Method for repairing and remanufacturing outer surface of piston rod of hydraulic cylinder or outer surface of intermediate cylinder

A piston rod and outer surface technology, applied in the field of equipment repair and remanufacturing, can solve the problems of limiting the wide application of surface laser cladding, unacceptable time period of repair, and thin single-layer thickness of surface cladding, and achieves good economical application. performance, avoid serious environmental pollution problems, and improve remediation performance

Active Publication Date: 2014-12-10
SHAANXI TIANYUAN MATERIALS PROTECTION TECH
View PDF5 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its shortcomings are also very prominent: (1) The high cost is its biggest problem. Since it is necessary to repair the entire surface of the repaired piston rod and intermediate cylinder, the cost exceeds 2-3 times the price of the parts themselves; The time period is also unacceptable; (2), the thickness of the surface cladding layer is relatively thin, which cannot solve the repair of parts with large curvature, and the time period for 2 or 3 times of multiple cladding also needs to be extended by 2-3 times
These defects directly limit the wide application of surface laser cladding in the repair of hydraulic supports in coal mines

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for repairing and remanufacturing outer surface of piston rod of hydraulic cylinder or outer surface of intermediate cylinder
  • Method for repairing and remanufacturing outer surface of piston rod of hydraulic cylinder or outer surface of intermediate cylinder
  • Method for repairing and remanufacturing outer surface of piston rod of hydraulic cylinder or outer surface of intermediate cylinder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Repair and remanufacture the outer surface of the hydraulic cylinder piston rod or intermediate cylinder with an outer diameter of Ф380mm, including the following steps:

[0048] (1) Clamp the piston rod or the intermediate cylinder on a standard lathe, turn it to remove the electroplating layer remaining on the surface,

[0049] The turning thickness is 1.0mm;

[0050] (2) Sandblast the treated piston rod or the outer surface of the intermediate cylinder. The sandblasting adopts 18 mesh brown corundum sand material, and the sandblasting pressure is 0.7Mpa. After sandblasting, use high-pressure gas of the same pressure to clean the surface after sandblasting;

[0051] (3) Place the piston rod or intermediate cylinder processed in step (2) in an oven for preheating, the preheating temperature is 100℃±10℃, and the preheating time is 30min;

[0052] (4) Immediately clamp the piston rod or intermediate cylinder preheated in step (3) on an arc thermal spraying device for arc ...

Embodiment 2

[0058] Repair and remanufacture the outer surface of the piston rod or intermediate cylinder with an outer diameter of Ф260mm:

[0059] (1) Clamp the piston rod or the intermediate cylinder on a standard lathe, turn it to remove the electroplating layer remaining on the surface,

[0060] The turning thickness is 1.0mm;

[0061] (2) Sandblast the treated piston rod or the outer surface of the intermediate cylinder. The sandblasting adopts 18 mesh brown corundum sand material, and the sandblasting pressure is 0.7Mpa. After sandblasting, use high-pressure gas of the same pressure to clean the surface after sandblasting;

[0062] (3) Place the piston rod or intermediate cylinder processed in step (2) in an oven for preheating, the preheating temperature is 100℃±10℃, and the preheating time is 30min;

[0063] (4) Immediately clamp the piston rod or intermediate cylinder preheated in step (3) on an arc thermal spraying device for arc thermal spraying. The specific spraying paramete...

Embodiment 3

[0069] Repair and remanufacture the outer surface of the piston rod with an outer diameter of Ф150mm:

[0070] (1) Clamp the piston rod on a standard lathe, turn it to remove the residual electroplating layer on the surface, and turn the thickness

[0071] is 0.8mm;

[0072] (2) Sandblast the outer surface of the treated piston rod, using 20 mesh brown corundum sand for sandblasting, and the sandblasting pressure is 0.6Mpa. After sandblasting, use high-pressure gas with the same pressure to clean the surface after sandblasting;

[0073] (3) Place the piston rod treated in step (2) in an oven for preheating, the preheating temperature is 100℃±10℃, and the preheating time is 30min;

[0074] (4) Immediately clamp the piston rod preheated in step (3) on an arc thermal spraying device for arc thermal spraying. The specific spraying parameters are: use a 1.6mm diameter powder core wire for arc thermal spraying, When the voltage is controlled at 39V, the current is controlled at 20...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for repairing and remanufacturing the surface of a piston rod of a hydraulic cylinder or the outer surface of an intermediate cylinder for coal mines. Aiming at remanufacturing after the surface of the piston rod of the hydraulic cylinder or the outer surface of the intermediate cylinder for the coal mines is damaged and fails, the long-term practice is combined, a metal wire adopting the specific metal powder proportion is creatively designed to serve as a powder core wire, and namely the metal wire is formed by wrapping the metal powder with Cr, Ni and Fe as the main ingredients through a stainless steel foil layer; based on the arc thermal spraying process method, the surface is repaired and remanufactured creatively, and on the premise that the corrosion resistance and the hardness of the repaired layer of the surface are equal to those of the surface treated through the surface laser cladding technology, consideration is given to the good economic applicability and the good practical production efficiency; an existing electroplating technology can be completely replaced, and the method has the wide application and popularization prospects in repairing of the piston rod of the hydraulic support oil cylinder and the intermediate cylinder for the coal mines.

Description

technical field [0001] The invention relates to the technical field of repair and remanufacture of equipment, and more specifically relates to a method for repair and remanufacture of a piston rod of a hydraulic cylinder or an outer surface of an intermediate cylinder. Background technique [0002] Both the piston rod and the intermediate cylinder are important parts of the hydraulic cylinder. The piston rod is a necessary part of the single-stage and multi-stage hydraulic cylinders. It is usually made of 45# steel or 27simn alloy steel to make a solid rod structure, while the intermediate cylinder is used for In the multi-stage hydraulic cylinder system, the hollow tube structure is usually made of 45# steel or 27simn alloy steel. The piston rod is stretched in the hollow structure of the intermediate cylinder, and at the same time, the intermediate cylinder itself is stretched in the larger diameter external oil cylinder. . Therefore, the surface of the piston rod and the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P6/02B23P6/00
CPCB23K9/048B23P6/02
Inventor 王春昌刘鸣苏成明张亚飞马尚
Owner SHAANXI TIANYUAN MATERIALS PROTECTION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap