Easy-adhesion agent for solar cell protection sheet, solar cell protection sheet, and solar cell module

A technology for solar cells and protective sheets, applied in the direction of film/sheet adhesives, non-polymer organic compound adhesives, adhesives, etc., can solve the problem of high cost, achieve small output reduction and excellent adhesion , The effect of excellent adhesion durability

Active Publication Date: 2014-09-10
TOYO INK SC HOLD CO LTD +1
View PDF13 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] However, such a film generally has a thickness of several tens of micrometers, so there is a problem of higher cost compared with the above-mentioned easy-adhesion treatment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Easy-adhesion agent for solar cell protection sheet, solar cell protection sheet, and solar cell module
  • Easy-adhesion agent for solar cell protection sheet, solar cell protection sheet, and solar cell module
  • Easy-adhesion agent for solar cell protection sheet, solar cell protection sheet, and solar cell module

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0340] Using the sample 1 for adhesive force evaluation, the adhesiveness of the easy-adhesive layer to the EVA film and the adhesiveness of the heat-and-moisture test (after 1000 hours and after 2000 hours) were evaluated by the method described later.

[0341] Adhesion Evaluation

[0342] Cut the surface of the solar cell protection sheet 1 of the sample 1 for adhesion evaluation into a width of 15 mm with a cutter knife, and the gap between the easy-adhesive layer formed on the solar cell protection sheet 1 and the EVA film as a sealing material was cut. Adhesion was measured. A tensile tester was used for the measurement, and a 180-degree peel test was performed at a loading speed of 100 mm / min. The obtained measured values ​​were evaluated as follows.

[0343] ◎: 50N / 15mm or more

[0344] ○: More than 30N / 15mm to less than 50N / 15mm

[0345] △: More than 10N / 15mm to less than 30N / 15mm

[0346] ×: less than 10N / 15mm

[0347] Adhesion evaluation after damp heat test

...

Embodiment 2～221、 comparative example 1～30

[0350] In the same manner as in Example 1, using samples 2 to 221 and 1' to 30' for adhesive force evaluation, the adhesiveness of the easily adhesive layer to the EVA film and the adhesiveness after the heat-and-moisture resistance test were evaluated. The above results are shown in Tables 13-1, 13-2, 13-3, 13-4, 14, 15-1A, 15-1B, 15-2, 15-3A, 15-3B, 16, 17-1A , 17-1B, 17-2A, 17-2B, 17-3A, 17-3B, 18, 19-1A, 19-1B, 19-2A, 19-2B, 19-3A, 19-3B, 20, 21 -1A, 21-1B, 21-2A, 21-2B, 21-3A, 21-3B, 22, 23-1, 23-2, 23-3, 24.

[0351] The abbreviations in Tables 13-1 to 24 indicate the contents shown below.

[0352] Compounds B1-B6 having a (meth)acryloyl group

[0353] Among the compounds B1 to B6 having a (meth)acryloyl group, the compounds described below were used as they were.

[0354] B1: Aronicus M-215 (manufactured by Toagosei Co., Ltd., isocyanuric acid EO-modified diacrylate)

[0355] B2: Aronicus M-315 (manufactured by Toagosei Co., Ltd., isocyanuric acid EO-modified triacr...

Embodiment 222

[0418] Manufacture of solar cell modules

[0419] Whiteboard glass・・・Solar cell surface protection material (I)

[0420] EVA film...Sealing material on the light receiving side (II)

[0421] Polycrystalline silicon solar cell element···solar cell (III)

[0422] EVA film...Sealing material on the non-light-receiving side (IV)

[0423] The above-mentioned (I)-(IV) and the solar cell protection sheet 1 are stacked in order so that the easy-adhesive layer of the solar cell protection sheet 1 is in contact with the sealing material (IV) on the non-light-receiving side side, and then put into a vacuum laminator , evacuated to about 1 Torr, under the state of applying atmospheric pressure as pressurized pressure, heated at 150°C for 30 minutes, and then heated at 150°C for 30 minutes to make a 10cm×10cm square photoelectric conversion efficiency evaluation. battery module 1.

[0424] Determination of Photoelectric Conversion Efficiency

[0425] The solar cell output of the obtai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

Provided are: an easy-adhesion agent that is for a solar cell protection sheet and has superior adhesion and adhesion durability; a solar cell protection sheet; and a solar cell module resulting from using the solar cell protection sheet. The easy-adhesion agent for a solar cell protection sheet contains a resin (R) other than a (meth)acrylic copolymer (A), and contains 0.01-50 g / 100 g by iodine value of (meth)acryloyl group-derived carbon-carbon double bonds. The solar cell protection sheet is equipped with: an easy-adhesion agent layer formed at the surfacemost layer and formed by means of the easy-adhesion agent for a solar cell protection sheet; and a plastic film of which one primary surface supports the easy-adhesion agent layer.

Description

technical field [0001] The invention relates to an easy adhesive for a solar cell protection sheet. Moreover, it is related with the solar cell protection sheet which used the said solar cell protection sheet easy adhesive, and the solar cell module which used this solar cell protection sheet. Background technique [0002] In recent years, due to the increasing awareness of environmental issues, solar cells have attracted attention as clean energy that does not cause environmental pollution, and have been intensively studied and promoted in terms of useful energy utilization. [0003] There are various forms of solar cell elements, and crystalline silicon solar cell elements, polycrystalline silicon solar cell elements, amorphous silicon solar cell elements, copper indium selenium solar cell elements, and compound semiconductor solar cell elements are known as typical ones. Among them, polycrystalline silicon solar cell elements, amorphous silicon solar cell elements, and c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/06H01L31/048C09J7/20
CPCC09J7/02C09J4/06C09J2203/322C09D201/02C09J2201/622B32B27/00Y02E10/50H01L31/048C09J201/02C09J7/20C09J2301/312
Inventor 山口浩史柳泽诚前田谕志梅泽三雄
Owner TOYO INK SC HOLD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com