of isophorone diisocyanate and polypropylene-1,2-ethylene glycol ether; the est...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a benzene and ketone free high temperature resistant table printing ink. The benzene and ketone free high temperature resistant table printing ink comprises, by mass, 25-40 parts of a polyurethane resin, 10-15 parts of polyethylene vinyl acetate, 30-45 parts of an ester alcohol solvent, 0.6-1 part of propylene glycol methyl ether acetate, 5-15 parts of a pigment, 0.3-0.6 parts of a dispersant, 0.3-0.6 parts of polyethylene wax powder, 0.8-1.5 parts of an adhesion promoter, 0.8-1.5 parts of an antistatic agent, 5-10 parts of a delustering agent, 0.3-0.6 parts of an antifoaming agent, 0.3-0.8 parts of a high temperature resistant assistant, and 1-2 parts of a curing agent. The adoption of a double liquid design increases the hardness and the adhesion of an ink film, effectively prevents offsetting or ink falling, realizes excellent high temperature and boiling resistances, and increases the shelf life of the printing ink.

Description

technical field [0001] The invention relates to the technical field of ink production, in particular to a high temperature resistant ink for surface printing. Background technique [0002] For a long time, printing inks in the packaging industry have mostly been based on benzene-based solvent-based gravure plastic film inks, and benzene-based solvents will not only pollute the environment, but also cause harm to the human body. At present, many countries in the world have banned or restricted the use of benzene solvents. In addition, for external-use flexible packaging materials such as food and medicine, it is required to undergo high-temperature sterilization and environmental protection, which requires the use of suitable printing inks that are resistant to high-temperature cooking. Contents of the invention [0003] The technical problem mainly solved by the present invention is to provide a benzene-free and ketone-free surface printing high-temperature resistant ink,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/102C09D11/106
Inventor 张东明
Owner SUZHOU ZHONGYA INK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com